High-Performance Hardmetal Materials

ABSTRACT

Hardmetal compositions each including hard particles having a first material and a binder matrix having a second, different material comprising rhenium or a Ni-based superalloy. Tungsten may also be used a binder matrix material. A two-step sintering process may be used to fabricate such hardmetals at relatively low sintering temperatures in the solid-state phase to produce substantially fully-densified hardmetals. A hardmetal coating or structure may be formed on a surface by using a thermal spray method.

This application is a divisional application of U.S. patent application Ser. No. 11/081,928, filed Mar. 15, 2005, which claims benefit of U.S. Provisional Patent Application No. 60/554,205, filed Mar. 17, 2004, and U.S. Provisional Patent Application No. 60/584,593, filed Jun. 30, 2004.

In addition, this application claims the benefit of and is a continuation-in-part application of U.S. patent application Ser. No. 10/453,085, filed Jun. 2, 2003, which claims benefit of U.S. Provisional Patent Application No. 60/439,838, filed Jan. 13, 2003, and U.S. Provisional Patent Application No. 60/449,305, filed Feb. 20, 2003.

Furthermore, this application claims benefit of and is a continuation-in-part application of U.S. patent application Ser. No. 10/941,967, filed Sep. 14, 2004.

The entire disclosures of the above referenced U.S. patent applications are considered and are incorporated by reference as part of the specification of this application.

BACKGROUND

This application relates to hardmetal compositions, their fabrication techniques, and associated applications.

Hardmetals include various composite materials and are specially designed to be hard and refractory, and exhibit strong resistance to wear. Examples of widely-used hardmetals include sintered or cemented carbides or carbonitrides, or a combination of such materials. Some hardmetals, called cermets, have compositions that may include processed ceramic particles (e.g., TiC) bonded with binder metal particles. Certain compositions of hardmetals have been documented in the technical literature. For example, a comprehensive compilation of hardmetal compositions is published in Brookes' World Dictionary and Handbook of Hardmetals, sixth edition, International Carbide Data, United Kingdom (1996).

Hardmetals may be used in a variety of applications. Exemplary applications include cutting tools for cutting metals, stones, and other hard materials, wire-drawing dies, knives, mining tools for cutting coals and various ores and rocks, and drilling tools for oil and other drilling applications. In addition, such hardmetals also may be used to construct housing and exterior surfaces or layers for various devices to meet specific needs of the operations of the devices or the environmental conditions under which the devices operate.

Many hardmetals may be formed by first dispersing hard, refractory particles of carbides or carbonitrides in a binder matrix and then pressing and sintering the mixture. The sintering process allows the binder matrix to bind the particles and to condense the mixture to form the resulting hardmetals. The hard particles primarily contribute to the hard and refractory properties of the resulting hardmetals.

SUMMARY

The hardmetal materials described below include materials comprising hard particles having a first material, and a binder matrix having a second, different material. The hard particles are spatially dispersed in the binder matrix in a substantially uniform manner. The first material for the hard particles may include, for example, materials based on tungsten carbide, materials based on titanium carbide, materials based on a mixture of tungsten carbide and titanium carbide, other carbides, nitrides, borides, silicides, and combinations of these materials. The second material for the binder matrix may include, among others, rhenium, a mixture of rhenium and cobalt, a nickel-based superalloy, a mixture of a nickel-based superalloy and rhenium, a mixture of a nickel-based superalloy, rhenium and cobalt, and these materials mixed with other materials. Tungsten may also be used as a binder matrix material in hardmetal materials. The nickel-based superalloy may be in the γ-γ′ metallurgic phase.

In various implementations, for example, the volume of the second material may be from about 3% to about 40% of a total volume of the material. For some applications, the binder matrix may comprise rhenium in an amount at or greater than 25% of a total weight of the binder matrix of the final material. For other applications, the second material may include a Ni-based superalloy. The Ni-based superalloy may include Ni and other elements such as Re for certain applications.

Fabrication of the hardmetal materials of this application may be carried out by, according to one implementation, sintering the material mixture under a vacuum condition and performing a solid-phase sintering under a pressure applied through a gas medium. Such hardmetals may also be coated on surfaces using thermal spray methods to form either hardmetal coatings and hardmetal structures.

Advantages arising from various implementations of the described hardmetal materials may include one or more of the following: superior hardness in general, enhanced hardness at high temperatures, and improved resistance to corrosion and oxidation.

Various specific implementations described in this application are summarized as follows. The first group of 265 specific implementations is as follows.

1. A material comprising:

hard particles having a first material; and

a binder matrix having a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium in an amount greater than 25% of a total weight of the material, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

2. The material as in the above item no. 1 or 14, wherein said first material includes a carbide comprising tungsten.

3. The material as in the above item no. 2, wherein said carbide comprises mono tungsten carbide (WC).

4. The material as in the above item no. 2, wherein said first material further includes another carbide having a metal element different from tungsten.

5. The material as in the above item no. 4, wherein said metal element is titanium (Ti).

6. The material as in the above item no. 4, wherein said metal element is tantalum (Ta).

7. The material as in the above item no. 4, wherein said metal element is niobium (Nb).

8. The material as in the above item no. 4, wherein said metal element is vanadium (V).

9. The material as in the above item no. 4, wherein said metal element is chromium (Cr).

10. The material as in the above item no. 4, wherein said metal element is hafnium (Hf).

11. The material as in the above item no. 4, wherein said metal element is molybdenum (Mo).

12. The material as in the above item no. 2, wherein said first material further includes a nitride.

13. The material as in the above item no. 2 or 12, wherein said nitride includes TiN, ZrN, VN, NbN, TaN or HfN.

14. A material, comprising:

hard particles comprising a first material which comprises a nitride; and

a binder matrix comprising a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

15. The material as in the above item no. 14, wherein said nitride includes TiN, ZrN, VN, NbN, TaN or HfN.

16. The material as in the above item no. 1, wherein said binder matrix further includes cobalt (Co).

17. A material comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium and nickel (Ni), wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

18. A material comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium and molybdenum (Mo), wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

19. A material comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium and iron (Fe), wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

20. A material comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium and chromium (Cr), wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

21. A material comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium and a Ni-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

22. The material as in the above item no. 21, wherein said binder material further includes cobalt.

23. A material comprising:

hard particles having a first material having a mixture selected from at least one from a group consisting of (1) a mixture of WC, TiC, and TaC, (2) a mixture of WC, TiC, and NbC, (3) a mixture of WC, TiC, and at least one of TaC and NbC, and (4) a mixture of WC, TiC, and at least one of HfC and NbC; and

a binder matrix having a second, different material, a volume of said binder matrix being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

24. A material comprising:

hard particles having a first material comprising a material selected from at least one from a group consisting of (1) WC, TiC, and TaC, (2) WC, TiC, and NbC, (3) WC, TiC, and at least one of TaC and NbC, and (4) WC, TiC, and at least one of HfC and NbC; and a binder matrix comprising a second, different material, a volume of said binder matrix being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium and

a Ni-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

25. A material comprising:

hard particles having a first material having a mixture of Mo₂C and TiC; and

a binder matrix having a second, different material, a volume of said binder matrix being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

26. A material, comprising:

hard particles comprising a first material which comprises TiN, Mo₂C and TiC; and

a binder matrix comprising a second, different material, a volume of said binder matrix being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

27. A material, comprising:

hard particles comprising a first material comprising Mo₂C and TiC; and

a binder matrix comprising a second, different material, a volume of said binder matrix being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium and a Ni-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

28. A method comprising:

forming a grade power by mixing a powder of hard particles with a binder matrix material comprising rhenium;

processing the grade powder to use the binder matrix material to bind the hard particles to produce a solid hardmetal material, wherein the processing includes (1) sintering the grade powder in a solid phase under a vacuum condition, and (2) sintering the grade power in a solid phase under a pressure in an inert gas medium.

29. The method as in the above item no. 28, wherein the binder matrix material further includes a Ni-based superalloy.

30. The method as in the above item no. 29, wherein the binder matrix material further includes cobalt.

31. The method as in the above item no. 28, wherein the binder matrix material further includes cobalt.

32. The method as in the above item no. 28, wherein each sintering is performed a temperature below an eutectic temperature of the hard particles and the binder matrix material.

33. A material comprising:

hard particles having a first material; and

a binder matrix having a second, different material comprising a nickel-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

34. The material as in the above item no. 33 or 47, wherein said first material includes a carbide comprising tungsten.

35. The material as in the above item no. 34, wherein said carbide comprises mono tungsten carbide (WC).

36. The material as in the above item no. 34, wherein said first material further includes another carbide having a metal element different from tungsten.

37. The material as in the above item no. 36, wherein said metal element is titanium (Ti).

38. The material as in the above item no. 36, wherein said metal element is tantalum (Ta).

39. The material as in the above item no. 36, wherein said metal element is niobium (Nb).

40. The material as in the above item no. 36, wherein said metal element is vanadium (V).

41. The material as in the above item no. 36, wherein said metal element is chromium (Cr).

42. The material as in the above item no. 36, wherein said metal element is hafnium (Hf).

43. The material as in the above item no. 36, wherein said metal element is molybdenum (Mo).

44. The material as in the above item no. 34, wherein said first material further includes a nitride.

45. The material as in the above item no. 34 or 44, wherein said nitride includes at least one of ZrN, HfN, VN, NbN, TaN and TiN.

46. The material as in the above item no. 34 or 44, wherein said first material includes a carbide.

47. A material, comprising:

hard particles comprising a first material which comprises a nitride; and

a binder matrix comprising a second, different material comprising a nickel-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

48. The material as in the above item no. 47, wherein said nitride includes at least one of ZrN, VN, NbN, TaN TiN and HfN.

49. The material as in the above item no. 33 or 47, wherein said nickel-based superalloy comprises primarily nickel and also comprises other elements.

50. The material as in the above item no. 49, wherein said other elements include Co, Cr, Al, Ti, Mo, Nb, W, and Zr.

51. A material, comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material which comprises a nickel-based superalloy and a second, different nickel-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

52. The material as in the above item no. 51, wherein said binder matrix further comprises rhenium.

53. The material as in the above item no. 52, wherein said binder matrix further comprises cobalt.

54. The material as in the above item no. 33, wherein said binder matrix further comprises rhenium.

55. A material, comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material which comprises a nickel-based superalloy, rhenium and cobalt, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

56. A material comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material which comprises a nickel-based superalloy and cobalt, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

57. A material, comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material which comprises a nickel-based superalloy and nickel, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

58. A material, comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material which comprises a nickel-based superalloy and iron, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

59. A material, comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material which comprises a nickel-based superalloy molybdenum, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

60. A material, comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material which comprises a nickel-based superalloy and chromium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

61. The material as in the above item no. 33, wherein said binder matrix further comprises another alloy that is not a nickel-based alloy.

62. A material, comprising:

hard particles having a first material comprising TiC and TiN; and

a binder matrix having a second, different material comprising at least one of Ni, Mo, and Mo₂C, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

63. A material, comprising:

hard particles comprising a first material which comprises TiC and TiN; and

a binder matrix comprising a second, different material which comprises Re and at least one of Ni, Mo, and Mo₂C, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

64. The material as in the above item no. 63, wherein said binder matrix further includes Co.

65. The material as in the above item no. 64, wherein said binder matrix further includes a Ni-based superalloy.

66. The material as in the above item no. 63, wherein said binder matrix further includes a Ni-based superalloy.

67. A material, comprising:

hard particles comprising a first material comprising TiC and TiN; and

a binder matrix comprising a second, different material which comprises a Ni-based superalloy, and at least one of Ni, Mo, and Mo₂C, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

68. A method comprising:

forming a grade powder by mixing a powder of hard particles with a binder matrix material comprising a nickel-based superalloy;

processing the grade powder to produce a solid hardmetal material by using the binder matrix material to bind the hard particles.

69. The method as in the above item no. 68, wherein said processing includes sequentially performing a pressing operation, a first sintering operation, a shaping operation, and a second sintering operation.

70. (The method as in the above item no. 68, further comprising: prior to the mixing, preparing the binder matrix material to further include rhenium.

71. The method as in the above item no. 68, further comprising: prior to the mixing, preparing the binder matrix material to further include cobalt.

72. The method as in the above item no. 68, wherein the processing includes a solid phase sintering in a hot isostatic pressing process.

73. The method as in the above item no. 68, wherein the processing includes (1) sintering the grade powder in a solid phase under a vacuum condition, and (2) sintering the grade power in a solid phase under a pressure in an inert gas medium.

74. The method as in the above item no. 68, further comprising: prior to the mixing, preparing the hard particles with a particle dimension less than 0.5 micron to reduce a temperature of the sintering operations.

75. A device, comprising a wear part that removes material from an object, said wear part having a material which comprises:

hard particles having a first material; and

a binder matrix having a second, different material comprising rhenium and a Ni-based super alloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

76. The device as in the above item no. 75, wherein said binder matrix further includes a cobalt.

77. A device, comprising a wear part having a material which comprises: hard particles having a first material; and

a binder matrix of a second, different material comprising a nickel-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

78. A material comprising:

hard particles having a first material selected from at least one from a group consisting of (1) a solid solution of WC, TiC, and TaC, (2) a solid solution of WC, TiC, and NbC, (3) a solid solution of WC, TiC, and at least one of TaC and NbC, and (4) a solid solution of WC, TiC, and at least one of HfC and NbC; and

a binder matrix having a second, different material, a volume of said binder matrix being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

79. The material as in the above item no. 78 or 87, wherein the hard particles comprise WC, TiC, and TaC, and the binder matrix is formed of pure Re.

80. The material as in the above item no. 79, wherein the hard particles are about 72% of and the Re is about 28% of the total weight of the material.

81. The material as in the above item no. 79, wherein the hard particles are about 85% of and the Re is about 15% of the total weight of the material.

82. The material as in the above item no. 79, wherein TiC and TaC are approximately equal in quantity and have a total quantity less than a quantity of the WC.

83. The material as in the above item no. 24, wherein the hard particles comprise WC, TiC, and TaC.

84. The material as in the above item no. 83, wherein each of TiC and TaC is from about 3% to less than about 6% in a total weight of the material, and WC is above 78% and below 89% in the total weight of the material.

85. The material as in the above item no. 83, wherein the binder matrix further includes Co.

86. The material as in the above item no. 83, wherein the Ni-based superalloy comprises mainly Ni and other elements including Co, Cr, Al, Ti, Mo, Nb, W, Zr, B, C, and V.

87. A material, comprising:

hard particles comprising a first material selected from at least one from a group consisting of (1) WC, TiC, and TaC, (2) WC, TiC, and NbC, (3) WC, TiC, and at least one of TaC and NbC, and (4) WC, TiC, and at least one of HfC and NbC; and

a binder matrix comprising a second, different material, a volume of said binder matrix being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner,

wherein the binder matrix includes Re and a Ni-based superalloy which includes Re.

88. The material as in the above item no. 21, wherein said Ni-based superalloy includes Re.

89. The material as in the above item no. 24, wherein said Ni-based superalloy includes Re.

90. The material as in the above item no. 21 or 47, wherein said Ni-based superalloy includes Re.

91. A material comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material which comprises a nickel-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner,

wherein said Ni-based superalloy includes Re.

92. A material, comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material which comprises a nickel-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner,

wherein said Ni-based superalloy is in a γ-γ′ phase.

93. A material, comprising:

hard particles comprising a first material; and

a binder matrix comprising a second, different material which comprises a nickel-based superalloy which comprises nickel and other elements, said other elements comprising Co, Cr, Al, Ti, Mo, Nb, W, Zr, and Re, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

94. The material as in the above item no. 17, wherein said first material comprises a boride.

95. The material as in the above item no. 95, wherein said boride is one of TiB₂, ZrB₂, HfB₂, TaB₂, VB₂, MoB₂, WB, and W₂B.

96. The material as in the above item no. 17, wherein said first material comprises a silicide.

97. The material as in the above item no. 96, wherein said silicide is one of TaSi₂, WSi₂, NbSi₂, and MoSi₂.

98. The material as in the above item no. 17, wherein said first material comprises a carbide.

99. The material as in the above item no. 98, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

100. The material as in the above item no. 17, wherein said first material further comprises a nitride.

101. The material as in the above item no. 100, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

102. The material as in the above item no. 100, wherein said first material further comprises a carbide.

103. The material as in the above item no. 102, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

104. The material as in the above item no. 102, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

105. The material as in the above item no. 18, wherein said first material comprises a boride.

106. The material as in the above item no. 105, wherein said boride is one of TiB₂, ZrB₂, HfB₂, TaB₂, VB₂, MoB₂, WB, and W₂B.

107. The material as in the above item no. 18, wherein said first material comprises a silicide.

108. The material as in the above item no. 107, wherein said silicide is one of TaSi₂, Wsi₂, NbSi₂, and MoSi₂.

109. The material as in the above item no. 18, wherein said first material comprises a carbide.

110. The material as in the above item no. 109, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

111. The material as in the above item no. 18, wherein said first material further comprises a nitride.

112. The material as in the above item no. 111, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

113. The material as in the above item no. 111, wherein said first material further comprises a carbide.

114. The material as in the above item no. 113, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

115. The material as in the above item no. 113, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

116. The material as in the above item no. 19, wherein said first material comprises a carbide.

117. The material as in the above item no. 116, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

118. The material as in the above item no. 19, wherein said first material comprises a boride.

119. The material as in the above item no. 118, wherein said boride is one of TiB₂, ZrB₂, HfB₂, TaB₂, VB₂, MoB₂, WB, and W₂B.

120. The material as in the above item no. 19, wherein said first material comprises a silicide.

121. The material as in the above item no. 120, wherein said silicide is one of TaSi₂, Wsi₂, NbSi₂, and MoSi₂.

122. The material as in the above item no. 19, wherein said first material further comprises a nitride.

123. The material as in the above item no. 122, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

124. The material as in the above item no. 122, wherein said first material further comprises a carbide.

125. The material as in the above item no. 124, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

126. The material as in the above item no. 125, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

127. The material as in the above item no. 20, wherein said first material comprises a boride.

128. The material as in the above item no. 127, wherein said boride is one of TiB₂, ZrB₂, HfB₂, TaB₂, VB₂, MoB₂, WB, and W₂B.

129. The material as in the above item no. 20, wherein said first material comprises a silicide.

130. The material as in the above item no. 129, wherein said silicide is one of TaSi₂, Wsi₂, NbSi₂, and MoSi₂.

131. The material as in the above item no. 20, wherein said first material comprises a carbide.

132. The material as in the above item no. 131, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

133. The material as in the above item no. 20, wherein said first material further comprises a nitride.

134. The material as in the above item no. 133, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

135. The material as in the above item no. 133, wherein said first material further comprises a carbide.

136. The material as in the above item no. 135, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

137. The material as in the above item no. 135, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

138. The material as in the above item no. 21, wherein said first material comprises a carbide.

139. The material as in the above item no. 138, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

140. The material as in the above item no. 21, wherein said first material comprises a boride.

141. The material as in the above item no. 140, wherein said boride is one of TiB₂, ZrB₂, HfB₂, TaB₂, VB₂, MoB₂, WB, and W₂B.

142. The material as in the above item no. 21, wherein said first material comprises a silicide.

143. The material as in the above item no. 142, wherein said silicide is one of TaSi₂, Wsi₂, NbSi₂, and MoSi₂.

144. The material as in the above item no. 21, wherein said first material comprises a nitride.

145. The material as in the above item no. 144, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

146. The material as in the above item no. 144, wherein said first material further comprises a carbide.

147. The material as in the above item no. 146, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

148. The material as in the above item no. 147, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

149. The material as in the above item no. 22, wherein said first material comprises a boride.

150. The material as in the above item no. 149, wherein said boride is one of TiB₂, ZrB₂, HfB₂, TaB₂, VB₂, MoB₂, WB, and W₂B.

151. The material as in the above item no. 22, wherein said first material comprises a silicide.

152. The material as in the above item no. 151, wherein said silicide is one of TaSi₂, Wsi₂, NbSi₂, and MoSi₂.

153. The material as in the above item no. 22, wherein said first material comprises a carbide.

154. The material as in the above item no. 153, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

155. The material as in the above item no. 22, wherein said first material further comprises a nitride.

156. The material as in the above item no. 155, wherein said nitride includes at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

157. The material as in the above item no. 155, wherein said first material further comprises a carbide.

158. The material as in the above item no. 157, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

159. The material as in the above item no. 157, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

160. The material as in the above item no. 24, wherein said first material further comprises a nitride.

161. The material as in the above item no. 160, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

162. The material as in the above item no. 24, wherein said binder matrix further comprises cobalt(Co).

163. The material as in the above item no. 24, wherein Re is from about 1.5% to about 24.4% of the total weight of the material, and said Ni-based superalloy is from about 0.86% to about 4.88% of the total weight of the material, and

wherein the first material comprises TiC which is from about 3% to about 14.7% of the total weight of the material, TaC which is from about 3% to about 6.2% of the total weight of the material, and WC which is above about 64% and below about 88% of the total weight of the material.

164. The material as in the above item no. 26, wherein said binder matrix further comprises a Ni-based superalloy.

165. The material as in the above item no. 164, wherein said binder matrix further comprises Co.

166. The material as in the above item no. 27, wherein said binder matrix further comprises Co.

167. The material as in the above item no. 27, wherein said Re is from about 8.8% to about 23.8% of the total weight of the material, and said Ni-based superalloy is from about 3.0% to about 10.3% of the total weight of the material, and wherein said Mo₂C is from about 13.8% to about 15.2% of the total weight of the material, and said TiC is from about 59.4% to about 65.7% of the total weight of the material.

168. The material as in the above item no. 47, wherein said first material further comprises a carbide.

169. The material as in the above item no. 168, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

170. The material as in the above item no. 168, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

171. The material as in the above item no. 49, wherein said other elements comprise Cr, Co, Fe, Al, Ti, Mo, W, Nb, Ta, Hf, Zr, B, C, Re.

172. The material as in the above item no. 51, wherein said first material comprises a carbide.

173. The material as in the above item no. 172, wherein said first material further comprises a nitride.

174. The material as in the above item no. 50, wherein said other elements further comprise Fe, Ta, Hf, C, and Re.

175. The material as in the above item no. 51, wherein said first material comprises a nitride.

176. The material as in the above item no. 55, wherein Re is from about 0.4% to about 1.8% of the total weight of the material, said Ni-based superalloy from about 2.7% to about 4.5% of the total weight of the material, and said cobalt from about 3% to about 4.8% of the total weight of the material, and

wherein said first material comprises WC which is from about 90.4% to about 91.5% of the total weight of the material, and VC which is from about 0.3% to about 0.6% of the total weight of the material.

177. The material as in the above item no. 55, wherein said first material further comprises a nitride.

178. The material as in the above item no. 55, wherein said first material further comprises a carbide.

179. The material as in the above item no. 56, wherein said first material further comprises a nitride.

180. The material as in the above item no. 179, wherein said first material further comprises a carbide.

181. The material as in the above item no. 56, wherein said first material further comprises a carbide.

182. The material as in the above item no. 57, wherein said first material further comprises a nitride.

183. The material as in the above item no. 182, wherein said first material further comprises a carbide.

184. The material as in the above item no. 57, wherein said first material further comprises a carbide.

185. The material as in the above item no. 58, wherein said first material further comprises a nitride.

186. The material as in the above item no. 185, wherein said first material further comprises a carbide.

187. The material as in the above item no. 58, wherein said first material further comprises a carbide.

188. The material as in the above item no. 59, wherein said first material further comprises a nitride.

189. The material as in the above item no. 188, wherein said first material further comprises a carbide.

190. The material as in the above item no. 59, wherein said first material further comprises a carbide.

191. The material as in the above item no. 60, wherein said first material further comprises a nitride.

192. The material as in the above item no. 191, wherein said first material further comprises a carbide.

193. The material as in the above item no. 60, wherein said first material further comprises a carbide.

194. The device as in the above item no. 75, wherein said first material comprises a carbide.

195. The device as in the above item no. 194, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

196. The device as in the above item no. 75, wherein said first material further comprises a nitride.

197. The device as in the above item no. 196, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

198. The device as in the above item no. 196, wherein said first material further comprises a carbide.

199. The device as in the above item no. 198, wherein said first material comprises WC, TiC, TaC and Mo₂C.

200. The device as in the above item no. 198, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

201. The device as in the above item no. 198, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

202. The device as in the above item no. 75, wherein said first material further comprises a boride.

203. The device as in the above item no. 202, wherein said first material comprises at least one of TiB₂, ZrB₂, HfB₂, TaB₂, VB₂, MoB₂, WB, and W₂B.

204. The device as in the above item no. 75, wherein said first material further comprises at least one boride and at least one carbide.

205. The device as in the above item no. 204, wherein said first material comprises WC, TiC, TaC, and B₄C.

206. The device as in the above item no. 75, wherein said first material comprises a silicide.

207. the device as in the above item no. 75, wherein said first material comprises at least one of TaSi₂, WSi₂, NbSi₂, and MoSi₂.

208. The device as in the above item no. 75, wherein said Re is from about 9.04% to about 9.32% of the total weight of the material, and said Ni-based superalloy is from about 3.53% to about 3.64% of the total weight of the material, and

wherein said first material comprises WC from about 67.24% to about 69.40% of the total weight of the material, TiC from about 6.35% to about 6.55% of the total weight of the material, TaC from about 6.24% to about 6.44% of, TiB₂ from about 0.40% to about 7.39% of the total weight of the material, and B₄C from about 0.22% to about 4.25% of the total weight of the material.

209. The device as in the above item no. 75, wherein said Re is from about 8.96% to about 9.37% of the total weight of the material, and said Ni-based superalloy is from about 3.50% to about 3.66% of the total weight of the material, and

wherein said first material comprises WC from about 58.61% to about 66.67% of the total weight of the material, TiC from about 14.69% to about 15.37% of the total weight of the material, TaC from about 6.19% to about 6.47% of the total weight of the material, and Mo₂C from 0 to about 6.51% of the total weight of the material.

210. The device as in the above item no. 75, wherein said binder matrix further comprises Ni.

211. The device as in the above item no. 75, wherein said binder matrix further comprises Fe.

212. The device as in the above item no. 75, wherein said binder matrix further comprises Mo.

213. The device as in the above item no. 75, wherein said binder matrix further comprises Cr.

214. The material as in the above item no. 83, wherein the Ni-based superalloy comprises mainly Ni and other elements which comprise Cr, Co, Fe, Al, Ti, Mo, W, Nb, Ta, Hf, Zr, B, C, Re.

215. The material as in the above item no. 91, wherein said first material comprises a carbide.

216. The material as in the above item no. 215, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

217. The material as in the above item no. 91, wherein said first material further comprises a nitride.

218. The material as in the above item no. 217, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

219. The material as in the above item no. 217, wherein said first material further comprises a carbide.

220. The material as in the above item no. 219, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

221. The material as in the above item no. 91, wherein said first material further comprises a boride.

222. The material as in the above item no. 221, wherein said first material comprises at least one of TiB₂, ZrB₂, HfB₂, TaB₂, VB₂, MoB₂, WB, and W₂B.

223. The material as in the above item no. 91, wherein said first material further comprises at least one boride and at least one carbide.

224. The material as in the above item no. 223, wherein said first material comprises WC, TiC, TaC, and B₄C.

225. The material as in the above item no. 91, wherein said first material comprises a silicide.

226. The material as in the above item no. 225, wherein said silicide comprises at least one of TaSi₂, WSi₂, NbSi₂, and MoSi₂.

227. The material as in the above item no. 91, wherein said binder matrix further comprises Ni.

228. The material as in the above item no. 91, wherein said binder matrix further comprises Fe.

229. The material as in the above item no. 91, wherein said binder matrix further comprises Mo.

230. The material as in the above item no. 91, wherein said binder matrix further comprises Cr.

231. The material as in the above item no. 92, wherein said first material comprises a carbide.

232. The material as in the above item no. 231, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

233. The material as in the above item no. 92, wherein said first material further comprises a nitride.

234. The material as in the above item no. 233, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

235. The material as in the above item no. 233, wherein said first material further comprises a carbide.

236. The material as in the above item no. 235, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

237. The material as in the above item no. 235, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

238. The material as in the above item no. 92, wherein said first material further comprises a boride.

239. The material as in the above item no. 238, wherein said first material comprises at least one of TiB₂, ZrB₂, HfB₂, TaB₂, VB₂, MoB₂, WB, and W₂B.

240. The material as in the above item no. 92, wherein said first material comprises a silicide.

241. The material as in the above item no. 92, wherein said first material comprises at least one of TaSi₂, WSi₂, NbSi₂, and MoSi₂.

242. The material as in the above item no. 92, wherein said second material further comprises at least one of Re, Ni, Co, Fe, Mo, and Cr.

243. The material as in the above item no. 92, wherein said second material further comprises at least another different Ni-based superalloy.

244. The material as in the above item no. 92, wherein said first material comprises WC from about 91.9% to about 92.5% of the total weight of the material, and VC from about 0.3% to about 0.6% of the total weight of the material, and wherein said Ni-based superalloy is from about 7.2% to about 7.5% of the total weight of the material.

245. The material as in the above item no. 92, wherein said first material comprises TiC and Mo₂C which are about 69.44% and 16.09% of the total weight of the material, respectively, and wherein said Ni-based superalloy is about 14.47% of the total weight of the material.

246. The material as in the above item no. 93, wherein said first material comprises a carbide.

247. The material as in the above item no. 246, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

248. The material as in the above item no. 93, wherein said first material further comprises a nitride.

249. The material as in the above item no. 248, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

250. The material as in the above item no. 249, wherein said first material further comprises a carbide.

251. The material as in the above item no. 250, wherein said carbide comprises at least one of TiC, ZrC, HfC, VC, NbC, TaC, Cr₂C₃, Mo₂C, and WC.

252. The material as in the above item no. 250, wherein said nitride comprises at least one of TiN, ZrN, HfN, VN, NbN, and TaN.

253. The material as in the above item no. 93, wherein said first material further comprises a boride.

254. The material as in the above item no. 253, wherein said first material comprises at least one of TiB₂, ZrB₂, HfB₂, TaB₂, VB₂, MoB₂, WB, and W₂B.

255. The material as in the above item no. 93, wherein said first material comprises a silicide.

256. The material as in the above item no. 93, wherein said first material comprises at least one of TaSi₂, WSi₂, NbSi₂, and MoSi₂.

257. The material as in the above item no. 93, wherein said second material further comprises at least one of Re, Ni, Co, Fe, Mo, and Cr.

258. The material as in the above item no. 93, wherein said second material further comprises at least another different Ni-based superalloy.

259. The material as in the above item no. 93, wherein said other elements in said nickel-based superalloy further comprise Fe, Ta, Hf, B, and C.

260. A method, comprising:

preparing a metal surface for a thermal spray process; and

performing the thermal spray process to coat a layer of a hardmetal layer over the metal surface,

wherein the hard metal layer comprises:

hard particles having a first material, and

a binder matrix having a second, different material, a volume of said second material being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium in an amount greater than 25% of a total weight of the material, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

261. A method, comprising:

preparing a metal surface for a thermal spray process; and

performing the thermal spray process to coat a layer of a hardmetal layer over the metal surface,

wherein the hard metal layer comprises:

hard particles having a first material having a mixture selected from at least one from a group consisting of (1) a mixture of WC, TiC, and TaC, (2) a mixture of WC, TiC, and NbC, (3) a mixture of WC, TiC, and at least one of TaC and NbC, and (4) a mixture of WC, TiC, and at least one of HfC and NbC; and

a binder matrix having a second, different material, a volume of said binder matrix being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

262. A method, comprising:

preparing a metal surface for a thermal spray process; and

performing the thermal spray process to coat a layer of a hardmetal layer over the metal surface,

wherein the hard metal layer comprises:

hard particles having a first material having a mixture of Mo₂C and TiC; and

a binder matrix having a second, different material, a volume of said binder matrix being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

263. A method, comprising:

preparing a metal surface for a thermal spray process; and

performing the thermal spray process to coat a layer of a hardmetal layer over the metal surface,

wherein the hard metal layer comprises:

hard particles having a first material; and

a binder matrix having a second, different material comprising a nickel-based superalloy, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

264. A method, comprising:

preparing a metal surface for a thermal spray process; and

performing the thermal spray process to coat a layer of a hardmetal layer over the metal surface,

wherein the hard metal layer comprises:

hard particles having a first material comprising TiC and TiN; and

a binder matrix having a second, different material comprising at least one of Ni, Mo, and Mo₂C, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

265. A method, comprising:

preparing a metal surface for a thermal spray process; and

performing the thermal spray process to coat a layer of a hardmetal layer over the metal surface,

wherein the hard metal layer comprises:

hard particles having a first material selected from at least one from a group consisting of (1) a solid solution of WC, TiC, and TaC, (2) a solid solution of WC, TiC, and NbC, (3) a solid solution of WC, TiC, and at least one of TaC and NbC, and (4) a solid solution of WC, TiC, and at least one of HfC and NbC; and

a binder matrix having a second, different material, a volume of said binder matrix being from about 3% to about 40% of a total volume of the material, said binder matrix comprising rhenium, wherein said hard particles are spatially dispersed in said binder matrix in a substantially uniform manner.

In addition, a second group of 288 specific implementations described in this application is as follows.

1. A material, comprising:

hard particles comprising at least one carbide selected from at least one of WC, TiC, and HfC; and

a binder matrix that binds the hard particles and comprises rhenium,

wherein the hard particles are less than 75% of a total weight of the material and rhenium is greater than 25% of the total weight of the material.

2. The material as in above item no. 1, wherein the at least one carbide is TiC which is greater than about 26% of the total weight of the material and the rhenium is less than about 74% of the total weight of the material.

3. The material as in above item no. 1, wherein the at least one carbide is WC which is greater than about 53% of the total weight of the material, and the rhenium is less than about 47% of the total weight of the material.

4. The material as in above item no. 1, wherein the at least one carbide is HfC which is greater than about 48% of the total weight of the material, and the rhenium is less than about 52% of the total weight of the material.

5. A material, comprising:

hard particles comprising at least one carbide selected from carbides that are formed from elements in IVb, Vb, and VIb columns of the periodic table of elements, exclusive of WC, TiC, and HfC; and

a binder matrix that binds the hard particles and comprises rhenium, wherein the hard particles are less than 75% of a total weight of the material and rhenium is between 4% to 72% of the total weight of the material.

6. The material as in above item no. 5, wherein the at least one carbide is ZrC which is greater than about 32% of the total weight of the material, and the rhenium is less than about 68% of the total weight of the material.

7. The material as in above item no. 5, wherein the at least one carbide is VC which is greater than about 28% of the total weight of the material, and the rhenium is less than about 72% of the total weight of the material.

8. The material as in above item no. 5, wherein the at least one carbide is NbC which is greater than about 36% of the total weight of the material, and the rhenium is less than about 64% of the total weight of the material.

9. The material as in above item no. 5, wherein the at least one carbide is TaC which is greater than about 51% of the total weight of the material, and the rhenium is less than about 49% of the total weight of the material.

10. The material as in above item no. 5, wherein the at least one carbide is Cr₂C₃ which is greater than about 32% of the total weight of the material, and the rhenium is less than about 68% of the total weight of the material.

11. The material as in above item no. 5, wherein the at least one carbide is Mo₂C which is greater than about 39% of the total weight of the material, and the rhenium is less than about 61% of the total weight of the material.

12. A material, comprising:

hard particles comprising at least one nitride from nitrides of IVB and Vb columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium, wherein the rhenium is between about 4% to about 72% of the total weight of the material.

13. The material as in above item no. 12, wherein the at least one nitride is TiN which is between about 28% to about 89% of the total weight of the material.

14. The material as in above item no. 12, wherein the at least one nitride is ZrN which is between about 34% to about 92% of the total weight of the material, and the rhenium is between about 8% to about 66% of the total weight of the material.

15. The material as in above item no. 12, wherein the at least one nitride is HfN which is between about 50% to about 96% of the total weight of the material, and the rhenium is between about 4% to about 50% of the total weight of the material.

16. The material as in above item no. 12, wherein the at least one nitride is VN which is between about 30% to about 91% of the total weight of the material, and the rhenium is between about 9% to about 70% of the total weight of the material.

17. The material as in above item no. 12, wherein the at least one nitride is NbN which is between about 34% to about 92% of the total weight of the material, and the rhenium is between about 8% to about 66% of the total weight of the material.

18. The material as in above item no. 12, wherein the at least one nitride is TaN which is between about 51% to about 96% of the total weight of the material, and the rhenium is between about 4% to about 49% of the total weight of the material.

19. A material, comprising:

hard particles comprising at least one nitride from nitrides of IVB and Vb columns in the periodic table; and

a binder matrix that binds the hard particles and comprises a Ni-based superalloy which is between about 1.7% to about 50% of a total weight of the material.

20. The material as in above item no. 19, wherein the at least one nitride is TiN between about 50% to about 96% of the total weight of the material and the Ni-based superalloy which is between about 4% to about 50% of the total weight of the material.

21. The material as in above item no. 19, wherein the at least one nitride is ZrN between about 58% to about 97% of the total weight of the material and the Ni-based superalloy which is between about 3% to about 42% of the total weight of the material.

22. The material as in above item no. 19, wherein the at least one nitride is HfN between about 72% to about 98.2% of the total weight of the material and the Ni-based superalloy which is between about 1.8% to about 28% of the total weight of the material.

23. The material as in above item no. 19, wherein the at least one nitride is VN between about 53% to about 96% of the total weight of the material and the Ni-based superalloy which is between about 4% to about 47% of the total weight of the material.

24. The material as in above item no. 19, wherein the at least one nitride is NbN between about 52% to about 97% of the total weight of the material and the Ni-based superalloy which is between about 3% to about 42% of the total weight of the material.

25. The material as in above item no. 19, wherein the at least one nitride is TaN between about 73% to about 98.3% of the total weight of the material and the Ni-based superalloy which is between about 1.7% to about 27% of the total weight of the material.

26. A material, comprising:

hard particles comprising at least one carbide from carbides of IVb, Vb, and VIb columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium and a Ni-based superalloy,

wherein the hard particles are between about 26.1% to about 98.4% of a total weight of the material.

27. The material as in above item no. 26, wherein the at least one carbide is TiC between about 26.1% to about 95.1% of the total weight of the material, the rhenium is not greater than about 73.6% of the total weight of the material, and the Ni-based superalloy is not greater than about 51.1% of the total weight of the material.

28. The material as in above item no. 26, wherein the at least one carbide is ZrC between about 32% to about 96% of the total weight of the material, the rhenium is not greater than about 67.7% of the total weight of the material, and the Ni-based superalloy is not greater than about 44.1% of the total weight of the material.

29. The material as in above item no. 26, wherein the at least one carbide is HfC between about 47.7% to about 98.1% of the total weight of the material, the rhenium is not greater about 52.1% of the total weight of the material, and the Ni-based superalloy is not greater about 29.2% of the total weight of the material.

30. The material as in above item no. 26, wherein the at least one carbide is VC between about 28.3% to about 95.6% of the total weight of the material, the rhenium does not exceed about 71.5% of the total weight of the material, and the Ni-based superalloy does exceed about 48.4% of the total weight of the material.

31. The material as in above item no. 26, wherein the at least one carbide is NbC between about 36% to about 96.9% of the total weight of the material, the rhenium is equal to or less than about 63.8% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 39.9% of the total weight of the material.

32. The material as in above item no. 26, wherein the at least one carbide is TaC between about 51% to about 98.3% of the total weight of the material, the rhenium is equal to or less than about 48.8% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 26.5% of the total weight of the material.

33. The material as in above item no. 26, wherein the at least one carbide is Cr₂C₃ between about 32.4% to about 96.4% of the total weight of the material, the rhenium is equal to or less than about 67.3% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 43.6% of the total weight of the material.

34. The material as in above item no. 26, wherein the at least one carbide is Mo₂C between about 39.6% to about 97.3% of the total weight of the material, the rhenium is equal to or less than about 60.2% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 36.3% of the total weight of the material.

35. The material as in above item no. 26, wherein the at least one carbide is WC between about 52.9% to about 98.4% of the total weight of the material, the rhenium is equal to or less than about 46.9% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 25% of the total weight of the material.

36. A material, comprising:

hard particles comprising at least one nitride from nitrides of IVb and Vb columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium and a Ni-based superalloy,

wherein the hard particles are between about 28% to about 98.3% of a total weight of the material.

37. The material as in above item no. 36, wherein the at least one nitride is TiN between about 28% to about 95.6% of the total weight of the material, the rhenium is equal to or less than about 71.7% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 48.7% of the total weight of the material.

38. The material as in above item no. 36, wherein the at least one nitride is ZrN between about 34.5% to about 96.7% of the total weight of the material, the rhenium is equal to or less than about 65.3% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 41.4% of the total weight of the material.

39. The material as in above item no. 36, wherein the at least one nitride is HfN between about 49.8% to about 98.2% of the total weight of the material, the rhenium is equal to or less than about 50% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 27.5% of the total weight of the material.

40. The material as in above item no. 36, wherein the at least one nitride is VN between about 30% to about 96% of the total weight of the material, the rhenium is equal to or less than about 69.6% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 46.2% of the total weight of the material.

41. The material as in above item no. 36, wherein the at least one nitride is NbN between about 34.4% to about 96.7% of the total weight of the material, the rhenium is equal to or less than about 65.3% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 41.5% of the total weight of the material.

42. The material as in above item no. 36, wherein the at least one nitride is TaN between about 50.7% to about 98.3% of the total weight of the material, the rhenium is equal to or less than about 49.1% of the total weight of the material, and the Ni-based superalloy is equal to or less than about 26.8% of the total weight of the material.

43. A material, comprising:

hard particles comprising at least one carbide from carbides of IVb, Vb, and VIb columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium and cobalt,

wherein the hard particles are between about 26.1% to about 98.2% of a total weight of the material.

44. The material as in above item no. 43, wherein the at least one carbide is TiC between about 26.1% to about 94.6% of the total weight of the material, the rhenium is equal to or less than about 73.6% of the total weight of the material, and the cobalt is equal to or less than about 54.1% of the total weight of the material.

45. The material as in above item no. 43, wherein the at least one carbide is ZrC between about 32% to about 96% of the total weight of the material, the rhenium is equal to or less than about 67.7% of the total weight of the material, and cobalt is equal to or less than about 47.1% of the total weight of the material.

46. The material as in above item no. 43, wherein the at least one carbide is HfC between about 47.6% to about 97.8% of the total weight of the material, the rhenium is equal to or less than about 52.1% of the total weight of the material, and the cobalt is equal to or less than about 31.8% of the total weight of the material.

47. The material as in above item no. 43, wherein the at least one carbide is VC between about 28.3% to about 95.1% of the total weight of the material, the rhenium is equal to or less than about 71.4% of the total weight of the material, and the cobalt is equal to or less than about 51.5% of the total weight of the material.

48. The material as in above item no. 43, wherein the at least one carbide is NbC between about 36% to about 96.5% of the total weight of the material, the rhenium is equal to or less than about 63.8% of the total weight of the material, and the cobalt is equal to or less than about 42.8% of the total weight of the material.

49. The material as in above item no. 43, wherein the at least one carbide is TaC between about 51% to about 98% of the total weight of the material, the rhenium is equal to or less than about 48.8% of the total weight of the material, and the cobalt is equal to or less than about 28.9% of the total weight of the material.

50. The material as in above item no. 43, wherein the at least one carbide is Cr₂C₃ between about 32.4% to about 96% of the total weight of the material, the rhenium is equal to or less than about 67.3% of the total weight of the material, and the cobalt is equal to or less than about 46.6% of the total weight of the material.

51. The material as in above item no. 43, wherein the at least one carbide is Mo₂C between about 39.6% to about 97% of the total weight of the material, the rhenium is equal to or less than about 60.2% of the total weight of the material, and the cobalt is equal to or less than about 39.2% of the total weight of the material.

52. The material as in above item no. 43, wherein the at least one carbide is WC between about 52.9% to about 98.2% of the total weight of the material, the rhenium is equal to or less than about 46.9% of the total weight of the material, and the cobalt is equal to or less than about 27.4% of the total weight of the material.

53. A material, comprising:

hard particles comprising at least one nitride from nitrides of IVb and Vb columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium and cobalt, wherein the hard particles are between about 28% to about 98% of a total weight of the material.

54. The material as in above item no. 53, wherein the at least one nitride is TiN between about 28% to about 95% of the total weight of the material, the rhenium is up to about 71.6% of the total weight of the material, and the cobalt is up to about 51.7% of the total weight of the material.

55. The material as in above item no. 53, wherein the at least one nitride is ZrN between about 34.5% to about 96.3% of the total weight of the material, the rhenium is up to about 65.3% of the total weight of the material, and the cobalt is up to about 44.4% of the total weight of the material.

56. The material as in above item no. 53, wherein the at least one nitride is HfN between about 49.8% to about 98% of the total weight of the material, the rhenium is up to about 50% of the total weight of the material, and the cobalt is up to about 30% of the total weight of the material.

57. The material as in above item no. 53, wherein the at least one nitride is VN between about 30% to about 95.5% of the total weight of the material, the rhenium is up to about 69.6% of the total weight of the material, and the cobalt is up to about 49.3% of the total weight of the material.

58. The material as in above item no. 53, wherein the at least one nitride is NbN between about 34.4% to about 96.3% of the total weight of the material, the rhenium is up to about 65.3% of the total weight of the material, and the cobalt is up to about 44.5% of the total weight of the material.

59. The material as in above item no. 53, wherein the at least one nitride is TaN between about 50.7% to about 98% of the total weight of the material, the rhenium is up to d about 49.1% of the total weight of the material, and the cobalt is up to about 29.2% of the total weight of the material.

60. A material, comprising:

hard particles comprising at least one carbide from carbides of IVb, Vb, and VIb columns in the periodic table; and

a binder matrix that binds the hard particles and comprises a Ni-based superalloy and cobalt,

wherein the hard particles are between about 45% to about 98% of a total weight of the material.

61. The material as in above item no. 60, wherein the at least one carbide is TiC between about 45% to about 95% of the total weight of the material, the Ni-based superalloy is up to about 51.5% of the total weight of the material, and the cobalt is up to about 54.5% of the total weight of the material.

62. The material as in above item no. 60, wherein the at least one carbide is ZrC between about 52% to about 96% of the total weight of the material, the Ni-based superalloy is up to about 44.4% of the total weight of the material, and cobalt is up to about 47.4% of the total weight of the material.

63. The material as in above item no. 60, wherein the at least one carbide is HfC between about 68% to about 98% of the total weight of the material, the Ni-based superalloy is up to about 29% of the total weight of the material, and the cobalt is up to about 32% of the total weight of the material.

64. The material as in above item no. 60, wherein the at least one carbide is VC between about 48% to about 96% of the total weight of the material, the Ni-based superalloy is up to about 49% of the total weight of the material, and the cobalt is up to about 52% of the total weight of the material.

65. The material as in above item no. 60, wherein the at least one carbide is NbC between about 57% to about 97% of the total weight of the material, the Ni-based superalloy is up to about 40% of the total weight of the material, and the cobalt is up to about 43% of the total weight of the material.

66. The material as in above item no. 60, wherein the at least one carbide is TaC between about 71% to about 98% of the total weight of the material, the Ni-based superalloy is up to about 27% of the total weight of the material, and the cobalt is up to about 29% of the total weight of the material.

67. The material as in above item no. 60, wherein the at least one carbide is Cr₂C₃ between about 53% to about 96% of the total weight of the material, the Ni-based superalloy is up to about 67.3% of the total weight of the material, and the cobalt is up to about 44% of the total weight of the material.

68. The material as in above item no. 60, wherein the at least one carbide is Mo₂C between about 60% to about 97% of the total weight of the material, the Ni-based superalloy is up to about 36.5% of the total weight of the material, and the cobalt is up to about 39% of the total weight of the material.

69. The material as in above item no. 60, wherein the at least one carbide is WC between about 72% to about 98% of the total weight of the material, the Ni-based superalloy is up to about 46.9% of the total weight of the material, and the cobalt is up to about 27.5% of the total weight of the material.

70. A material, comprising:

hard particles comprising at least one nitride from nitrides of IVb and Vb columns in the periodic table; and

a binder matrix that binds the hard particles and comprises a Ni-based superalloy and cobalt,

wherein the hard particles are between about 47% to about 98% of a total weight of the material.

71. The material as in above item no. 70, wherein the at least one nitride is TiN between about 47% to about 96% of the total weight of the material, the Ni-based superalloy is up to about 49% of the total weight of the material, and the cobalt is up to about 52% of the total weight of the material.

72. The material as in above item no. 70, wherein the at least one nitride is ZrN between about 55% to about 97% of the total weight of the material, the Ni-based superalloy is up to about 42% of the total weight of the material, and the cobalt is up to about 45% of the total weight of the material.

73. The material as in above item no. 70, wherein the at least one nitride is HfN between about 70% to about 98% of the total weight of the material, the Ni-based superalloy is up to about 31% of the total weight of the material, and the cobalt is up to about 27% of the total weight of the material.

74. The material as in above item no. 70, wherein the at least one nitride is VN between about 50% to about 96% of the total weight of the material, the Ni-based superalloy is up to about 53% of the total weight of the material, and the cobalt is up to about 44% of the total weight of the material.

75. The material as in above item no. 70, wherein the at least one nitride is NbN between about 55% to about 97% of the total weight of the material, the Ni-based superalloy is up to about 47% of the total weight of the material, and the cobalt is up to about 40% of the total weight of the material.

76. The material as in above item no. 70, wherein the at least one nitride is TaN between about 70% to about 98% of the total weight of the material, the Ni-based superalloy is up to about 30% of the total weight of the material, and the cobalt is up to about 26% of the total weight of the material.

77. A material, comprising:

hard particles comprising at least one carbide from carbides of IVb, Vb, and VIb columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium, a Ni-based superalloy and cobalt,

wherein the hard particles are between about 26% to about 98.3% of a total weight of the material.

78. The material as in above item no. 77, wherein the at least one carbide is TiC between about 26% to about 95% of the total weight of the material, the rhenium is up to about 73.6% of the total weight of the material, the Ni-based superalloy is up to about 51.3% of the total weight of the material, and the cobalt is up to about 54.3% of the total weight of the material.

79. The material as in above item no. 77, wherein the at least one carbide is ZrC between about 32% to about 96% of the total weight of the material, the rhenium is up to about 67.7% of the total weight of the material, the Ni-based superalloy is up to about 44.2% of the total weight of the material, and the cobalt is up to about 47.2% of the total weight of the material.

80. The material as in above item no. 77, wherein the at least one carbide is HfC between about 48% to about 98% of the total weight of the material, the rhenium is up to about 52.1% of the total weight of the material, the Ni-based superalloy is up to about 29.3% of the total weight of the material, and the cobalt is up to about 31.8% of the total weight of the material.

81. The material as in above item no. 77, wherein the at least one carbide is VC between about 28% to about 96% of the total weight of the material, the rhenium is up to about 71.5% of the total weight of the material, the Ni-based superalloy is up to about 48.6% of the total weight of the material, and the cobalt is up to about 51.7% of the total weight of the material.

82. The material as in above item no. 77, wherein the at least one carbide is NbC between about 36% to about 97% of the total weight of the material, the rhenium is up to about 63.8% of the total weight of the material, the Ni-based superalloy is up to about 40% of the total weight of the material, and the cobalt is up to about 43% of the total weight of the material.

83. The material as in above item no. 77, wherein the at least one carbide is TaC between about 51% to about 98.3% of the total weight of the material, the rhenium is up to about 48.8% of the total weight of the material, the Ni-based superalloy is up to about 26.6% of the total weight of the material, and the cobalt is up to about 29% of the total weight of the material.

84. The material as in above item no. 77, wherein the at least one carbide is Cr₂C₃ between about 32% to about 96% of the total weight of the material, the rhenium is up to about 67.3% of the total weight of the material, the Ni-based superalloy is up to about 43.8% of the total weight of the material, and the cobalt is up to about 46.8% of the total weight of the material.

85. The material as in above item no. 77, wherein the at least one carbide is Mo₂C between about 39% to about 97% of the total weight of the material, the rhenium is up to about 60.2% of the total weight of the material, the Ni-based superalloy is up to about 36.4% of the total weight of the material, and the cobalt is up to about 39.3% of the total weight of the material.

86. The material as in above item no. 77, wherein the at least one carbide is WC between about 53% to about 98% of the total weight of the material, the rhenium is up to about 46.9% of the total weight of the material, the Ni-based superalloy is up to about 25.1% of the total weight of the material, and the cobalt is up to about 27.5% of the total weight of the material.

87. A material, comprising:

hard particles comprising at least one nitride from nitrides of IVb and Vb columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium, a Ni-based superalloy, and cobalt,

wherein the hard particles are between about 28% to about 98.3% of a total weight of the material.

88. The material as in above item no. 87, wherein the at least one nitride is TiN between about 28% to about 96% of the total weight of the material, the rhenium is up to about 71.6% of the total weight of the material, the Ni-based superalloy is up to about 48.8% of the total weight of the material, and the cobalt is up to about 51.9% of the total weight of the material.

89. The material as in above item no. 87, wherein the at least one nitride is ZrN between about 34% to about 97% of the total weight of the material, the rhenium is up to about 65.3% of the total weight of the material, the Ni-based superalloy is up to about 41.6% of the total weight of the material, and the cobalt is up to about 44.6% of the total weight of the material.

90. The material as in above item no. 87, wherein the at least one nitride is HfN between about 50% to about 98% of the total weight of the material, the rhenium is up to about 50% of the total weight of the material, the Ni-based superalloy is up to about 27.5% of the total weight of the material, and the cobalt is up to about 30% of the total weight of the material.

91. The material as in above item no. 87, wherein the at least one nitride is VN between about 30% to about 96% of the total weight of the material, the rhenium is up to about 60% of the total weight of the material, the Ni-based superalloy is up to about 46.4% of the total weight of the material, and the cobalt is up to about 49% of the total weight of the material.

92. The material as in above item no. 87, wherein the at least one nitride is NbN between about 34% to about 97% of the total weight of the material, the rhenium is up to about 65% of the total weight of the material, the Ni-based superalloy is up to about 42% of the total weight of the material, and the cobalt is up to about 45% of the total weight of the material.

93. The material as in above item no. 87, wherein the at least one nitride is TaN between about 51% to about 98.3% of the total weight of the material, the rhenium is up to about 49% of the total weight of the material, the Ni-based superalloy is up to about 27% of the total weight of the material, and the cobalt is up to about 29% of the total weight of the material.

94. A material, comprising:

hard particles comprising WC and TiC which are between about 40% to about 96% and between about 0.3% to about 21% of a total weight of the material, respectively; and a binder matrix that binds the hard particles and comprises rhenium which is between about 4% to about 54% of the total weight of the material.

95. A material, comprising:

hard particles comprising WC between about 44% to about 96% and TaC up to about 21% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium which is between about 4% to about 48% of the total weight of the material.

96. A material, comprising:

hard particles comprising WC, TiC and TaC which are between about 36% to about 95%, up to about 22%, and up to about 25% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium which is between about 4% to about 48% of a total weight of the material.

97. A material, comprising:

hard particles comprising WC and TiC which are between about 60% to about 98%, and up to about 25% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises a Nickel-based superalloy which is between about 1.5% to about 31% of the total weight of the material.

98. A material, comprising:

hard particles comprising WC and TaC which are between about 63% to about 98%, and up to about 26% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises a Nickel-based superalloy which is between about 1.5% to about 26% of the total weight of the material.

99. A material, comprising:

hard particles comprising WC, TiC and TaC which are between about 51% to about 98%, up to about 23%, and up to about 26% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises a Nickel-based superalloy which is between about 1.5% to about 26% of the total weight of the material.

100. A material, comprising:

hard particles comprising WC and TiC which are between about 40% to about 98%, and up to about 24% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium and a Nickel-based superalloy which are up to about 52% and 29% of the total weight of the material, respectively.

101. A material, comprising:

hard particles comprising WC and TaC which are between about 44% to about 98%, and up to about 24% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium and a Nickel-based superalloy which are up to about 47% and about 25% of the total weight of the material, respectively.

102. A material, comprising:

hard particles comprising WC, TiC and TaC which are between about 40% to about 98%, up to about 23%, and up about 26% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium and a Nickel-based superalloy which are up to about 53% and about 30% of the total weight of the material, respectively.

103. A material, comprising:

hard particles comprising WC and TiC which are between about 40% to about 98%, and up to about 23% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium and cobalt which are up to about 53% and about 31% of the total weight of the material, respectively.

104. A material, comprising:

hard particles comprising WC and TaC which are between about 44% to about 98%, and up to about 24% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium and cobalt which are up to about 47% and about 28% of the total weight of the material, respectively.

105. A material, comprising:

hard particles comprising WC, TiC and TaC which are between about 40% to about 98%, up to about 23%, and up to about 26% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium and cobalt which are up to about 53% and about 33% of the total weight of the material, respectively.

106. A material, comprising:

hard particles comprising WC and TiC which are between about 58% to about 98%, and up to about 24% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises cobalt and a nickel-based superalloy which are up to about 33% and about 29% of the total weight of the material, respectively.

107. A material, comprising:

hard particles comprising WC and TaC which are between about 61% to about 98%, and up to about 24% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises cobalt and a nickel-based superalloy which are up to about 28% and about 25% of the total weight of the material, respectively.

108. A material, comprising:

hard particles comprising WC, TiC and TaC which are between about 57% to about 98%, up to about 23%, and up to about 26% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises cobalt and a nickel-based superalloy which are up to about 33% and about 30% of the total weight of the material, respectively.

109. A material, comprising:

hard particles comprising WC and TiC which are between about 40% to about 98%, and up to about 24% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises cobalt up to about 32% of the total weight of the material, rhenium and a nickel-based superalloy which are up to about 54% and about 29% of the total weight of the material, respectively.

110. A material, comprising:

hard particles comprising WC and TaC which are between about 45% to about 98%, and up to about 24% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises cobalt up to about 28% of the total weight of the material, rhenium and a nickel-based superalloy which are up to about 47% and about 26% of the total weight of the material, respectively. 111. A material, comprising:

hard particles comprising WC, TiC and TaC which are between about 35% to about 93%, up to about 25%, and up to about 26% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises cobalt up to about 44% of the total weight of the material, rhenium and a nickel-based superalloy which are up to about 65% and about 41% of the total weight of the material, respectively.

112. A material, comprising:

hard particles comprising TiC between about 19% to about 88% of a total weight of the material and Mo₂C up to about 38% of the total weight of the material; and

a binder matrix that binds the hard particles and comprises rhenium between about 9.5% to about 65% of the total weight of the material.

113. A material, comprising:

hard particles comprising TiN between about 21% to about 89% of a total weight of the material and Mo₂C up to about 36% of the total weight of the material; and

a binder matrix that binds the hard particles and comprises rhenium between about 9% to about 63% of the total weight of the material.

114. A material, comprising:

hard particles comprising TiC up to about 84% of a total weight of the material, TiN up to about 85% of the total weight of the material, and Mo₂C up to about 36% of the total weight of the material; and

a binder matrix that binds the hard particles and comprises rhenium between about 9% to about 64% of the total weight of the material.

115. A material, comprising:

hard particles comprising TiC up to about 83% of a total weight of the material, TiN up to about 85% of the total weight of the material, Mo₂C up to about 25% of the total weight of the material, WC up to about 39% of the total weight of the material, TaC up to about 30% of the total weight of the material, VC up to about 11% of the total weight of the material, and Cr₂C₃ up to about 16% of the total weight of the material; and

a binder matrix that binds the hard particles and comprises rhenium between about 6% to about 65% of the total weight of the material.

116. A material, comprising:

hard particles comprising TiC and Mo₂C which are between about 30% to about 90% and up to about 40% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises a nickel based superalloy which is between about 4% to about 41% of the total weight of the material.

117. A material, comprising:

hard particles comprising TiN and Mo₂C which are up to about 91% and up to about 38% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises a nickel based superalloy which is between about 4% to about 38% of the total weight of the material.

118. A material, comprising:

hard particles comprising TiC, TiN and Mo₂C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises a nickel based superalloy which is between about 4% to about 40% of the total weight of the material.

119. A material, comprising:

hard particles comprising TiC, TiN, Mo₂C, WC, and TaC which are up to about 90%, about 90%, about 25%, about 42%, and about 36% of a total weight of the material, respectively, the hard particles further comprising VC and Cr₂C₃ up to about 14% and 18% of the total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises a nickel based superalloy which is between about 2% to about 40% of the total weight of the material.

120. A material, comprising:

hard particles comprising TiC, TiN and Mo₂C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium and a nickel based superalloy which are up to about 64% and about 40% of the total weight of the material, respectively.

121. A material, comprising:

hard particles comprising TiC, TiN, Mo₂C, WC, and TaC which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr₂C₃ up to about 16% and 18% of the total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium and a nickel based superalloy which are up to about 64% and about 40% of the total weight of the material, respectively.

122. A material, comprising:

hard particles comprising TiC, TiN and Mo₂C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium and nickel which are up to about 64% and about 42% of the total weight of the material, respectively.

123. A material, comprising:

hard particles comprising TiC, TiN, Mo₂C, WC, and TaC which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr₂C₃ up to about 16% and 18% of the total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium and nickel which are up to about 64% and about 42% of the total weight of the material, respectively.

124. A material, comprising:

hard particles comprising TiC, TiN and Mo₂C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium and cobalt which are up to about 64% and about 43% of the total weight of the material, respectively.

125. A material, comprising:

hard particles comprising TiC, TiN, Mo₂C, WC, and TaC which are up to about 89%, about 90%, about 26%, about 42%, and about 32% of a total weight of the material, respectively,

the hard particles further comprising VC and Cr₂C₃ up to about 16% and 18% of the total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium and cobalt which are up to about 64% and about 43% of the total weight of the material, respectively.

126. A material, comprising:

hard particles comprising TiC, TiN and Mo₂C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises a nickel-based superalloy and cobalt which are up to about 40% and about 43% of the total weight of the material, respectively.

127. A material, comprising:

hard particles comprising TiC, TiN, Mo₂C, WC, and TaC which are up to about 89%, about 90%, about 26%, between about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr₂C₃ up to about 16% and 18% of the total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises a nickel-based superalloy and cobalt which are up to about 40% and about 43% of the total weight of the material, respectively.

128. A material, comprising:

hard particles comprising TiC, TiN and Mo₂C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises a nickel-based superalloy and nickel which are up to about 40% and about 43% of the total weight of the material, respectively.

129. A material, comprising:

hard particles comprising TiC, TiN, Mo₂C, WC, and TaC which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr₂C₃ up to about 16% and 18% of the total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises a nickel-based superalloy and nickel which are up to about 40% and about 43% of the total weight of the material, respectively.

130. A material, comprising:

hard particles comprising TiC, TiN and Mo₂C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium, a nickel-based superalloy and cobalt which are up to about 64%, about 40% and about 42% of the total weight of the material, respectively.

131. A material, comprising:

hard particles comprising TiC, TiN, Mo₂C, WC, and TaC which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr₂C₃ up to about 16% and 18% of the total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium, a nickel-based superalloy and cobalt which are up to about 63%, about 39% and about 42% of the total weight of the material, respectively.

132. A material, comprising:

hard particles comprising TiC, TiN and Mo₂C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium, a nickel-based superalloy and nickel which are up to about 63%, about 40% and about 42% of the total weight of the material, respectively.

133. A material, comprising:

hard particles comprising TiC, TiN, Mo₂C, WC, and TaC which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr₂C₃ up to about 16% and 18% of the total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium, a nickel-based superalloy and nickel which are up to about 63%, about 39% and about 42% of the total weight of the material, respectively.

134. A material, comprising:

hard particles comprising TiC, TiN and Mo₂C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium, nickel and cobalt which are up to about 63%, about 42% and about 42% of the total weight of the material, respectively.

135. A material, comprising:

hard particles comprising TiC, TiN, Mo₂C, WC, and TaC which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr₂C₃ up to about 16% and 18% of the total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium, a nickel and cobalt which are up to about 63%, about 42% and about 42% of the total weight of the material, respectively . . . .

136. A material, comprising:

hard particles comprising TiC, TiN and Mo₂C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises a nickel-based superalloy, nickel and cobalt which are up to about 40%, about 42% and about 43% of the total weight of the material, respectively.

137. A material, comprising:

hard particles comprising TiC, TiN, Mo₂C, WC, and TaC which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr₂C₃ up to about 16% and 18% of the total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises a nickel-based superalloy, nickel and cobalt which are up to about 40%, about 42% and about 42% of the total weight of the material, respectively.

138. A material, comprising:

hard particles comprising TiC, TiN and Mo₂C which are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium, a nickel-based superalloy, nickel and cobalt which are up to about 63%, about 39%, about 42% and about 42% of the total weight of the material, respectively.

139. A material, comprising:

hard particles comprising TiC, TiN, Mo₂C, WC, and TaC which are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, the hard particles further comprising VC and Cr₂C₃ up to about 16% and 18% of the total weight of the material, respectively; and

a binder matrix that binds the hard particles and comprises rhenium, a nickel-based superalloy, nickel and cobalt which are up to about 63%, about 39%, about 42% and about 42% of the total weight of the material, respectively.

140. A material, comprising:

hard particles comprising at least one boride from borides of IVB, VB and VIB columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium, wherein the rhenium is between about 4% to about 76% of the total weight of the material.

141. The material as in above item no. 140, wherein the at least one boride is TiB₂ which is between about 24% to about 87.5% of the total weight of the material, and the rhenium is between about 12.5% to about 76% of the total weight of the material.

142. The material as in above item no. 140, wherein the at least one boride is ZrB₂ which is between about 30% to about 90.5% of the total weight of the material, and the rhenium is between about 9.5% to about 70% of the total weight of the material.

143. The material as in above item no. 140, wherein the at least one boride is HfB₂ which is between about 44.5% to about 94.5% of the total weight of the material, and the rhenium is between about 5.5% to about 55.5% of the total weight of the material.

144. The material as in above item no. 140, wherein the at least one boride is VB₂ which is between about 27% to about 89% of the total weight of the material, and the rhenium is between about 11% to about 73% of the total weight of the material.

145. The material as in above item no. 140, wherein the at least one boride is NbB₂ which is between about 34% to about 92% of the total weight of the material, and the rhenium is between about 8% to about 66% of the total weight of the material.

146. The material as in above item no. 140, wherein the at least one boride is TaB₂ which is between about 47% to about 95% of the total weight of the material, and the rhenium is between about 5% to about 53% of the total weight of the material.

147. The material as in above item no. 140, wherein the at least one boride is Cr₃B₂ which is between about 30.5% to about 90.5% of the total weight of the material, and the rhenium is between about 9.5% to about 69.5% of the total weight of the material.

148. The material as in above item no. 140, wherein the at least one boride is MoB₂ which is between about 36% to about 92.5% of the total weight of the material, and the rhenium is between about 7.5% to about 64% of the total weight of the material.

149. The material as in above item no. 140, wherein the at least one boride is WB which is between about 53% to about 96% of the total weight of the material, and the rhenium is between about 4% to about 47% of the total weight of the material.

150. The material as in above item no. 140, wherein the at least one boride is W₂B which is between about 53% to about 96% of the total weight of the material, and the rhenium is between about 4% to about 47% of the total weight of the material.

151. A material, comprising:

hard particles comprising at least one silicide from silicides of IVB, VB and VIB columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium, wherein the rhenium is between about 6% to about 77% of the total weight of the material.

152. The material as in above item no. 151, wherein the at least one silicide is Ti₅Si₃ which is between about 23% to about 87% of the total weight of the material, and the rhenium is between about 13% to about 77% of the total weight of the material.

153. The material as in above item no. 151, wherein the at least one silicide is Zr₆Si₅ which is between about 28% to about 90% of the total weight of the material, and the rhenium is between about 10% to about 72% of the total weight of the material.

154. The material as in above item no. 151, wherein the at least one silicide is NbSi₂ which is between about 31% to about 91% of the total weight of the material, and the rhenium is between about 9% to about 69% of the total weight of the material.

155. The material as in above item no. 151, wherein the at least one silicide is TaSi₂ which is between about 38% to about 93% of the total weight of the material, and the rhenium is between about 7% to about 62% of the total weight of the material.

156. The material as in above item no. 151, wherein the at least one silicide is MoSi₂ which is between about 31% to about 91% of the total weight of the material, and the rhenium is between about 9% to about 69% of the total weight of the material.

157. The material as in above item no. 151, wherein the at least one silicide is WSi₂ which is between about 40% to about 94% of the total weight of the material, and the rhenium is between about 6% to about 60% of the total weight of the material.

158. A material, comprising:

hard particles; and

a binder matrix that binds the hard particles and comprises tungsten.

159. The material as in above item no. 158, wherein the hard particles comprise at least one carbide from carbides of IVB, VB and VIB columns in the periodic table and the tungsten is between about 4% to about 72% of the total weight of the material.

160. The material as in above item no.159, wherein the at least one carbide is TiC which is between about 28% and about 89% of the total weight of the material, and the tungsten is between about 11% and about 72% of the total weight of the material.

161. The material as in above item no. 159, wherein the at least one carbide is ZrC which is between about 34% and about 92% of the total weight of the material, and the tungsten is between about 8% and about 66% of the total weight of the material.

162. The material as in above item no. 159, wherein the at least one carbide is HfC which is between about 50% and about 96% of the total weight of the material, and the tungsten is between about 4% and about 50% of the total weight of the material.

163. The material as in above item no. 159, wherein the at least one carbide is VC which is between about 30% and about 90% of the total weight of the material, and the tungsten is between about 10% and about 70% of the total weight of the material.

164. The material as in above item no. 159, wherein the at least one carbide is NbC which is between about 38% and about 93% of the total weight of the material, and the tungsten is between about 7% and about 62% of the total weight of the material.

165. The material as in above item no. 159, wherein the at least one carbide is TaC which is between about 53% and about 96% of the total weight of the material, and the tungsten is between about 4% and about 47% of the total weight of the material.

166. The material as in above item no. 159, wherein the at least one carbide is Cr₂C₃ which is between about 34% and about 92% of the total weight of the material, and the tungsten is between about 8% and about 66% of the total weight of the material.

167. The material as in above item no. 159, wherein the at least one carbide is Mo₂C which is between about 41% and about 94% of the total weight of the material, and the tungsten is between about 6% and about 59% of the total weight of the material.

168. The material as in above item no. 159, wherein the at least one carbide is WC which is between about 55% and about 96% of the total weight of the material, and the tungsten is between about 4% and about 45% of the total weight of the material.

169. The material as in above item no. 158, wherein the hard particles comprise at least one nitride from nitrides of IVB and VB columns in the periodic table and the tungsten is between about 4% and about 72% of the total weight of the material.

170. The material as in above item no. 169, wherein the at least one nitride is TiN which is between about 28% and about 89% of the total weight of the material, and the tungsten is between about 11% and about 72% of the total weight of the material.

171. The material as in above item no. 169, wherein the at least one nitride is ZrN which is between about 36% and about 92% of the total weight of the material, and the tungsten is between about 8% and about 64% of the total weight of the material.

172. The material as in above item no. 169, wherein the at least one nitride is HfN which is between about 52% and about 96% of the total weight of the material, and the tungsten is between about 4% and about 48% of the total weight of the material.

173. The material as in above item no. 169, wherein the at least one nitride is VN which is between about 32% and about 91% of the total weight of the material, and the tungsten is between about 9% and about 68% of the total weight of the material.

174. The material as in above item no. 169, wherein the at least one nitride is NbN which is between about 36% and about 92% of the total weight of the material, and the tungsten is between about 8% and about 64% of the total weight of the material.

175. The material as in above item no. 169, wherein the at least one nitride is TaN which is between about 53% and about 96% of the total weight of the material, and the tungsten is between about 4% and about 47% of the total weight of the material.

176. The material as in above item no. 158, wherein the hard particles comprise at least one boride from borides of IVB, VB and VIB columns in the periodic table and the tungsten is between about 3% and about 74% of the total weight of the material.

177. The material as in above item no. 176, wherein the at least one boride is TiB₂ which is between about 26% and about 88% of the total weight of the material, and the tungsten is between about 12% and about 74% of the total weight of the material.

178. The material as in above item no. 176, wherein the at least one boride is ZrB₂ which is between about 32% and about 91% of the total weight of the material, and the tungsten is between about 9% and about 68% of the total weight of the material.

179. The material as in above item no. 176, wherein the at least one boride is HfB₂ which is between about 46% and about 95% of the total weight of the material, and the tungsten is between about 5% and about 54% of the total weight of the material.

180. The material as in above item no. 176, wherein the at least one boride is VB₂ which is between about 28% and about 90% of the total weight of the material, and the tungsten is between about 10% and about 72% of the total weight of the material.

181. The material as in above item no. 176, wherein the at least one boride is NbB₂ which is between about 36% and about 92% of the total weight of the material, and the tungsten is between about 8% and about 64% of the total weight of the material.

182. The material as in above item no. 176, wherein the at least one boride is TaB₂ which is between about 49% and about 95% of the total weight of the material, and the tungsten is between about 5% and about 51% of the total weight of the material.

183. The material as in above item no. 176, wherein the at least one boride is Cr₃B₂ which is between about 32% and about 91% of the total weight of the material, and the tungsten is between about 9% and about 68% of the total weight of the material.

184. The material as in above item no. 176, wherein the at least one boride is MoB₂ which is between about 38% and about 93% of the total weight of the material, and the tungsten is between about 7% and about 62% of the total weight of the material.

185. The material as in above item no. 176, wherein the at least one boride is WB which is between about 55% and about 96% of the total weight of the material, and the tungsten is between about 4% and about 45% of the total weight of the material.

186. The material as in above item no. 176, wherein the at least one boride is W₂B which is between about 56% and about 97% of the total weight of the material, and the tungsten is between about 3% and about 44% of the total weight of the material.

187. The material as in above item no. 158, wherein the hard particles comprise at least one silicide from silicides of IVB, VB and VIB columns in the periodic table and the tungsten is between about 6% and about 75% of the total weight of the material.

188. The material as in above item no. 187, wherein the at least one silicide is Ti₅Si₃ which is between about 25% and about 88% of the total weight of the material, and the tungsten is between about 12% and about 75% of the total weight of the material.

189. The material as in above item no. 187, wherein the at least one silicide is Zr₆Si₅ which is between about 30% and about 90% of the total weight of the material, and the tungsten is between about 10% and about 70% of the total weight of the material.

190. The material as in above item no. 187, wherein the at least one silicide is NbSi₂ which is between about 33% and about 91% of the total weight of the material, and the tungsten is between about 9% and about 67% of the total weight of the material.

191. The material as in above item no. 187, wherein the at least one silicide is TaSi₂ which is between about 40% and about 93% of the total weight of the material, and the tungsten is between about 7% and about 60% of the total weight of the material.

192. The material as in above item no. 187, wherein the at least one silicide is MoSi₂ which is between about 31% and about 91% of the total weight of the material, and the tungsten is between about 9% and about 67% of the total weight of the material.

193. The material as in above item no. 187, wherein the at least one silicide is WSi₂ which is between about 42% and about 94% of the total weight of the material, and the tungsten is between about 6% and about 58% of the total weight of the material.

194. The material as in above item no. 158, wherein the binder matrix material further comprises rhenium in addition to tungsten.

195. The material as in above item no. 194, wherein the hard particles comprise at least one carbide from carbides of IVB, VB and VIB columns in the periodic table, and

wherein the rhenium is less than about 73% and tungsten is less than about 72% of the total weight of the material.

196. The material as in above item no. 195, wherein the at least one carbide is TiC which is between about 26% and about 89% of the total weight of the material.

197. The material as in above item no. 195, wherein the at least one carbide is ZrC which is between about 32% and about 92% of the total weight of the material.

198. The material as in above item no. 195, wherein the at least one carbide is HfC which is between about 48% and about 95% of the total weight of the material.

199. The material as in above item no. 195, wherein the at least one carbide is VC which is between about 28% and about 90% of the total weight of the material.

200. The material as in above item no. 195, wherein the at least one carbide is NbC which is between about 36% and about 93% of the total weight of the material.

201. The material as in above item no. 195, wherein the at least one carbide is TaC which is between about 51% and about 96% of the total weight of the material.

202. The material as in above item no. 195, wherein the at least one carbide is Cr₂C₃ which is between about 32% and about 92% of the total weight of the material.

203. The material as in above item no. 195, wherein the at least one carbide is Mo₂C which is between about 39% and about 94% of the total weight of the material.

204. The material as in above item no. 195, wherein the at least one carbide is WC which is between about 53% and about 96% of the total weight of the material.

205. The material as in above item no. 194, wherein the hard particles comprise at least one nitride from nitrides of IVB and VB columns in the periodic table, and

wherein the rhenium is less than about 71% and tungsten is less than about 70% of the total weight of the material.

206. The material as in above item no. 205, wherein the at least one nitride is TiN which is between about 28% and about 90% of the total weight of the material.

207. The material as in above item no. 205, wherein the at least one nitride is ZrN which is between about 34% and about 92% of the total weight of the material.

208. The material as in above item no. 205, wherein the at least one nitride is HfN which is between about 50% and about 96% of the total weight of the material.

209. The material as in above item no. 205, wherein the at least one nitride is VN which is between about 30% and about 91% of the total weight of the material.

210. The material as in above item no. 205, wherein the at least one nitride is NbN which is between about 35% and about 92% of the total weight of the material.

211. The material as in above item no. 205, wherein the at least one nitride is TaN which is between about 51% and about 96% of the total weight of the material.

212. The material as in above item no. 194, wherein the hard particles comprise at least one boride from borides of IVB, VB and VIB columns in the periodic table, and

wherein the rhenium is less than about 75% and tungsten is less than about 73% of the total weight of the material.

213. The material as in above item no. 212, wherein the at least one boride is TiB₂ which is between about 24% and about 88% of the total weight of the material.

214. The material as in above item no. 212, wherein the at least one boride is ZrB₂ which is between about 30% and about 91% of the total weight of the material.

215. The material as in above item no. 212, wherein the at least one boride is HfB₂ which is between about 44% and about 95% of the total weight of the material.

215A. The material as in above item no. 212, wherein the at least one boride is VB₂ which is between about 27% and about 90% of the total weight of the material.

216. The material as in above item no. 212, wherein the at least one boride is NbrB₂ which is between about 34% and about 92% of the total weight of the material.

217. The material as in above item no. 212, wherein the at least one boride is TaB₂ which is between about 47% and about 96% of the total weight of the material.

218. The material as in above item no. 212, wherein the at least one boride is Cr₃B₂ which is between about 32% and about 91% of the total weight of the material.

219. The material as in above item no. 212, wherein the at least one boride is MoB₂ which is between about 36% and about 93% of the total weight of the material.

220. The material as in above item no. 212, wherein the at least one boride is WB which is between about 53% and about 96% of the total weight of the material.

221. The material as in above item no. 212, wherein the at least one boride is W₂B which is between about 54% and about 97% of the total weight of the material.

223. The material as in above item no. 194, wherein the hard particles comprise at least one silicide from silicides of IVB, VB and VIB columns in the periodic table, and

wherein the rhenium is less than about 76% and tungsten is less than about 74% of the total weight of the material.

224. The material as in above item no. 223, wherein the at least one silicide is Ti₅Si₃ which is between about 24% and about 88% of the total weight of the material.

225. The material as in above item no. 223, wherein the at least one silicide is Zr₆Si₅ which is between about 28% and about 90% of the total weight of the material.

226. The material as in above item no. 223, wherein the at least one silicide is NbSi₂ which is between about 31% and about 91% of the total weight of the material.

227. The material as in above item no. 223, wherein the at least one silicide is TaSi₂ which is between about 38% and about 93% of the total weight of the material.

228. The material as in above item no. 223, wherein the at least one silicide is MoSi₂ which is between about 31% and about 91% of the total weight of the material.

229. The material as in above item no. 223, wherein the at least one silicide is WSi₂ which is between about 40% and about 94% of the total weight of the material.

230. A material, comprising:

hard particles comprising at least one nitride from nitrides of IVB and VB columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium which is less than 71% of a total weight of the material and cobalt which is less than 52% of the total weight of the material.

231. The material as in above item no. 230, wherein the at least one nitride is TiN which is between about 28% and about 95% of the total weight of the material.

232. The material as in above item no. 230, wherein the at least one nitride is ZrN which is between about 34% and about 96% of the total weight of the material.

233. The material as in above item no. 230, wherein the at least one nitride is HfN which is between about 50% and about 98% of the total weight of the material.

234. The material as in above item no. 230, wherein the at least one nitride is VN which is between about 30% and about 96% of the total weight of the material.

235. The material as in above item no. 230, wherein the at least one nitride is NbN which is between about 34% and about 96% of the total weight of the material.

236. The material as in above item no. 230, wherein the at least one nitride is TaN which is between about 51% and about 98% of the total weight of the material.

237. A material, comprising:

hard particles comprising at least one boride from borides of IVB, VB and VIB columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium which is less than 75% of a total weight of the material and cobalt which is less than 56% of the total weight of the material.

238. The material as in above item no. 237, wherein the at least one boride is TiB₂ which is between about 24% and about 34% of the total weight of the material.

239. The material as in above item no. 237, wherein the at least one boride is ZrB₂ which is between about 30% and about 96% of the total weight of the material.

240. The material as in above item no. 237, wherein the at least one boride is HfB₂ which is between about 45% and about 98% of the total weight of the material.

241. The material as in above item no. 237, wherein the at least one boride is VB₂ which is between about 27% and about 95% of the total weight of the material.

242. The material as in above item no. 237, wherein the at least one boride is NbB₂ which is between about 34% and about 96% of the total weight of the material.

243. The material as in above item no. 237, wherein the at least one boride is TaB₂ which is between about 48% and about 98% of the total weight of the material.

244. The material as in above item no. 237, wherein the at least one boride is Cr₃B₂ which is between about 30% and about 96% of the total weight of the material.

245. The material as in above item no. 237, wherein the at least one boride is MoB₂ which is between about 36% and about 97% of the total weight of the material.

246. The material as in above item no. 237, wherein the at least one boride is WB which is between about 53% and about 98% of the total weight of the material.

247. The material as in above item no. 237, wherein the at least one boride is W₂B which is between about 55% and about 98% of the total weight of the material.

248. A material, comprising:

hard particles comprising at least one silicide from silicides of IVB and VB columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium which is less than 76% of a total weight of the material and cobalt which is less than 57% of the total weight of the material.

249. The material as in above item no. 248, wherein the at least one silicide is Ti₅Si₃ which is between about 24% and about 94% of the total weight of the material.

250. The material as in above item no. 248, wherein the at least one silicide is Zr₆Si₃ which is between about 28% and about 95% of the total weight of the material.

251. The material as in above item no. 248, wherein the at least one silicide is NbSi₂ which is between about 31% and about 96% of the total weight of the material.

252. The material as in above item no. 248, wherein the at least one silicide is TaSi₂ which is between about 38% and about 97% of the total weight of the material.

253. The material as in above item no. 248, wherein the at least one silicide is MoSi₂ which is between about 31% and about 96% of the total weight of the material.

254. The material as in above item no. 248, wherein the at least one silicide is WSi₂ which is between about 40% and about 97% of the total weight of the material.

255. A material, comprising:

hard particles comprising at least one carbide from carbides of IVB, VB and VIB columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium which is less than 74% of a total weight of the material and molybdenum which is less than 57% of the total weight of the material.

256. The material as in above item no. 255, wherein the at least one carbide is TiC which is between about 26% and about 94% of the total weight of the material.

257. The material as in above item no. 255, wherein the at least one carbide is ZrC which is between about 32% and about 95% of the total weight of the material.

258. The material as in above item no. 255, wherein the at least one carbide is HfC which is between about 48% and about 98% of the total weight of the material.

259. The material as in above item no. 255, wherein the at least one carbide is VC which is between about 28% and about 95% of the total weight of the material.

260. The material as in above item no. 255, wherein the at least one carbide is NbC which is between about 36% and about 98% of the total weight of the material.

261. The material as in above item no. 255, wherein the at least one carbide is TaC which is between about 51% and about 98% of the total weight of the material.

262. The material as in above item no. 255, wherein the at least one carbide is Cr₂C₃ which is between about 32% and about 95% of the total weight of the material.

263. The material as in above item no. 255, wherein the at least one carbide is Mo₂C which is between about 40% and about 97% of the total weight of the material.

264. The material as in above item no. 255, wherein the at least one carbide is WC which is between about 53% and about 98% of the total weight of the material.

265. A material, comprising:

hard particles comprising at least one carbide from carbides of IVB, VB and VIB columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium which is less than 74% of a total weight of the material and nickel which is less than 54% of the total weight of the material.

266. The material as in above item no. 265, wherein the at least one carbide is TiC which is between about 26% and about 95% of the total weight of the material.

267. The material as in above item no. 265, wherein the at least one carbide is ZrC which is between about 32% and about 96% of the total weight of the material.

268. The material as in above item no. 265, wherein the at least one carbide is HfC which is between about 48% and about 98% of the total weight of the material.

269. The material as in above item no. 265, wherein the at least one carbide is VC which is between about 28% and about 95% of the total weight of the material.

270. The material as in above item no. 265, wherein the at least one carbide is NbC which is between about 36% and about 97% of the total weight of the material.

271. The material as in above item no. 265, wherein the at least one carbide is TaC which is between about 51% and about 98% of the total weight of the material.

272. The material as in above item no. 265, wherein the at least one carbide is Cr₂C₃ which is between about 32% and about 96% of the total weight of the material.

273. The material as in above item no. 265, wherein the at least one carbide is Mo₂C which is between about 40% and about 97% of the total weight of the material.

274. The material as in above item no. 265, wherein the at least one carbide is WC which is between about 53% and about 98% of the total weight of the material.

275. A material, comprising:

hard particles comprising at least one carbide from carbides of IVB, VB and VIB columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium which is less than 74% of a total weight of the material and chromium which is less than 48% of the total weight of the material.

276. The material as in above item no. 275, wherein the at least one carbide is TiC which is between about 26% and about 96% of the total weight of the material.

277. The material as in above item no. 275, wherein the at least one carbide is ZrC which is between about 32% and about 97% of the total weight of the material.

278. The material as in above item no. 275, wherein the at least one carbide is HfC which is between about 48% and about 98% of the total weight of the material.

279. The material as in above item no. 275, wherein the at least one carbide is VC which is between about 28% and about 95% of the total weight of the material.

280. The material as in above item no. 275, wherein the at least one carbide is NbC which is between about 36% and about 97% of the total weight of the material.

281. The material as in above item no. 275, wherein the at least one carbide is TaC which is between about 51% and about 98% of the total weight of the material.

282. The material as in above item no. 275, wherein the at least one carbide is Cr₂C₃ which is between about 32% and about 97% of the total weight of the material.

283. The material as in above item no. 275, wherein the at least one carbide is Mo₂C which is between about 40% and about 98% of the total weight of the material.

284. The material as in above item no. 275, wherein the at least one carbide is WC which is between about 53% and about 98.6% of the total weight of the material.

285. A method, comprising:

preparing a metal surface for a thermal spray process; and

performing the thermal spray process to deposit a hardmetal over the metal surface,

wherein the hard metal comprises:

hard particles comprising at least a material made of a carbide, nitride, boride, or silicide; and

a binder matrix to bind the hard particles and comprising at least rhenium.

286. A method, comprising:

preparing a metal surface for a thermal spray process; and

performing the thermal spray process to deposit a hardmetal over the metal surface,

wherein the hard metal comprises:

hard particles comprising at least a material made of a carbide, nitride, boride, or silicide; and

a binder matrix to bind the hard particles and comprising at least a Ni-based superalloy.

287. A method, comprising:

preparing a metal surface for a thermal spray process; and

performing the thermal spray process to deposit a hardmetal over the metal surface,

wherein the hard metal comprises:

hard particles comprising at least a material made of a carbide, nitride, boride, or silicide; and

a binder matrix to bind the hard particles and comprising at least tungsten.

These and other features, implementations, and advantages are now described in details with respect to the drawings, the detailed description, and the claims.

1. A material, comprising:

hard particles comprising at least one carbide from carbides of IVb, Vb, and VIb columns in the periodic table; and

a binder matrix that binds the hard particles and comprises a Ni-based superalloy and cobalt.

2. The material as in claim 1, wherein the hard particles are between about 45% to about 98% of a total weight of the material.

3. The material as in claim 1, wherein the hard particles comprise WC and TiC.

4. The material as in claim 3, wherein WC and TiC are between about 58% to about 98%, and up to about 24% of a total weight of the material, respectively, and

wherein cobalt and the nickel-based superalloy are up to about 33% and about 29% of the total weight of the material, respectively.

5. The material as in claim 1, wherein the hard particles comprise WC and TaC.

6. The material as in claim 5, wherein WC and TaC are between about 61% to about 98%, and up to about 24% of a total weight of the material, respectively, and

wherein cobalt and the nickel-based superalloy are up to about 28% and about 25% of the total weight of the material, respectively.

7. A material, comprising:

hard particles comprising hard particles comprising at least one carbide from carbides of IVb, Vb, and VIb columns in the periodic table; and

a binder matrix that binds the hard particles and comprises a nickel-based superalloy.

8. The material as in claim 7, wherein the at least one carbide comprise TiC and Mo₂C.

9. The material as in claim 8, wherein TiC and Mo₂Care between about 30% to about 90% and up to about 40% of a total weight of the material, respectively; and

wherein the nickel-based superalloy is between about 4% to about 41% of the total weight of the material.

10. The material as in claim 7, wherein the at least one carbide comprise Mo₂C, and wherein the hard particles further comprise TiN.

11. The material as in claim 10, wherein TiN and Mo₂C are up to about 91% and up to about 38% of a total weight of the material, respectively; and

wherein the nickel-based superalloy is between about 4% to about 38% of the total weight of the material.

12. The material as in claim 10, wherein the at least one carbide comprise TiC.

13. The material as in claim 12, wherein TiC, TiN and Mo₂C are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and

wherein the nickel based superalloy which is between about 4% to about 40% of the total weight of the material.

14. The material as in claim 10, wherein the at least one carbide comprise TiC, WC, TaC, VC and Cr₂C₃.

15. The material as in claim 14, wherein TiC, TiN, Mo₂C, WC, and TaC are up to about 90%, about 90%, about 25%, about 42%, and about 36% of a total weight of the material, respectively, and VC and Cr₂C₃ are up to about 14% and 18% of the total weight of the material, respectively; and

wherein the nickel based superalloy is between about 2% to about 40% of the total weight of the material.

16. A material, comprising:

hard particles comprising hard particles comprising TiN and at least one carbide from carbides of IVb, Vb, and VIb columns in the periodic table; and

a binder matrix that binds the hard particles and comprises rhenium, a nickel-based superalloy and cobalt.

17. The material as in claim 16, wherein the at least one carbide comprise TiC and Mo₂C.

18. The material as in claim 17, wherein TiC, TiN and Mo₂C are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and

wherein rhenium, the nickel-based superalloy and cobalt are up to about 64%, about 40% and about 42% of the total weight of the material, respectively.

19. The material as in claim 16, wherein the at least one carbide comprise TiC, Mo₂C, WC, TaC, VC and Cr₂C₃.

20. The material as in claim 19, wherein TiC, TiN, Mo₂C, WC, and TaC are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, and VC and Cr₂C₃ are up to about 16% and 18% of the total weight of the material, respectively; and

wherein rhenium, the nickel-based superalloy and cobalt are up to about 63%, about 39% and about 42% of the total weight of the material, respectively.

21. The material as in claim 1, wherein the hard particles comprise WC, TiC and TaC.

22. The material as in claim 21, wherein WC, TiC and TaC are between about 57% to about 98%, up to about 23%, and up to about 26% of a total weight of the material, respectively, and

wherein cobalt and the nickel-based superalloy are up to about 33% and about 30% of the total weight of the material, respectively.

23. The material as in claim 1, wherein the at least one carbide comprise TiC and Mo₂C, and wherein the hard particles further comprise TiN.

24. The material as in claim 23, wherein TiC, TiN and Mo₂C are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and

wherein the nickel-based superalloy and cobalt are up to about 40% and about 43% of the total weight of the material, respectively.

25. The material as in claim 1, wherein the at least one carbide comprise hard particles comprising TiC, Mo₂C, WC, TaC, VC and Cr₂C₃, and wherein the hard particles further comprise TiN.

26. The material as in claim 25, wherein TiC, TiN, Mo₂C, WC, and TaC are up to about 89%, about 90%, about 26%, between about 42%, and about 33% of a total weight of the material, respectively, and VC and Cr₂C₃ are to about 16% and 18% of the total weight of the material, respectively; and

wherein the nickel-based superalloy and cobalt are up to about 40% and about 43% of the total weight of the material, respectively.

DRAWING DESCRIPTION

FIG. 1 shows one exemplary fabrication flow in making a hardmetal according to one implementation.

FIG. 2 shows an exemplary two-step sintering process for processing hardmetals in a solid state.

FIGS. 3, 4, 5, 6, 7, and 8 show various measured properties of selected exemplary hardmetals.

FIGS. 9 and 10 illustrate examples of the thermal spray methods.

DETAILED DESCRIPTION

Compositions of hardmetals are important in that they directly affect the technical performance of the hardmetals in their intended applications, and processing conditions and equipment used during fabrication of such hardmetals. The hardmetal compositions also can directly affect the cost of the raw materials for the hardmetals, and the costs associated with the fabrication processes. For these and other reasons, extensive efforts have been made in the hardmetal industry to develop technically superior and economically feasible compositions for hardmetals. This application describes, among other features, material compositions for hardmetals with selected binder matrix materials that, together, provide performance advantages.

Material compositions for hardmetals of interest include various hard particles and various binder matrix materials. In general, the hard particles may be formed from carbides of the metals in columns IVB (e.g., TiC, ZrC, HfC), VB (e.g., VC, NbC, TaC), and VIB (e.g., Cr₃C₂, Mo₂C, WC) in the Periodic Table of Elements. In addition, nitrides formed by metals elements in columns IVB (e.g., TiN, ZrN, HfN) and VB (e.g., VN, NbN, and TaN) in the Periodic Table of Elements may also be used. For example, one material composition for hard particles that is widely used for many hardmetals is a tungsten carbide, e.g., the mono tungsten carbide (WC). Various nitrides may be mixed with carbides to form the hard particles. Two or more of the above and other carbides and nitrides may be combined to form WC-based hardmetals or WC-free hardmetals. Examples of mixtures of different carbides include but are not limited to a mixture of WC and TiC, and a mixture of WC, TiC, and TaC. In addition to various carbides, nitrides, carbonitrides, borides, and silicides may also be used as hard particles for hardmetals. Examples of various suitable hard particles are described in this application.

The material composition of the binder matrix, in addition to providing a matrix for bonding the hard particles together, can significantly affect the hard and refractory properties of the resulting hardmetals. In general, the binder matrix may include one or more transition metals in the eighth column of the Periodic Table of Elements, such as cobalt (Co), nickel (Ni), and iron (Fe), and the metals in the 6B column such as molybdenum (Mo) and chromium (Cr). Two or more of such and other binder metals may be mixed together to form desired binder matrices for bonding suitable hard particles. Some binder matrices, for example, use combinations of Co, Ni, and Mo with different relative weights.

The hardmetal compositions described here were developed in part based on a recognition that the material composition of the binder matrix may be specially configured and tailored to provide high-performance hardmetals to meet specific needs of various applications. In particular, the material composition of the binder matrix has significant effects on other material properties of the resulting hardmetals, such as the elasticity, the rigidity, and the strength parameters (including the transverse rupture strength, the tensile strength, and the impact strength). Hence, the inventor recognized that it was desirable to provide the proper material composition for the binder matrix to better match the material composition of the hard particles and other components of the hardmetals in order to enhance the material properties and the performance of the resulting hardmetals.

More specifically, these hardmetal compositions use binder matrices that include rhenium, a nickel-based superalloy or a combination of at least one nickel-based superalloy and other binder materials. Other suitable binder materials may include, among others, rhenium (Re) or cobalt. A Ni-based superalloy exhibits a high material strength at a relatively high temperature. The resulting hardmetal formed with such a binder material can benefit from the high material strength at high temperatures of rhenium and Ni-superalloy and exhibit enhanced performance at high temperatures. In addition, a Ni-based superalloy also exhibits superior resistance to corrosion and oxidation, and thus, when used as a binder material, can improve the corresponding resistance of the hardmetals.

The compositions of the hardmetals described in this application may include the binder matrix material from about 3% to about 40% by volume of the total materials in the hardmetals so that the corresponding volume percentage of the hard particles is about from 97% to about 60%, respectively. Within the above volume percentage range, the binder matrix material in certain implementations may be from about 4% to about 35% by volume out of the volume of the total hardmetal materials. More preferably, some compositions of the hardmetals may have from about 5% to about 30% of the binder matrix material by volume out of the volume of the total hardmetal materials. The weight percentage of the binder matrix material in the total weight of the resulting hardmetals may be derived from the specific compositions of the hardmetals.

In various implementations, the binder matrices may be formed primarily by a nickel-based superalloy, and by various combinations of the nickel-based superalloy with other elements such as Re, Co, Ni, Fe, Mo, and Cr. A Ni-based superalloy of interest may comprise, in addition to Ni, elements Co, Cr, Al, Ti, Mo, W, and other elements such as Ta, Nb, B, Zr and C. For example, Ni-based superalloys may include the following constituent metals in weight percentage of the total weight of the superalloy: Ni from about 30% to about 70%, Cr from about 10% to about 30%, Co from about 0% to about 25%, a total of Al and Ti from about 4% to about 12%, Mo from about 0% to about 10%, W from about 0% to about 10%, Ta from about 0% to about 10%, Nb from about 0% to about 5%, and Hf from about 0% to about 5%. Ni-based superalloys may also include either or both of Re and Hf, e.g., Re from 0% to about 10%, and Hf from 0% to about 5%. Ni-based superalloy with Re may be used in applications under high temperatures. A Ni-based super alloy may further include other elements, such as B, Zr, and C, in small amounts.

Compounds TaC and NbC have similar properties to a certain extent and may be used to partially or completely substitute or replace each other in hardmetal compositions in some implementations. Either one or both of HfC and NbC also may be used to substitute or replace a part or all of TaC in hardmetal designs. Compounds WC, TiC, TaC may be produced individually and then mixed to form a mixture or may be produced in a form of a solid solution. When a mixture is used, the mixture may be selected from at least one from a group consisting of (1) a mixture of WC, TiC, and TaC, (2) a mixture of WC, TiC, and NbC, (3) a mixture of WC, TiC, and at least one of TaC and NbC, and (4) a mixture of WC, TiC, and at least one of HfC and NbC. A solid solution of multiple carbides may exhibit better properties and performances than a mixture of several carbides. Hence, hard particles may be selected from at least one from a group consisting of (1) a solid solution of WC, TiC, and TaC, (2) a solid solution of WC, TiC, and NbC, (3) a solid solution of WC, TiC, and at least one of TaC and NbC, and (4) a solid solution of WC, TiC, and at least one of HfC and NbC.

The nickel-based superalloy as a binder material may be in a γ-γ′ phase where the γ′ phase with a FCC structure mixes with the γ phase. The strength increases with temperature within a certain extent. Another desirable property of such a Ni-based superalloy is its high resistance to oxidation and corrosion. The nickel-based superalloy may be used to either partially or entirely replace Co in various Co-based binder compositions. As demonstrated by examples disclosed in this application, the inclusion of both of rhenium and a nickel-based superalloy in a binder matrix of a hardmetal can significantly improve the performance of the resulting hardmetal by benefiting from the superior performance at high temperatures from presence of Re while utilizing the relatively low-sintering temperature of the Ni-based superalloy to maintain a reasonably low sintering temperature for ease of fabrication. In addition, the relatively low content of Re in such binder compositions allows for reduced cost of the binder materials so that such materials be economically feasible.

Such a nickel-based superalloy may have a percentage weight from several percent to 100% with respect to the total weight of all material components in the binder matrix based on the specific composition of the binder matrix. A typical nickel-based superalloy may primarily comprise nickel and other metal components in a γ-γ′ phase strengthened state so that it exhibits an enhanced strength which increases as temperature rises.

Various nickel-based superalloys may have a melting point lower than the common binder material cobalt, such as alloys under the trade names Rene-95, Udimet-700, Udimet-720 from Special Metals which comprise primarily Ni in combination with Co, Cr, Al, Ti, Mo, Nb, W, B, and Zr. Hence, using such a nickel-based superalloy alone as a binder material may not increase the melting point of the resulting hardmetals in comparison with hardmetals using binders with Co.

However, in one implementation, the nickel-based superalloy can be used in the binder to provide a high material strength and to improve the material hardness of the resulting hardmetals, at high temperatures near or above 500° C. Tests of some fabricated samples have demonstrated that the material hardness and strength for hardmetals with a Ni-based superalloy in the binder can improve significantly, e.g., by at least 10%, at low operating temperatures in comparison with similar material compositions without Ni-based superalloy in the binder. The following table show measured hardness parameters of samples P65 and P46A with Ni-based superalloy in the binder in comparison with samples P49 and P47A with pure Co as the binder, where the compositions of the samples are listed in Table 4.

Effects of Ni-based Superalloy (NS) in Binder Sample Hv at Room Ksc at room Code Co or NS Temperature temperature Name Binder (Kg/mm²) (×10⁶ Pa · m^(1/2)) Comparison P49 Co: 10 2186 6.5 volume % P65 NS: 10 2532 6.7 Hv is about 16% volume % greater than that of P49 P47A Co: 15 2160 6.4 volume % P46A NS: 15 2364 6.4 Hv is about 10% volume % greater than that of P47A

Notably, at high operating temperatures above 500° C., hardmetal samples with Ni-based superalloy in the binder can exhibit a material hardness that is significantly higher than that of similar hardmetal samples without having a Ni-based superalloy in the binder. In addition, Ni-based superalloy as a binder material can also improve the resistance to corrosion of the resulting hardmetals or cermets in comparison with hardmetals or cermets using the conventional cobalt as the binder.

A nickel-based superalloy may be used alone or in combination with other elements to form a desired binder matrix. Other elements that may be combined with the nickel-based superalloy to form a binder matrix include but are not limited to, another nickel-based superalloy, other non-nickel-based alloys, Re, Co, Ni, Fe, Mo, and Cr.

Rhenium as a binder material may be used to provide strong bonding of hard particles and in particular can produce a high melting point for the resulting hardmetal material. The melting point of rhenium is about 3180° C., much higher than the melting point of 1495° C. of the commonly-used cobalt as a binder material. This feature of rhenium partially contributes to the enhanced performance of hardmetals with binders using Re, e.g., the enhanced hardness and strength of the resulting hardmetals at high temperatures. Re also has other desired properties as a binder material. For example, the hardness, the transverse rapture strength, the fracture toughness, and the melting point of the hardmetals with Re in their binder matrices can be increased significantly in comparison with similar hardmetals without Re in the binder matrices. A hardness Hv over 2600 Kg/mm² has been achieved in exemplary WC-based hardmetals with Re in the binder matrices. The melting point of some exemplary WC-based hardmetals, i.e., the sintering temperature, has shown to be greater than 2200° C. In comparison, the sintering temperature for WC-based hardmetals with Co in the binders in Table 2.1 in the cited Brookes is below 1500° C. A hardmetal with a high sintering temperature allows the material to operate at a high temperature below the sintering temperature. For example, tools based on such Re-containing hardmetal materials may operate at high speeds to reduce the processing time and the overall throughput of the processing.

The use of Re as a binder material in hardmetals, however, may present limitations in practice. For example, the desirable high-temperature property of Re generally leads to a high sintering temperature for fabrication. Thus, the oven or furnace for the conventional sintering process needs to operate at or above the high sintering temperature. Ovens or furnaces capable of operating at such high temperatures, e.g., above 2200° C., can be expensive and may not be widely available for commercial use. U.S. Pat. No. 5,476,531 discloses a use of a rapid omnidirectional compaction (ROC) method to reduce the processing temperature in manufacturing WC-based hardmetals with pure Re as the binder material from 6% to 18% of the total weight of each hardmetal. This ROC process, however, is still expensive and is generally not suitable for commercial fabrication.

One potential advantage of the hardmetal compositions and the composition methods described here is that they may provide or allow for a more practical fabrication process for fabricating hardmetals with either Re or mixtures of Re with other binder materials in the binder matrices. In particular, this two-step process makes it possible to fabricate hardmetals where Re is at or more than 25% of the total weight of the binder matrix of the resulting hardmetal. Such hardmetals with Re at or more than 25% may be used to achieve a high hardness and a high material strength at high temperatures.

Another limitation of using pure Re as a binder material for hardmetals is that Re oxidizes severely in air at or above about 350° C. This poor oxidation resistance may dramatically reduce the use of pure Re as binder for any application above about 300° C. Since Ni-based superalloy has exceptionally strength and oxidation resistance under 1000° C., a mixture of a Ni-based superalloy and Re where Re is the dominant material in the binder may be used to improve the strength and oxidation resistance of the resulting hardmetal using such a mixture as the binder. On the other hand, the addition of Re into a binder primarily comprised of a Ni-based superalloy can increase the melting range of the resulting hardmetal, and improve the high temperature strength and creep resistance of the Ni-based superalloy binder.

In general, the percentage weight of the rhenium in the binder matrix should be between a several percent to essentially 100% of the total weight of the binder matrix in a hardmetal. Preferably, the percentage weight of rhenium in the binder matrix should be at or above 5%. In particular, the percentage weight of rhenium in the binder matrix may be at or above 10% of the binder matrix. In some implementations, the percentage weight of rhenium in the binder matrix may be at or above 25% of the total weight of the binder matrix of the resulting hardmetal. Hardmetals with such a high concentration of Re may be fabricated at relatively low temperatures with a two-step process described in this application.

Since rhenium is generally more expensive than other materials used in hardmetals, cost should be considered in designing binder matrices that include rhenium. Some of the examples given below reflect this consideration. In general, according to one implementation, a hardmetal composition includes dispersed hard particles having a first material, and a binder matrix having a second, different material that includes rhenium, where the hard particles are spatially dispersed in the binder matrix in a substantially uniform manner. The binder matrix may be a mixture of Re and other binder materials to reduce the total content of Re to in part reduce the overall cost of the raw materials and in part to explore the presence of other binder materials to enhance the performance of the binder matrix. Examples of binder matrices having mixtures of Re and other binder materials include, mixtures of Re and at least one Ni-based superalloy, mixtures of Re, Co and at least one Ni-based superalloy, mixtures of Re and Co, and others.

TABLE 1 lists some examples of hardmetal compositions of interest. In this table, WC-based compositions are referred to as “hardmetals” and the TiC-based compositions are referred to as “cermets.” Traditionally, TiC particles bound by a mixture of Ni and Mo or a mixture of Ni and Mo₂C are cermets. Cermets as described here further include hard particles formed by mixtures of TiC and TiN, of TiC, TiN, WC, TaC, and NbC with the binder matrices formed by the mixture of Ni and Mo or the mixture of Ni and Mo₂C. For each hardmetal composition, three different weight percentage ranges for the given binder material in the are listed. As an example, the binder may be a mixture of a Ni-based superalloy and cobalt, and the hard particles may a mixture of WC, TiC, TaC, and NbC. In this composition, the binder may be from about 2% to about 40% of the total weight of the hardmetal. This range may be set to from about 3% to about 35% in some applications and may be further limited to a smaller range from about 4% to about 30% in other applications.

TABLE 1 (NS: Ni-based superalloy) Binder Composition for 1^(st) Binder 2^(nd) Binder 3^(rd) Binder Composition Hard Particles Wt. % Range Wt. % Range Wt. % Range Hardmetals Re WC 4 to 40 5 to 35 6 to 30 WC—TiC—TaC—NbC 4 to 40 5 to 35 6 to 30 NS WC 2 to 30 3 to 25 4 to 20 WC—TiC—TaC—NbC 2 to 30 3 to 25 4 to 20 NS—Re WC 2 to 40 3 to 35 4 to 30 WC—TiC—TaC—NbC 2 to 40 3 to 35 4 to 30 Re—Co WC 2 to 40 3 to 35 4 to 30 WC—TiC—TaC—NbC 2 to 40 3 to 35 4 to 30 NS—Re—Co WC 2 to 40 3 to 35 4 to 30 WC—TiC—TaC—NbC 2 to 40 3 to 35 4 to 30 Cermets NS Mo₂C—TiC 5 to 40 6 to 35 8 to 40 Mo₂C—TiC—TiN— 5 to 40 6 to 35 8 to 40 WC—TaC—NbC Re Mo₂C—TiC 10 to 55 12 to 50 15 to 45 Mo₂C—TiC—TiN— 10 to 55 12 to 50 15 to 45 WC—TaC—NbC NS—Re Mo₂C—TiC 5 to 55 6 to 50 8 to 45 Mo₂C—TiC—TiN— 5 to 55 6 to 50 8 to 45 WC—TaC—NbC

Fabrication of hardmetals with Re or a nickel-based superalloy in binder matrices may be carried out as follows. First, a powder with desired hard particles such as one or more carbides or carbonitrides is prepared. This powder may include a mixture of different carbides or a mixture of carbides and nitrides. The powder is mixed with a suitable binder matrix material that includes Re or a nickel-based superalloy. In addition, a pressing lubricant, e.g., a wax, may be added to the mixture.

The mixture of the hard particles, the binder matrix material, and the lubricant is mixed through a milling or attriting process by milling or attriting over a desired period, e.g., hours, to fully mix the materials so that each hard particle is coated with the binder matrix material to facilitate the binding of the hard particles in the subsequent processes. The hard particles should also be coated with the lubricant material to lubricate the materials to facilitate the mixing process and to reduce or eliminate oxidation of the hard particles. Next, pressing, pre-sintering, shaping, and final sintering are subsequently performed to the milled mixture to form the resulting hardmetal. The sintering process is a process for converting a powder material into a continuous mass by heating to a temperature that is below the melting temperature of the hard particles and may be performed after preliminary compacting by pressure. During this process, the binder material is densified to form a continuous binder matrix to bind hard particles therein. One or more additional coatings may be further formed on a surface of the resulting hardmetal to enhance the performance of the hardmetal. FIG. 1 is a flowchart for this implementation of the fabrication process.

In one implementation, the manufacture process for cemented carbides includes wet milling in solvent, vacuum drying, pressing, and liquid-phase sintering in vacuum. The temperature of the liquid-phase sintering is between melting point of the binder material (e.g., Co at 1495° C.) and the eutectic temperature of the mixture of hardmetal (e.g., WC—Co at 1320° C.). In general, the sintering temperature of cemented carbide is in a range of 1360 to 1480° C. For new materials with low concentration of Re or a Ni-based superalloy in binder alloy, manufacture process is same as conventional cemented carbide process. The principle of liquid phase sintering in vacuum is applied in here. The sintering temperature is slightly higher than the eutectic temperature of binder alloy and carbide. For example, the sintering condition of P17 (25% of Re in binder alloy, by weight) is at 1700° C. for one hour in vacuum.

FIG. 2 shows a two-step fabrication process based on a solid-state phase sintering for fabricating various hardmetals described in this application. Examples of hardmetals that can be fabricated with this two-step sintering method include hardmetals with a high concentration of Re in the binder matrix that would otherwise require the liquid-phase sintering at high temperatures. This two-step process may be implemented at relatively low temperatures, e.g., under 2200° C., to utilize commercially feasible ovens and to produce the hardmetals at reasonably low costs. The liquid phase sintering is eliminated in this two-step process because the liquid phase sintering may not be practical due to the generally high eutectic temperatures of the binder alloy and carbide. As discussed above, sintering at such high temperatures requires ovens operating at high temperatures which may not be commercially feasible.

The first step of this two-step process is a vacuum sintering where the mixture materials for the binder matrix and the hard particles are sintered in vacuum. The mixture is initially processed by, e.g., wet milling, drying, and pressing, as performed in conventional processes for fabricating cemented carbides. This first step of sintering is performed at a temperature below the eutectic temperature of the binder alloy and the hard particle materials to remove or eliminate the interconnected porosity. The second step is a solid phase sintering at a temperature below the eutectic temperature and under a pressured condition to remove and eliminate the remaining porosities and voids left in the sintered mixture after the first step. A hot isostatic pressing (HIP) process may be used as this second step sintering. Both heat and pressure are applied to the material during the sintering to reduce the processing temperature which would otherwise be higher in absence of the pressure. A gas medium such as an inert gas may be used to apply and transmit the pressure to the sintered mixture. The pressure may be at or over 1000 bar. Application of pressure in the HIP process lowers the required processing temperature and allows for use of conventional ovens or furnaces. The temperatures of solid phase sintering and HIPping for achieving fully condensed materials are generally significantly lower than the temperatures for liquid phase sintering. For example, the sample P62 which uses pure Re as the binder may be fully densified by vacuum sintering at 2200° C. for one to two hours and then HIPping at about 2000° C. under a pressure of 30,000 PSI in the inert gas such as Ar for about one hour. Notably, the use of ultra fine hard particles with a particulate dimension less than 0.5 micron can reduce the sintering temperature for fully densifying the hardmetals (fine particles are several microns in size). For example, in making the samples P62 and P63, the use of such ultra fine WC allows for sintering temperatures to be low, e.g., around 2000° C. This two-step process is less expensive than the ROC method and may be used to commercial production.

The following sections describe exemplary hardmetal compositions and their properties based on various binder matrix materials that include at least rhenium or a nickel-based superalloy.

TABLE 2 provides a list of code names (lot numbers) for some of the constituent materials used to form the exemplary hardmetals, where H1 represents rhenium, and L1, L2, and L3 represent three exemplary commercial nickel-based superalloys. TABLE 3 further lists compositions of the above three exemplary nickel-based superalloys, Udimet720(U720), Rene'95(R-95), and Udimet700(U700), respectively. TABLE 4 lists compositions of exemplary hardmetals, both with and without rhenium or a nickel-based superalloy in the binder matrices. For example, the material composition for Lot P17 primarily includes 88 grams of T32 (WC), 3 grams of 132 (TiC), 3 grams of A31 (TaC), 1.5 grams of H1 (Re) and 4.5 grams of L2 (R-95) as binder, and 2 grams of a wax as lubricant. Lot P58 represents a hardmetal with a nickel-based superalloy L2 as the only binder material without Re. These hardmetals were fabricated and tested to illustrate the effects of either or both of rhenium and a nickel-based superalloy as binder materials on various properties of the resulting hardmetals. TABLES 5-8 further provide summary information of compositions and properties of different sample lots as defined above.

FIGS. 3 through 8 show measurements of selected hardmetal samples of this application. FIGS. 3 and 4 show measured toughness and hardness parameters of some exemplary hardmetals for the steel cutting grades. FIGS. 5 and 6 show measured toughness and hardness parameters of some exemplary hardmetals for the non-ferrous cutting grades. Measurements were performed before and after the solid-phase sintering HIP process and the data suggests that the HIP process significantly improves both the toughness and the hardness of the materials. FIG. 7 shows measurements of the hardness as a function of temperature for some samples. As a comparison, FIGS. 7 and 8 also show measurements of commercial C2 and C6 carbides under the same testing conditions, where FIG. 7 shows the measured hardness and FIG. 8 shows measured change in hardness from the value at the room temperature (RT). Clearly, the hardmetal samples based on the compositions described here outperform the commercial grade materials in terms of the hardness at high temperatures. These results demonstrate that the superior performance of binder matrices with either or both of Re and a nickel-based superalloy as binder materials in comparison with Co-based binder matrix materials.

TABLE 2 Powder Code Composition Note T32 WC Particle size 1.5 μm, from Alldyne T35 WC Particle size 15 μm, from Alldyne Y20 Mo Particle size 1.7-2.2 μm, from Alldyne L3 U-700 −325 Mesh, special metal Udimet 700 L1 U-720 −325 Mesh, Special Metal, Udimet 720 L2 Re-95 −325 Mesh, Special Metal, Rene 95 H1 Re −325 Mesh, Rhenium Alloy Inc. I32 TiC from AEE, Ti − 302 I21 TiB₂ from AEE, Ti − 201, 1-5 μm A31 TaC from AEE, TA − 301 Y31 Mo₂C from AEE, MO − 301 D31 VC from AEE, VA − 301 B1 Co from AEE, CO − 101 K1 Ni from AEE, Ni − 101 K2 Ni from AEE, Ni − 102 I13 TiN from Cerac, T − 1153 C21 ZrB2 from Cerac, Z − 1031 Y6 Mo from AEE Mo + 100, 1-2 μm L6 Al from AEE Al − 100, 1-5 μm R31 B₄C from AEE Bo − 301, 3 μm T3.8 WC Particle size 0.8 μm, Alldyne T3.4 WC Particle size 0.4 μm, OMG T3.2 WC Particle size 0.2 μm, OMG

TABLE 3 Ni Co Cr Al Ti Mo Nb W Zr B C V R95 61.982 8.04 13.16 3.54 2.53 3.55 3.55 3.54 0.049 0.059 U700 54.331 17.34 15.35 4.04 3.65 5.17 .028 .008 .04 .019 .019 .005 U720 56.334 15.32 16.38 3.06 5.04 3.06 0.01 1.30 .035 .015 .012 .004

TABLE 4 Lot No Composition (units in grams) P17 H1 = 1.5, L2 = 4.5, I32 = 3, A31 = 3, T32 = 88, Wax = 2 P18 H1 = 3, L2 = 3, I32 = 3, A31 = 3, T32 = 88, Wax = 2 P19 H1 = 1.5, L3 = 4.5, I32 = 3, A31 = 3, T32 = 88, Wax = 2 P20 H1 = 3, L3 = 3, I32 = 3, A31 = 3, T32 = 88, Wax = 2 P25 H1 = 3.75, L2 = 2.25, I32 = 3, A31 = 3, T32 = 88, Wax = 2 P25A H1 = 3.75, L2 = 2.25, I32 = 3, A31 = 3, T32 = 88, Wax = 2 P31 H1 = 3.44, B1 = 4.4, T32 = 92.16, Wax = 2 P32 H1 = 6.75, B1 = 2.88, T32 = 90.37, Wax = 2 P33 H1 = 9.93, B1 = 1.41, T32 = 88.66, Wax = 2 P34 L2 = 14.47, I32 = 69.44, Y31 = 16.09 P35 H1 = 8.77, L2 = 10.27, I32 = 65.73, Y31 = 15.23 P36 H1 = 16.66, L2 = 6.50, I32 = 62.4, Y31 = 14.56 P37 H1 = 23.80, L2 = 3.09, I32 = 59.38, Y31 = 13.76 P38 K1 = 15.51, I32 = 68.60, Y31 = 15.89 P39 K2 = 15.51, I32 = 68.60, Y31 = 15.89 P40 H1 = 7.57, L2 = 2.96, I32 = 5.32, A31 = 5.23, T32 = 78.92, Wax = 2 P40A H1 = 7.57, L2 = 2.96, I32 = 5.32, A31 = 5.23, T32 = 78.92, Wax = 2 P41 H1 = 11.1, L2 = 1.45, I32 = 5.20, A31 = 5.11, T32 = 77.14, Wax = 2 P41A H1 = 11.1, L2 = 1.45, I32 = 5.20, A31 = 5.11, T32 = 77.14, Wax = 2 P42 H1 = 9.32, L2 = 3.64, I32 = 6.55, A31 = 6.44, I21 = 0.40, R31 = 4.25, T32 = 69.40, Wax = 2 P43 H1 = 9.04, L2 = 3.53, I32 = 6.35, A31 = 6.24, I21 = 7.39, R31 = 0.22, T32 = 67.24, Wax = 2 P44 H1 = 8.96, L2 = 3.50, I32 = 14.69, A31 = 6.19, T32 = 66.67, Wax = 2 P45 H1 = 9.37, L2 = 3.66, I32 = 15.37, A31 = 6.47, Y31 = 6.51, T32 = 58.61, Wax = 2 P46 H1 = 11.40, L2 = 4.45, I32 = 5.34, A31 = 5.25, T32 = 73.55, Wax = 2 P46A H1 = 11.40, L2 = 4.45, I32 = 5.34, A31 = 5.25, T32 = 73.55, Wax = 2 P47 H1 = 11.35, B1 = 4.88, I32 = 5.32, A31 = 5.23, T32 = 73.22, Wax = 2 P47A H1 = 11.35, B1 = 4.88, I32 = 5.32, A31 = 5.23, T32 = 73.22, Wax = 2 P48 H1 = 3.75, L2 = 2.25, I32 = 5, A31 = 5, T32 = 84, Wax = 2 P49 H1 = 7.55, B1 = 3.25, I32 = 5.31, A31 = 5.21, T32 = 78.68, Wax = 2 P50 H1 = 4.83, L2 = 1.89, I32 = 5.31, A31 = 5.22, T32 = 82.75, Wax = 2 P51 H1 = 7.15, L2 = 0.93, I32 = 5.23, A31 = 5.14, T32 = 81.55, Wax = 2 P52 B1 = 8, D31 = 0.6, T3.8 = 91.4, Wax = 2 P53 B1 = 8, D31 = 0.6, T3.4 = 91.4, Wax = 2 P54 B1 = 8, D31 = 0.6, T3.2 = 91.4, Wax = 2 P55 H1 = 1.8, B1 = 7.2, D31 = 0.6, T3.4 = 90.4, Wax = 2 P56 H1 = 1.8, B1 = 7.2, D31 = 0.6, T3.2 = 90.4, Wax = 2 P56A H1 = 1.8, B1 = 7.2, D31 = 0.6, T3.2 = 90.4, Wax = 2 P57 H1 = 1.8, B1 = 7.2, T3.2 = 91, Wax = 2 P58 L2 = 7.5, D31 = 0.6, T3.2 = 91.9, Wax = 2 P59 H1 = 0.4, B1 = 3, L2 = 4.5, D31 = 0.6, T3.2 = 91.5, Wax = 2 P62 H1 = 14.48, I32 = 5.09, A31 = 5.00, T3.2 = 75.43, Wax = 2 P62A H1 = 14.48, I32 = 5.09, A31 = 5.00, T3.2 = 75.43, Wax = 2 P63 H1 = 12.47, L2 = 0.86, I32 = 5.16, A31 = 5.07, T3.2 = 76.45, Wax = 2 P65 H1 = 7.57, L2 = 2.96, I32 = 5.32, A31 = 5.23, T3.2 = 78.92, Wax = 2 P65A H1 = 7.57, L2 = 2.96, I32 = 5.32, A31 = 5.23, T3.2 = 78.92, Wax = 2 P66 H1 = 27.92, I32 = 4.91, A31 = 4.82, T3.2 = 62.35, Wax = 2 P67 H1 = 24.37, L3 = 1.62, I32 = 5.04, A31 = 4.95, T32 = 32.01, T33 = 32.01, Wax = 2 P69 L2 = 7.5, D31 = 0.4, T3.2 = 92.1, Wax = 2 P70 L1 = 7.4, D31 = 0.3, T3.2 = 92.3, Wax = 2 P71 L3 = 7.2, D31 = 0.3, T3.2 = 92.5, Wax = 2 P72 H1 = 1.8, B1 = 7.2, D31 = 0.3, T3.2 = 90.7, Wax = 2 P73 H1 = 1.8, B1 = 4.8, L2 = 2.7, D31 = 0.3, T3.2 = 90.4, Wax = 2 P74 H1 = 1.8, B1 = 3, L2 = 4.5, D31 = 0.3, T3.2 = 90.4, Wax = 2 P75 H1 = 0.8, B1 = 3, L2 = 4.5, D31 = 0.3, T3.2 = 91.4, Wax = 2 P76 H1 = 0.8, B1 = 3, L1 = 4.5, D31 = 0.3, T3.2 = 91.4, Wax = 2 P77 H1 = 0.8, B1 = 3, L3 = 4.5, D31 = 0.3, T3.2 = 91.4, Wax = 2 P78 H1 = 0.8, B1 = 4.5, L1 = 3, D31 = 0.3, T3.2 = 91.4, Wax = 2 P79 H1 = 0.8, B1 = 4.5, L3 = 3.1, D31 = 0.3, T3.2 = 91.3, Wax = 2

Several exemplary categories of hardmetal compositions are described below to illustrate the above general designs of the various hardmetal compositions to include either of Re and Nickel-based superalloy, or both. The exemplary categories of hardmetal compositions are defined based on the compositions of the binder matrices for the resulting hardmetals or cermets. The first category uses a binder matrix having pure Re, the second category uses a binder matrix having a Re—Co alloy, the third category uses a binder matrix having a Ni-based superalloy, and the fourth category uses a binder matrix having an alloy having a Ni-based superalloy in combination with of Re with or without Co.

In general, hard and refractory particles used in hardmetals of interest may include, but are not limited to, carbides, nitrides, carbonitrides, borides, and silicides. Some examples of Carbides include WC, TiC, TaC, HfC, NbC, Mo₂C, Cr₂C₃, VC, ZrC, B₄C, and SiC. Examples of Nitrides include TiN, ZrN, HfN, VN, NbN, TaN, and BN. Examples of Carbonitrides include Ti(C,N), Ta(C,N), Nb(C,N), Hf(C,N), Zr(C,N), and V(C,N). Examples of Borides include TiB₂, ZrB₂, HfB₂, TaB₂, VB₂, MoB₂, WB, and W₂B. In addition, examples of Silicides are TaSi₂, Wsi₂, NbSi₂, and MoSi₂. The above-identified four categories of hardmetals or cermets can also use these and other hard and refractory particles.

In the first category of hardmetals based on the pure Re alloy binder matrix, the Re may be approximately from 5% to 40% by volume of all material compositions used in a hardmetal or cermet. For example, the sample with a lot No. P62 in TABLE 4 has 10% of pure Re, 70% of WC, 15% of TiC, and 5% of TaC by volume. This composition approximately corresponds to 14.48% of Re, 75.43% of WC, 5.09% of TiC and 5.0% of TaC by weight. In fabrication, the Specimen P62-4 was vacuum sintered at 2100° C. for about one hour and 2158° C. for about one hour. The density of this material is about 14.51 g/cc, where the calculated density is 14.50 g/cc. The average hardness Hv is 2627±35 Kg/mm² for 10 measurements taken at the room temperature under a load of 10 Kg. The measured surface fracture toughness K_(sc) is about 7.4×10⁶ Pa·m^(1/2) estimated by Palmvist crack length at a load of 10 Kg.

Another example under this category is P66 in TABLE 4. This sample has about 20% of Re, 60% of WC, 15% of TiC, and 5% of TaC by volume in composition. In the weight percentage, this sample has about 27.92% of Re, 62.35% of WC, 4.91% of TiC, and 4.82% of TaC. The Specimen P66-4 was first processed with a vacuum sintering process at about 2200° C. for one hour and was then sintered in the solid-phase with a HIP process to remove porosities and voids. The density of the resulting hardmetal is about 14.40 g/cc compared to the calculated density of 15.04 g/cc. The average hardness Hv is about 2402±44 Kg/mm² for 7 different measurements taken at the room temperature under a load of 10 Kg. The surface fracture toughness K_(sc) is about 8.1×10⁶ Pa·m^(1/2). The sample P66 and other compositions described here with a high concentration of Re with a weight percentage greater than 25%, as the sole binder material or one of two or more different binder materials in the binder, may be used for various applications at high operating temperatures and may be manufactured by using the two-step process based on solid-phase sintering.

The microstructures and properties of Re bound multiples types of hard refractory particles, such as carbides, nitrides, carbonnitrides, silicides, and borides, may provide advantages over Re-bound WC material. For example, Re bound WC—TiC—TaC may have better crater resistance in steel cutting than Re bound WC material. Another example is materials formed by refractory particles of Mo₂C and TiC bound in a Re binder.

For the second category with a Re—Co alloy as the binder matrix, the Re—Co alloy may be about from 5 to 40 Vol % of all material compositions used in the composition. In some implementations, the Re-to-Co ratio in the binder may vary from 0.01 to 0.99 approximately. Inclusion of Re can improve the mechanical properties of the resulting hardmetals, such as hardness, strength and toughness special at high temperature compared to Co bounded hardmetal. The higher Re content is the better high temperature properties are for most materials using such a binder matrix.

The sample P31 in TABLE 4 is one example within this category with 2.5% of Re, 7.5% of Co, and 90% of WC by volume, and 3.44% of Re, 4.40% of Co and 92.12% of WC by weight. In fabrication, the Specimen P31-1 was vacuum sintered at 1725° C. for about one hour. slight under sintering with some porosities and voids. The density of the resulting hardmetal is about 15.16 g/cc (calculated density at 15.27 g/cc). The average hardness Hv is about 1889±18 Kg/mm² at the room temperature under 10 Kg and the surface facture toughness K_(sc) is about 7.7 Pa·m^(1/2). In addition, the Specimen P31-1 was treated with a hot isostatic press (HIP) process at about 1600° C./15 ksi for about one hour after sintering. The HIP reduces or substantially eliminates the porosities and voids in the compound to increase the material density. After HIP, the measured density is about 15.25 g/cc (calculated density at 15.27 g/cc). The measured hardness Hv is about 1887±12 Kg/mm² at the room temperature under 10 Kg. The surface fracture toughness K_(sc) is about 7.6×10⁶ Pa·m^(1/2).

Another example in this category is P32 in TABLE 4 with 5.0% of Re, 5.0% of Co, and 90% of WC in volume (6.75% of Re, 2.88% of Co and 90.38% of WC in weight). The Specimen P32-4 was vacuum sintered at 1800° C. for about one hour. The measured density is about 15.58 g/cc in comparison with the calculated density at 15.57 g/cc. The measured hardness Hv is about 2065 Kg/mm² at the room temperature under 10 Kg. The surface fracture toughness K_(sc) is about 5.9×10⁶ Pa·m^(1/2). The Specimen P32-4 was also HIP at 1600° C./15 ksi for about one hour after Sintering. The measured density is about 15.57 g/cc (calculated density at 15.57 g/cc). The average hardness Hv is about 2010±12 Kg/mm² at the room temperature under 10 Kg. The surface fracture toughness K_(sc) is about 5.8×10⁶ Pa·m^(1/2).

The third example is P33 in TABLE 4 which has 7.5% of Re, 2.5% of Co, and 90% of WC by volume and 9.93% of Re, 1.41% of Co and 88.66% of WC by weight. In fabrication, the Specimen P33-7 was vacuum sintered at 1950° C. for about one hour and was under sintering with porosities and voids. The measured density is about 15.38 g/cc (calculated density at 15.87 g/cc). The measured hardness Hv is about 2081 Kg/mm² at the room temperature under a force of 10 Kg. The surface fracture toughness Ksc is about 5.6×10⁶ Pa·m^(1/2). The Specimen P33-7 was HIP at 1600° C./15 ksi for about one hour after sintering. The measured density is about 15.82 g/cc (calculated density=15.87 g/cc). The average hardness Hv is measured at about 2039±18 Kg/mm² at the room temperature under 10 Kg. The surface fracture toughness Ksc is about 6.5×10⁶ Pa·m^(1/2).

TABLE 5 Re—Co alloy bound hardmetals Density Temperature g/cc Hv ° C. Calcu- Meas- Kg/ Ksc ×10⁶ Grain Sinter HIP lated ured mm² Pa · m^(1/2) size P55-1 1350 1300 14.77 14.79 2047 8.6 Ultra-fine P56-5 1360 1300 14.77 14.72 2133 8.6 Ultra-fine P56A-4 1350 1300 14.77 14.71 2108 8.5 Ultra-fine P57-1 1350 1300 14.91 14.93 1747 12.3 Fine

The samples P55, P56, P56A, and P57 in TABLE 4 are also examples for the category with a Re—Co alloy as the binder matrix. These samples have about 1.8% of Re, 7.2% of Co, 0.6% of VC except that P57 has no VC, and finally WC in balance. These different compositions are made to study the effects of hardmetal grain size on Hv and Ksc. TABLE 5 lists the results.

TABLE 6 Properties of Ni-based superalloys, Ni, Re, and Co Test Temp. C. R-95 U-700 U720 Nickel Rhenium Cobalt Density 21 8.2 7.9 8.1 8.9 21 8.9 (g/c.c.) Melting 1255 1205 1210 1450 3180 1495 Point (° C.) Elastic 21 30.3 32.4 32.2 207 460 211 Modulus (Gpa) Ultimate 21 1620 1410 1570 317 1069 234 Tensile 760 1170 1035 1455 Strength 800 620 (Mpa) 870 690 1150 1200 414 0.2% 21 1310 965 1195 60 Yield 760 1100 825 1050 Strength 800 (Mpa) 870 635 1200 Tensile 21 15 17 13 30 >15 Elongation 760 15 20 9 (%) 800 5 870 27 1200 2 Oxidation Excellent Excellent Excellent Good Poor Good Resistance

The third category is based on binder matrices with Ni-based superalloys from 5 to 40% in volume of all materials in the resulting hardmetal. Ni-based superalloys are a family of high temperature alloys with γ′ strengthening. Three different strength alloys, Rene'95, Udimet 720, and Udimet 700 are used as examples to demonstrate the effects of the binder strength on mechanical properties of the final hardmetals. The Ni-based superalloys have a high strength specially at elevated temperatures. Also, these alloys have good environmental resistance such as resistance to corrosion and oxidation at elevated temperature. Therefore, Ni-based superalloys can be used to increase the hardness of Ni-based superalloy bound hardmetals when compared to Cobalt bound hardmetals. Notably, the tensile strengths of the Ni-based superalloys are much stronger than the common binder material cobalt as shown by TABLE 6. This further shows that Ni-based superalloys are good binder materials for hardmetals.

One example for this category is P58 in TABLE 4 which has 7.5% of Rene'95, 0.6% of VC, and 91.9% of WC in weight and compares to cobalt bound P54 in TABLE 4 (8% of Co, 0.6% of VC, and 91.4% of WC). The hardness of P58 is significant higher than P54 as shown in TABLE 7.

TABLE 7 Comparison of P54 and P58 Hv, Ksc ×10⁶ Sintering HIP Kg/mm² Pa · m^(1/2) P54-1 1350 C./1 hr 1305° C. 2094 8.8 P54-2 1380 C./1 hr 15 KSI 2071 7.8 P54-3 1420 C./1 hr under Ar 2107 8.5 P58-1 1350, 1380, 1400, 1420, 1 hour 2322 7.0 1450, 1475 for 1 hour at each temperature P58-3 1450 C./1 hr 2272 7.4 P58-5 1500 C./1 hr 2259 7.2 P58-7 1550 C./1 hr 2246 7.3

The fourth category is Ni-based superalloy plus Re as binder, e.g., approximately from 5% to 40% by volume of all materials in the resulting hardmetal or cermet. Because addition of Re increases the melting point of binder alloy of Ni-based superalloy plus Re, the processing temperature of hardmetal with Ni-based superalloy plus Re binder increases as the Re content increases. Several hardmetals with different Re concentrations are listed in TABLE 8. TABLE 9 further shows the measured properties of the hardmetals in TABLE 8.

TABLE 8 Hardmetal with a binder comprising Ni-based superalloy plus Re Sintering Composition, weight % Re to Binder Temperature Re Rene95 U-700 U-720 WC TiC TaC Ratio ° C. P17 1.5 4.5 88 3 3  25% 1600~1750 P18 3 3.0 88 3 3  50% 1600~1775 P25 3.75 2.25 88 3 3 62.5% 1650~1825 P48 3.75 2.25 84 5 5 62.5% 1650~1825 P50 4.83 1.89 82.75 5.31 5.22 71.9% 1675~1850 P40 7.57 2.96 78.92 5.32 5.23 71.9% 1675~1850 P46 11.40 4.45 73.55 5.34 5.24 71.9% 1675~1850 P51 7.15 0.93 81.55 5.23 5.14 88.5% 1700~1900 P41 11.10 1.45 77.14 5.20 5.11 88.5% 1700~1900 P63 12.47 0.86 76.45 5.16 5.07 93.6% 1850~2100 P19 1.5 4.5 88 3 3  25% 1600~1750 P20 3 3 88 3 3  50% 1600~1775 P67 24.37 1.62 64.02 5.04 4.95 93.6% 1950~2300

TABLE 9 Properties of hardmetals bound by Ni-based superalloy and Re Temperature, C. Density, g/cc Hv Ksc ×10⁶ Sinter HIP Calculated Measured Kg/mm² Pa · m^(1/2) P17 1700 14.15 14.18 2120 6.8 P17 1700 1600 14.15 14.21 2092 7.2 P18 1700 14.38 14.47 2168 5.9 P18 1700 1600 14.38 14.42 2142 6.1 P25 1750 14.49 14.41 2271 6.1 P25 1750 1600 14.49 14.48 2193 6.5 P48 1800 1600 13.91 13.99 2208 6.3 P50 1800 1600 13.9 13.78 2321 6.5 P40 1800 13.86 13.82 2343 P40 1800 1600 13.86 13.86 2321 6.3 P46 1800 13.81 13.88 2282 7.1 P46 1800 1725 13.81 13.82 2326 6.7 P51 1800 1600 14.11 13.97 2309 6.6 P41 1800 1600 14.18 14.63 2321 6.5 P63 2000 14.31 14.37 2557 7.9 P19 1700 14.11 14.11 2059 7.6 P19 1700 1600 14.11 2012 8.0 P20 1725 14.35 14.52 2221 6.4 P20 1725 1600 14.35 14.35 2151 7.0 P67 2200 14.65 14.21 2113 8.1 P67 2200 1725 14.65 14.34 2210 7.1

Another example under the fourth category uses a Ni-based superalloy plus Re and Co as binder which is also about 5% to 40% by volume. Exemplary compositions of hardmetals bound by Ni-based superalloy plus Re and Co are list in TABLE 10.

TABLE 10 Composition of hardmetals bound by Ni-based superalloy plus Re and Co Composition, weight % Re Co Rene95 U-720 U-700 WC VC P73 1.8 4.8 2.7 90.4 0.3 P74 1.8 3 4.5 90.4 0.3 P75 0.8 3 4.5 91.4 0.3 P76 0.8 3 4.5 91.4 0.3 P77 0.8 3 4.5 91.4 0.3 P78 0.8 4.5 3 91.4 0.3 P79 0.8 4.5 3.1 91.3 0.3

Measurements on selected samples have been performed to study properties of the binder matrices with Ni-based superalloys. In general, Ni-based superalloys not only exhibit excellent strengths at elevated temperatures but also possess outstanding resistances to oxidation and corrosion at high temperatures. Ni-based superalloys have complex microstructures and strengthening mechanisms. In general, the strengthening of Ni-based superalloys is primarily due to precipitation strengthening of γ-γ′ and solid-solution strengthening. The measurements the selected samples demonstrate that Ni-based superalloys can be used as a high-performance binder materials for hardmetals.

TABLE 11 lists compositions of selected samples by their weight percentages of the total weight of the hardmetals. The WC particles in the samples are 0.2 μm in size. TABLE 12 lists the conditions for the two-step process performed and measured densities, hardness parameters, and toughness parameters of the samples. The Palmqvist fracture toughness Ksc is calculated from the total crack length of Palmqvist crack which is produced by the Vicker Indentor: Ksc=0.087*(Hv*W)^(1/2). See, e.g., Warren and H. Matzke, Proceedings Of the

International Conference On the Science of Hard Materials, Jackson, Wyo., Aug. 23-28, 1981. Hardness Hv and Crack Length are measured at a load of 10 Kg for 15 seconds. During each measurement, eight indentations were made on each specimen and the average value was used in computation of the listed data.

TABLE 11 Weight % Re in Vol % Re Co R-95 WC VC Binder Binder P54 0 8 0 91.4 0.6 0 13.13 P58 0 0 7.5 91.9 0.6 0 13.25 P56 1.8 7.2 0 90.4 0.6 20 13.20 P72 1.8 7.2 0 90.7 0.3 20 13.18 P73 1.8 4.8 2.7 90.4 0.3 20 14.00 P74 1.8 3 4.5 90.4 0.3 20 14.24

TABLE 12 Palmqvist Cal. Measu. Toughness Sample Sinter HIP Density Density Hardness, Hv Ksc, Code Condition Condition g/c.c. g/c.c. Kg/mm² ×10⁶ Pa · m^(1/2) P54-5 1360° C./1 hr 14.63 14.58 2062 ± 35 8.9 ± 0.2 1360° C./1 hr 1305° C./ 14.55 2090 ± 22 8.5 ± 0.2 15 ksi/1 hr P58-7 1550° C./1 hr 14.50 14.40 2064 ± 12 7.9 ± 0.2 1550° C./1 hr 1305° C./ 14.49 2246 ± 23 7.3 ± 0.1 15 ksi/1 hr P56-5 1360° C./1 hr 14.77 14.71 2064 ± 23 8.2 ± 0.1 1360° C./1 hr 1305° C./ 14.72 2133 ± 34 8.6 ± 0.2 15 ksi/1 hr P72-6 1475° C./1 hr 14.83 14.77 2036 ± 34 8.5 ± 0.6 1475° C./1 hr 1305° C./ 14.91 2041 ± 30 9.1 ± 0.4 15 ksi/1 hr P73-6 1475° C./1 hr 14.73 14.70 2195 ± 23 7.7 ± 0.1 1475° C./1 hr 1305° C./ 14.72 2217 ± 25 8.1 ± 0.2 15 ksi/1 hr P74-5 1500° C./1 hr 14.69 14.69 2173 ± 30 7.4 ± 0.3 and 1520° C./1 hr 1500° C./1 hr 1305° C./ 14.74 2223 ± 34 7.7 ± 0.1 and 1520° C./1 hr 15 ksi/1 hr

Among the tested samples, the sample P54 uses the conventional binder consisting of Co. The Ni-superalloy R-95 is used in the sample P58 to replace Co as the binder in the sample P54. As a result, the Hv increases from 2090 of P54 to 2246 of P58. In the sample P56, the mixture of Re and Co is used to replace Co as binder and the corresponding Hv increases from 2090 of P54 to 2133 of P56. The samples P72, P73, P74 have the same Re content but different amounts of Co and R95. The mixtures of Re, Co, and R95 are used in samples P73 and P74 to replace the binder having a mixture of Re and Co as the binder in the sample 72. The hardness Hv increases from 2041(P72) to 2217(P73) and 2223(P74).

TABLE 13 Weight % WC Re in Vol. % Re R-95 Co TiC TaC WC (2 μm) (0.2 μm) Binder Binder P17 1.5 4.5 0 3 3 88 0 25 8.78 P18 3 3 0 3 3 88 0 50 7.31 P25 3.75 2.25 0 3 3 88 0 62.5 6.57 P48 3.75 2.25 0 5 5 84 0 62.5 6.3 P50 4.83 1.89 0 5.31 5.22 82.75 0 71.9 6.4 P51 7.15 0.93 0 5.23 5.14 81.55 0 88.5 6.4 P49 7.55 0 3.25 5.31 5.21 78.68 0 69.9 10 P40A 7.57 2.96 0 5.32 5.23 78.92 0 71.9 10 P63 12.47 0.86 0 5.16 5.07 0 76.45 93.6 10 P62A 14.48 0 0 5.09 5.00 0 75.43 100 10 P66 27.92 0 0 4.91 4.82 0 62.35 100 20

Measurements on selected samples have also been performed to further study properties of the binder matrices with Re in the binder matrices. TABLE 13 lists the tested samples. The WC particles with two different particle sizes of 2 μm and 0.2 μm were used. TABLE 14 lists the conditions for the two-step process performed and the measured densities, hardness parameters, and toughness parameters of the selected samples.

TABLE 14 Cal. Measu. Palmqvist Sample Sinter HIP Density Density Hardness, Hv Toughness** Code Condition Condition g/c.c. g/c.c. Kg/mm² Ksc, MPam^(0.5) P17-5 1800° C./1 hr 1600° C./15 ksi/ 14.15 14.21 2092 ± 3  7.2 ± 0.1 1 hr P18-3 1800° C./1 hr 1600° C./15 ksi/ 14.38 14.59 2028 ± 88 6.8 ± 0.3 1 hr P25-3 1750° C./1 hr 1600° C./15 ksi/ 14.49 14.48 2193 ± 8  6.5 ± 0.1 1 hr P48-1 1800° C./1 hr 1600° C./15 ksi/ 13.91 13.99 2208 ± 12 6.3 ± 0.4 1 hr P50-4 1800° C./1 hr 1600° C./15 ksi/ 13.9 13.8 2294 ± 20 6.3 ± 0.1 1 hr P51-1 1800° C./1 hr 1600° C./15 ksi/ 14.11 13.97 2309 ± 6  6.6 ± 0.1 1 hr P40A-1 1800° C./1 hr 1600° C./15 ksi/ 13.86 13.86 2321 ± 10 6.3 ± 0.1 1 hr P49-1 1800° C./1 hr 1600° C./15 ksi/ 13.91 13.92 2186 ± 29 6.5 ± 0.2 1 hr P62A-6 2200° C./1 hr 1725° C./30 ksi/ 14.5 14.41 2688 ± 22 6.7 ± 0.1 1 hr P63-5 2200° C./1 hr 1725° C./30 ksi/ 14.31 14.37 2562 ± 31 6.7 ± 0.2 1 hr P66-4 2200° C./1 hr 15.04 14.40 2402 ± 44 8.2 ± 0.4 P66-4 2200° C./1 hr 1725° C./30 ksi/ 15.04 14.52 1 hr P66-4 2200° C./1 hr 1725° C./30 ksi/ 15.04 14.53 2438 ± 47 6.9 ± 0.2 1 hr + 1950° C./30 ksi/ 1 hr P66-5 2200° C./1 hr 15.04 14.33 2092 ± 23 7.3 ± 0.3 P66-5 2200° C./1 hr 1725° C./30 ksi/ 15.04 14.63 1 hr P66-5 2200° C./1 hr 1725° C./30 ksi/ 15.04 14.66 2207 ± 17 7.1 ± 0.2 1 hr + 1850° C./30 ksi/ 1 hr

TABLE 15 further shows measured hardness parameters under various temperatures for the selected samples, where the Knoop hardness H_(k) were measured under a load of 1 Kg for 15 seconds on a Nikon QM hot hardness tester and R is a ratio of H_(k) at an elevated testing temperature over H_(k) at 25° C. The hot hardness specimens of C2 and C6 carbides were prepared from inserts SNU434 which were purchased from MSC Co. (Melville, N.Y.).

TABLE 15 (each measured value at a given temperature is an averaged value of 3 different measurements) Testing Temperature, ° C. Hv Lot No. 25 400 500 600 700 800 900 @25° P17-5 Hk, 1880 ± 10 1720 ± 17 1653 ± 25 1553 ± 29 1527 ± 6  2092 ± 3  Kg/mm² R, % 100 91 88 83 81 P18-3 Hk, 1773 ± 32 1513 ± 12 1467 ± 21 1440 ± 10 1340 ± 16 2028 ± 88 Kg/mm² R, % 100 85 83 81 76 P25-3 Hk, 1968 ± 45 1813 ± 12 1710 ± 0  1593 ± 5 2193 ± 8  Kg/mm² R, % 100 92 87 81 P40A-1 Hk, 2000 ± 35 1700 ± 17 1663 ± 12 1583 ± 21 1540 ± 35 2321 ± 10 Kg/mm² R, % 100 85 83 79 77 P48-1 Hk, 1925 ± 25 1613 ± 15 1533 ± 29 1477 ± 6  1377 ± 15 2208 ± 12 Kg/mm² R, % 100 84 80 77 72 P49-1 Hk, 2023 ± 32 1750 ± 0  1633 ± 6  1600 ± 17 2186 ± 29 Kg/mm² R, % 100 87 81 79 P50-4 Hk, 2057 ± 25 1857 ± 15 1780 ± 20 1713 ± 6  1627 ± 40 2294 ± 20 Kg/mm² R, % 100 90 87 83 79 P51-1 Hk, 2050 ± 26 1797 ± 6  1743 ± 35 1693 ± 15 1607 ± 15 2309 ± 6  Kg/mm² R, % 100 88 85 83 78 P62A-6 Hk, 2228 ± 29 2063 ± 25 1960 ± 76 1750 ± 0 2688 ± 22 Kg/mm² R, % 100 93 88 79 P63-5 Hk, 1887 ± 6  1707 ± 35 1667 ± 15 1633 ± 6  1603 ± 25 2562 ± 31 Kg/mm² R, % 100 C2 Hk, 1503 ± 38 988 ± 9  711 ± 0  584 ± 27 1685 ± 16 Carbide Kg/mm² R, % 100 66 47 39 C6 Hk, 1423 ± 23 1127 ± 25 1090 ± 10 1033 ± 23  928 ± 18 1576 ± 11 Carbide Kg/mm² R, % 100 79 77 73 65

Inclusion of Re in the binder matrices of the hardmetals increases the melting point of binder alloys that include Co—Re, Ni superalloy-Re, Ni superalloy-Re—Co. For example, the melting point of the sample P63 is much higher than the temperature of 2200° C. used for the solid-phase sintering process. Hot hardness values of such hardmetals with Re in the binders (e.g., P17 to P63) are much higher than conventional Co bound hardmetals(C2 and C6 carbides). In particular, the above measurements reveal that an increase in the concentration of Re in the binder increases the hardness at high temperatures. Among the tested samples, the sample P62A with pure Re as the binder has the highest hardness. The sample P63 with a binder composition of 94% of Re and 6% of the Ni-based superalloy R95 has the second highest hardness. The samples P40A(71.9% Re-29.1% R95), P49(69.9% Re-30.1% R95), P51(88.5% Re-11.5% R95), and P50(71.9% Re-28.1% R95) are the next group in their hardness. The sample P48 with 62.5% of Re and 37.5% of R95 in its binder has the lowest hardness at high temperatures among the tested materials in part because its Re content is the lowest.

In yet another category, a hardmetal or cermet may include TiC and TiN bonded in a binder matrix having Ni and Mo or Mo₂C. The binder Ni of cermet can be fully or partially replaced by Re, by Re plus Co, by Ni-based superalloy, by Re plus Ni-based superalloy, and by Re plus Co and Ni-based superalloy. Samples P38 and P39 are examples of Ni-bound cermets. The sample P34 is an example of Rene95-bound Cermet. The P35, P36, P37, and P45 are Re plus Rene95 bound cermet. Compositions of P34, 35, 36, 37, 38, 39, and 45 are listed in TABLE 16.

TABLE 16 Composition of P34 to P39 Weight % Re Rene95 Ni 1 Ni 2 TiC Mo₂C WC TaC P34 14.47 69.44 16.09 P35 8.77 10.27 65.37 15.23 P36 16.6 6.50 62.40 14.46 P37 23.8 3.09 59.38 13.76 P38 15.51 68.60 15.89 P39 15.51 68.60 15.89 P45 9.37 3.66 15.37 6.51 58.6 6.47

TABLES 17-29 list additional compositions with 3 exemplary composition ranges 1, 2, and 3 which may be used for different applications.

TABLE 17 Compositions that use pure Re as a binder for binding a carbide from carbides of IVb, Vb, & VIb columns of the Periodic Table or a nitride from nitrides of IVb & Vb columns Composition Composition Composition Estimated Range 1 Range 2 Range 3 Melting Volume % Weight % Volume % Weight % Volume % Weight % Point, ° C. Re Re 7.25 to 40   25 to 74 7.25 to 35   25 to 70 7.25 to 30   25 to 65 3000 to 3200 Bound TiC   60 to 92.75 26 to 75   65 to 92.75 30 to 75   70 to 92.75 35 to 75 TiC Re Re  3 to 40  9 to 68  4 to 35 12 to 63  5 to 30 14 to 58 3000 to 3200 Bound ZrC 60 to 97 32 to 93 65 to 96 37 to 88 70 to 95 42 to 86 ZrC Re Re 16.75 to 40   25 to 52 16.75 to 35   25 to 47 16.75 to 30   25 to 42 3000 to 3200 Bound HfC   60 to 83.25 48 to 75   65 to 83.25 53 to 75   70 to 83.25 58 to 75 HfC Re Re  3 to 40 11 to 72  4 to 35 14 to 67  5 to 30 17 to 62 2700 to 3100 Bound VC 60 to 97 28 to 89 65 to 96 33 to 86 70 to 95 38 to 83 VC Re Re  3 to 40  8 to 64  4 to 35 10 to 59  5 to 30 12 to 54 3000 to 3200 Bound NbC 60 to 97 36 to 92 65 to 96 41 to 90 70 to 95 46 to 88 NbC Re Re  3 to 40  4 to 49  4 to 35  6 to 44  5 to 30  7 to 38 3000 to 3200 Bound TaC 60 to 97 51 to 96 65 to 96 56 to 94 70 to 95 62 to 93 TaC Re Re  3 to 40  9 to 68  4 to 35 12 to 63  5 to 30 14 to 57 1700 to 1900 Bound Cr₂C₃ 60 to 97 32 to 91 65 to 96 37 to 88 70 to 95 43 to 86 Cr₂C₃ Re Re  3 to 40  7 to 61  4 to 35  9 to 55  5 to 30 11 to 50 2300 to 2600 Bound Mo₂C 60 to 97 39 to 93 65 to 96 45 to 91 70 to 95 50 to 89 Mo₂C Re Re 20 to 40 25 to 47 20 to 35 25 to 42 20 to 30 25 to 37 2700 to 2900 Bound WC 60 to 80 53 to 75 65 to 80 58 to 75 70 to 80 63 to 75 WC Re Re  3 to 40 11 to 72  4 to 35 14 to 68  5 to 30 17 to 62 2900 to 3100 Bound TiN 60 to 97 28 to 89 65 to 96 32 to 86 70 to 95 38 to 83 TiN Re Re  3 to 40  8 to 66  4 to 35 11 to 61  5 to 30 13 to 55 2900 to 3100 Bound ZrN 60 to 97 34 to 92 65 to 96 39 to 89 70 to 95 45 to 87 ZrN Re Re  3 to 40  4 to 50  4 to 35  6 to 45  5 to 30  7 to 39 3000 to 3200 Bound HfN 60 to 97 50 to 96 65 to 96 55 to 94 70 to 95 61 to 93 HfN Re Re  3 to 40  9 to 70  4 to 35 13 to 65  5 to 30 16 to 62 2100 to 2300 Bound VN 60 to 97 30 to 91 65 to 96 35 to 87 70 to 95 38 to 84 VN Re Re  3 to 40  8 to 66  4 to 35 11 to 61  5 to 30 13 to 55 2300 to 2500 Bound NbN 60 to 97 34 to 92 65 to 96 39 to 89 70 to 95 45 to 87 NbN Re Re  3 to 40  4 to 49  4 to 35  6 to 44  5 to 30  7 to 39 3000 to 3200 Bound TaN 60 to 97 51 to 96 65 to 96 56 to 94 70 to 95 61 to 93 TaN

TABLE 18 Compositions that use Ni-based superalloy(NBSA) in a binder for binding a nitride from nitrides of IVb &Vb columns of the Periodic Table. Composition Range 1 Composition Range 2 Composition Range 3 Volume % Weight % Volume % Weight % Volume % Weight % NBSA - NBSA  3 to 40  4 to 50  4 to 35  6 to 44  5 to 30  7 to 39 TiN TiN 60 to 97 50 to 96 65 to 96 56 to 94 70 to 95 61 to 93 NBSA - NBSA  3 to 40  3 to 42  4 to 35  4 to 37  5 to 30  5 to 32 ZrN ZrN 60 to 97 58 to 97 65 to 96 63 to 96 70 to 95 68 to 95 NBSA - NBSA  3 to 40 1.8 to 28   4 to 35 2.4 to 24   5 to 30  3 to 19 HfN HfN 60 to 97   72 to 98.2 65 to 96   76 to 97.6 70 to 95 81 to 97 NBSA - NBSA  3 to 40  4 to 47  4 to 35  5 to 42  5 to 30  7 to 36 VN VN 60 to 97 53 to 96 65 to 96 58 to 95 70 to 95 64 to 93 NBSA - NBSA  3 to 40  3 to 42  4 to 35  4 to 37  5 to 30  5 to 32 NbN NbN 60 to 97 52 to 97 65 to 96 33 to 96 70 to 95 68 to 95 NBSA - NBSA  3 to 40 1.7 to 27   4 to 35 2.3 to 23   5 to 30  3 to 19 TaN TaN 60 to 97   73 to 98.3 65 to 96   77 to 97.7 70 to 95 81 to 97

TABLE 19 Compositions that use Re and Ni-based superalloy (Re + NBSA) in a binder for binding a carbide from carbides of IVb, Vb, & VIb or a nitride from nitrides of IVb & Vb. The range of the binder is from 1% Re + 99% superalloy to 99% Re + 1% superalloy. Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (Re + NBSA) - Re 0.03 to 39.6 0.13 to 73.6 0.04 to 34.7 0.17 to 69.3 0.05 to 29.7 0.21 to 64.3 TiC NBSA 0.03 to 39.6 0.04 to 51.1 0.04 to 34.7 0.06 to 45.9 0.05 to 29.7 0.07 to 40.4 TiC 60 to 97 26.1 to 95.1 65 to 96 30.5 to 93.6 70 to 95 35.5 to 92   (Re + NBSA) - Re 0.03 to 39.6 0.09 to 67.7 0.04 to 34.7 0.13 to 62.9 0.05 to 29.7 0.16 to 57.5 ZrC NBSA 0.03 to 39.6 0.03 to 44.1 0.04 to 34.7 0.05 to 39.0 0.05 to 29.7 0.06 to 33.8 ZrC 60 to 97 32 to 96 65 to 96 37 to 95 70 to 95 42 to 94 (Re + NBSA) - Re 0.03 to 39.6 0.05 to 52.1 0.04 to 34.7 0.07 to 46.8 0.05 to 29.7 0.08 to 41.2 HfC NBSA 0.03 to 39.6 0.02 to 29.2 0.04 to 34.7 0.025 to 25   0.05 to 29.7 0.03 to 21   HfC 60 to 97 47.7 to 98.1 65 to 96   53 to 97.4 70 to 95 58.6 to 96.7 (Re + NBSA) - Re 0.03 to 39.6 0.11 to 71.5 0.04 to 34.7 0.15 to 67.0 0.05 to 29.7 0.19 to 61.8 VC NBSA 0.03 to 39.6 0.04 to 48.4 0.04 to 34.7 0.05 to 43.3 0.05 to 29.7 0.06 to 37.9 VC 60 to 97 28.3 to 95.6 65 to 96 32.8 to 94.2 70 to 95   38 to 92.8 (Re + NBSA) - Re 0.03 to 39.6 0.08 to 63.8 0.04 to 34.7  0.1 to 58.7 0.05 to 29.7 0.13 to 53.1 NbC NBSA 0.03 to 39.6 0.03 to 39.9 0.04 to 34.7 0.04 to 35   0.05 to 29.7 0.05 to 30   NbC 60 to 97   36 to 96.9 65 to 96   41 to 95.8 70 to 95 46.6 to 94.8 (Re + NBSA) - Re 0.03 to 39.6 0.04 to 48.8 0.04 to 34.7 0.06 to 43.5 0.05 to 29.7 0.07 to 38   TaC NBSA 0.03 to 39.6 0.016 to 26.5   0.04 to 34.7 0.02 to 22.6 0.05 to 29.7 0.03 to 18.9 TaC 60 to 97   51 to 98.3 65 to 96 56.3 to 97.7 70 to 95 61.8 to 97.1 (Re + NBSA) - Re 0.03 to 39.6 0.09 to 67.3 0.04 to 34.7 0.12 to 62.5 0.05 to 29.7 0.16 to 57.0 Cr₂C₃ NBSA 0.03 to 39.6 0.03 to 43.6 0.04 to 34.7 0.04 to 38.6 0.05 to 29.7 0.05 to 33.4 Cr₂C₃ 60 to 97 32.4 to 96.4 65 to 96 37.3 to 95.2 70 to 95 42.8 to 94.0 (Re + NBSA) - Re 0.03 to 39.6 0.07 to 60.2 0.04 to 34.7 0.1 to 55  0.05 to 29.7 0.12 to 49.3 Mo₂C NBSA 0.03 to 39.6 0.025 to 36.3  0.04 to 34.7 0.03 to 31.6 0.05 to 29.7 0.04 to 26.9 Mo₂C 60 to 97 39.6 to 97.3 65 to 96 44.8 to 96.4 70 to 95 50.5 to 95.5 (Re + NBSA) - Re 0.03 to 39.6 0.04 to 46.9 0.04 to 34.7 0.05 to 41.7 0.05 to 29.7 0.07 to 36.3 WC NBSA 0.03 to 39.6 0.015 to 25   0.04 to 34.7 0.02 to 21.3 0.05 to 29.7 0.025 to 17.8  WC 60 to 97 52.9 to 98.4 65 to 96 58.2 to 97.9 70 to 95 63.6 to 97.3 (Re + NBSA) - Re 0.03 to 39.6  0.1 to 71.7 0.04 to 34.7 0.15 to 67.2 0.05 to 29.7 0.19 to 62   TiN NBSA 0.03 to 39.6 0.04 to 48.7 0.04 to 34.7 0.05 to 43.5 0.05 to 29.7 0.06 to 38   TiN 60 to 97   28 to 95.6 65 to 96 32.6 to 94.1 70 to 95 37.8 to 92.7 (Re + NBSA) - Re 0.03 to 39.6 0.09 to 65.3 0.04 to 34.7  0.1 to 60.3 0.05 to 29.7 0.14 to 54.8 ZrN NBSA 0.03 to 39.6 0.03 to 41.4 0.04 to 34.7 0.04 to 36.5 0.05 to 29.7 0.05 to 31.4 ZrN 60 to 97 34.5 to 96.7 65 to 96 39.4 to 95.6 70 to 95   45 to 94.5 (Re + NBSA) - Re 0.03 to 39.6 0.05 to 50   0.04 to 34.7 0.06 to 44.7 0.05 to 29.7 0.08 to 39.2 HfN NBSA 0.03 to 39.6 0.017 to 27.5  0.04 to 34.7 0.02 to 23.5 0.05 to 29.7 0.03 to 19.6 HfN 60 to 97 49.8 to 98.2 65 to 96 55.1 to 97.6 70 to 95 60.7 to 97   (Re + NBSA) - Re 0.03 to 39.6  0.1 to 69.6 0.04 to 34.7 0.14 to 65   0.05 to 29.7 0.17 to 59.6 VN NBSA 0.03 to 39.6 0.04 to 46.2 0.04 to 34.7 0.05 to 41.1 0.05 to 29.7 0.06 to 35.8 VN 60 to 97 30 to 96 65 to 96   35 to 94.7 70 to 95   40 to 93.3 (Re + NBSA) - Re 0.03 to 39.6 0.09 to 65.3 0.04 to 34.7  0.1 to 60.4 0.05 to 29.7 0.14 to 54.9 NbN NBSA 0.03 to 39.6 0.03 to 41.5 0.04 to 34.7 0.04 to 36.5 0.05 to 29.7 0.05 to 31.5 NbN 60 to 97 34.4 to 96.7 65 to 96 39.4 to 95.6 70 to 95   45 to 94.5 (Re + NBSA) - Re 0.03 to 39.6 0.04 to 49.1 0.04 to 34.7 0.06 to 43.8 0.05 to 29.7 0.08 to 38.3 TaN NBSA 0.03 to 39.6 0.017 to 26.8  0.04 to 34.7 0.02 to 22.8 0.05 to 29.7 0.027 to 19   TaN 60 to 97 50.7 to 98.3 65 to 96   56 to 97.7 70 to 95 61.5 to 97  

TABLE 20 Compositions that use Re and Co (Re + Co) in a binder for binding a carbide from carbides of IVb, Vb, & VIb or a nitride from nitrides of IVb & Vb. The range of Binder is from 1% Re + 99% Co to 99% Re + 1% Co. Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (Re + Co) - Re 0.03 to 39.6 0.13 to 73.6 0.04 to 34.7 0.17 to 69.3 0.05 to 29.7 0.20 to 64.3 TiC Co 0.03 to 39.6 0.05 to 54.1 0.04 to 34.7 0.07 to 48.9 0.05 to 29.7 0.08 to 43.3 TiC 60 to 97 26.1 to 94.6 65 to 96 30.4 to 92.8 70 to 95 35.5 to 91   (Re + Co) - Re 0.03 to 39.6 0.09 to 67.7 0.04 to 34.7 0.13 to 62.9 0.05 to 29.7 0.16 to 57.5 ZrC Co 0.03 to 39.6 0.04 to 47.1 0.04 to 34.7 0.05 to 42.0 0.05 to 29.7 0.06 to 36.6 ZrC 60 to 97 32 to 96 65 to 96 37 to 95 70 to 95 42 to 93 (Re + Co) - Re 0.03 to 39.6 0.05 to 52.1 0.04 to 34.7 0.07 to 46.8 0.05 to 29.7 0.08 to 41.2 HfC Co 0.03 to 39.6 0.02 to 31.8 0.04 to 34.7 0.028 to 27   0.05 to 29.7 0.035 to 23   HfC 60 to 97 47.6 to 97.8 65 to 96   53 to 97.1 70 to 95 58.6 to 96.3 (Re + Co) - Re 0.03 to 39.6 0.11 to 71.4 0.04 to 34.7 0.15 to 67.0 0.05 to 29.7 0.19 to 61.8 VC Co 0.03 to 39.6 0.05 to 51.5 0.04 to 34.7 0.06 to 46.3 0.05 to 29.7 0.07 to 40.8 VC 60 to 97 28.3 to 95.1 65 to 96 32.8 to 93.5 70 to 95 38 to 92 (Re + Co) - Re 0.03 to 39.6 0.08 to 63.8 0.04 to 34.7  0.1 to 58.7 0.05 to 29.7 0.13 to 53.1 NbC Co 0.03 to 39.6 0.03 to 42.8 0.04 to 34.7 0.04 to 37.8 0.05 to 29.7 0.05 to 32.6 NbC 60 to 97   36 to 96.5 65 to 96   41 to 95.4 70 to 95 46.6 to 94.2 (Re + Co) - Re 0.03 to 39.6 0.04 to 48.8 0.04 to 34.7 0.06 to 43.5 0.05 to 29.7 0.07 to 38   TaC Co 0.03 to 39.6 0.018 to 28.9  0.04 to 34.7 0.024 to 24.8  0.05 to 29.7 0.03 to 20.8 TaC 60 to 97 51 to 98 65 to 96 56.3 to 97.4 70 to 95 61.8 to 96.8 (Re + Co) - Re 0.03 to 39.6 0.09 to 67.3 0.04 to 34.7 0.12 to 62.5 0.05 to 29.7 0.15 to 57.0 Cr₂C₃ Co 0.03 to 39.6 0.04 to 46.6 0.04 to 34.7 0.05 to 41.5 0.05 to 29.7 0.06 to 36.1 Cr₂C₃ 60 to 97 32.4 to 96   65 to 96 37.3 to 94.6 70 to 95 42.7 to 93.3 (Re + Co) - Re 0.03 to 39.6 0.07 to 60.2 0.04 to 34.7 0.1 to 55  0.05 to 29.7 0.12 to 49.3 Mo₂C Co 0.03 to 39.6 0.03 to 39.2 0.04 to 34.7 0.04 to 34.3 0.05 to 29.7 0.05 to 29.4 Mo₂C 60 to 97 39.6 to 97   65 to 96 44.8 to 96   70 to 95 50.5 to 95   (Re + Co) - Re 0.03 to 39.6 0.04 to 46.9 0.04 to 34.7 0.05 to 41.7 0.05 to 29.7 0.07 to 36.3 WC Co 0.03 to 39.6 0.017 to 27.4  0.04 to 34.7 0.023 to 23.4 0.05 to 29.7 0.028 to 19.6  WC 60 to 97 52.9 to 98.2 65 to 96 58.2 to 97   70 to 95 63.6 to 97   (Re + Co) - Re 0.03 to 39.6  0.1 to 71.6 0.04 to 34.7 0.15 to 67.1 0.05 to 29.7 0.19 to 62   TiN Co 0.03 to 39.6 0.05 to 51.7 0.04 to 34.7 0.06 to 46.5 0.05 to 29.7 0.07 to 41   TiN 60 to 97 28 to 95 65 to 96 32.6 to 93.4 70 to 95 37.8 to 92   (Re + Co) - Re 0.03 to 39.6 0.09 to 65.3 0.04 to 34.7 0.11 to 60.3 0.05 to 29.7 0.14 to 54.8 ZrN Co 0.03 to 39.6 0.035 to 44.4  0.04 to 34.7 0.046 to 39.3  0.05 to 29.7 0.056 to 34   ZrN 60 to 97 34.5 to 96.3 65 to 96 39.4 to 95   70 to 95   45 to 93.8 (Re + Co) - Re 0.03 to 39.6 0.05 to 50   0.04 to 34.7 0.06 to 44.7 0.05 to 29.7 0.08 to 39.2 HfN Co 0.03 to 39.6 0.02 to 30   0.04 to 34.7 0.026 to 25.7  0.05 to 29.7 0.03 to 21.6 HfN 60 to 97 49.8 to 98   65 to 96 55.1 to 97.3 70 to 95 60.7 to 96.6 (Re + Co) - Re 0.03 to 39.6  0.1 to 69.6 0.04 to 34.7 0.14 to 65   0.05 to 29.7 0.17 to 59.6 VN Co 0.03 to 39.6 0.04 to 49.3 0.04 to 34.7 0.055 to 44   0.05 to 29.7 0.067 to 38.6  VN 60 to 97   30 to 95.5 65 to 96 35 to 94 70 to 95   40 to 92.6 (Re + Co) - Re 0.03 to 39.6 0.09 to 65.3 0.04 to 34.7 0.11 to 60.4 0.05 to 29.7 0.14 to 54.8 NbN Co 0.03 to 39.6 0.035 to 44.5  0.04 to 34.7 0.046 to 39.4  0.05 to 29.7 0.057 to 34.1  NbN 60 to 97 34.4 to 96.3 65 to 96 39.4 to 95   70 to 95   45 to 93.8 (Re + Co) - Re 0.03 to 39.6 0.04 to 49.1 0.04 to 34.7 0.06 to 43.8 0.05 to 29.7 0.075 to 38.3  TaN Co 0.03 to 39.6 0.019 to 29.2  0.04 to 34.7 0.025 to 25   0.05 to 29.7 0.03 to 21   TaN 60 to 97 50.7 to 98   65 to 96   56 to 97.4 70 to 95 61.5 to 96.7

TABLE 21 Compositions that use Ni-based superalloy (NBSA) and Co in a binder for binding a carbide from carbides of IVb, Vb, & VIb or a nitride from nitrides of IVb & Vb. The range of Binder is from 1% NBSA + 99% Co to 99% NBSA + 1% Co. Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (NBSA + Co) - NBSA 0.03 to 39.6 0.05 to 51.5 0.04 to 34.7 0.06 to 46.2 0.05 to 29.7 0.08 to 40.6 TiC Co 0.03 to 39.6 0.05 to 54.5 0.04 to 34.7 0.07 to 49.2 0.05 to 29.7 0.09 to 43.6 TiC 60 to 97 45 to 95 65 to 96   50 to 93.6 70 to 95 56 to 92 (NBSA + Co) - NBSA 0.03 to 39.6 0.04 to 44.4 0.04 to 34.7 0.05 to 39.2 0.05 to 29.7 0.06 to 57.5 ZrC Co 0.03 to 39.6 0.04 to 47.4 0.04 to 34.7 0.05 to 42   0.05 to 29.7 0.07 to 34   ZrC 60 to 97 52 to 96 65 to 96 57 to 95 70 to 95 63 to 94 (NBSA + Co) - NBSA 0.03 to 39.6 0.02 to 29   0.04 to 34.7 0.026 to 25   0.05 to 29.7 0.03 to 21   HfC Co 0.03 to 39.6 0.02 to 32   0.04 to 34.7 0.03 to 27.5 0.05 to 29.7 0.036 to 23   HfC 60 to 97 68 to 98 65 to 96   72 to 97.4 70 to 95   77 to 96.8 (NBSA + Co) - NBSA 0.03 to 39.6 0.04 to 49   0.04 to 34.7 0.06 to 44   0.05 to 29.7 0.07 to 38   VC Co 0.03 to 39.6 0.05 to 52   0.04 to 34.7 0.06 to 47   0.05 to 29.7 0.08 to 41   VC 60 to 97 48 to 96 65 to 96   53 to 93.5 70 to 95 59 to 93 (NBSA + Co) - NBSA 0.03 to 39.6 0.03 to 40   0.04 to 34.7 0.04 to 35   0.05 to 29.7 0.05 to 30   NbC Co 0.03 to 39.6 0.035 to 43   0.04 to 34.7 0.046 to 38   0.05 to 29.7 0.06 to 33   NbC 60 to 97 57 to 97 65 to 96 62 to 96 70 to 95 67 to 95 (NBSA + Co) - NBSA 0.03 to 39.6 0.017 to 27   0.04 to 34.7 0.022 to 23   0.05 to 29.7 0.03 to 19   TaC Co 0.03 to 39.6 0.02 to 29   0.04 to 34.7 0.025 to 25   0.05 to 29.7 0.03 to 21   TaC 60 to 97 71 to 98 65 to 96   75 to 97.8 70 to 95 79 to 97 (NBSA + Co) - NBSA 0.03 to 39.6 0.09 to 67.3 0.04 to 34.7 0.12 to 62.5 0.05 to 29.7 0.15 to 57.0 Cr₂C₃ Co 0.03 to 39.6 0.04 to 44   0.04 to 34.7 0.05 to 39   0.05 to 29.7 0.06 to 34   Cr₂C₃ 60 to 97 53 to 96 65 to 96 58 to 95 70 to 95 63 to 94 (NBSA + Co) - NBSA 0.03 to 39.6 0.026 to 36.5  0.04 to 34.7 0.035 to 32   0.05 to 29.7 0.044 to 27   Mo₂C Co 0.03 to 39.6 0.03 to 39   0.04 to 34.7 0.04 to 34   0.05 to 29.7 0.05 to 30   Mo₂C 60 to 97 60 to 97 65 to 96 65 to 96 70 to 95   70 to 95.6 (NBSA + Co) - NBSA 0.03 to 39.6 0.04 to 46.9 0.04 to 34.7 0.05 to 41.7 0.05 to 29.7 0.07 to 36.3 WC Co 0.03 to 39.6 0.018 to 27.5  0.04 to 34.7 0.024 to 23.5  0.05 to 29.7 0.03 to 19.7 WC 60 to 97 72 to 98 65 to 96 76 to 98 70 to 95 80 to 97 (NBSA + Co) - NBSA 0.03 to 39.6 0.4 to 49  0.04 to 34.7 0.06 to 44   0.05 to 29.7 0.07 to 38   TiN Co 0.03 to 39.6 0.05 to 52   0.04 to 34.7 0.065 to 47   0.05 to 29.7 0.08 to 41   TiN 60 to 97 47 to 96 65 to 96 53 to 94 70 to 95 58 to 93 (NBSA + Co) - NBSA 0.03 to 39.6 0.03 to 42   0.04 to 34.7 0.04 to 37   0.05 to 29.7 0.05 to 32   ZrN Co 0.03 to 39.6 0.04 to 45   0.04 to 34.7 0.05 to 40   0.05 to 29.7 0.06 to 34   ZrN 60 to 97 55 to 97 65 to 96 60 to 96 70 to 95 65 to 95 (NBSA + Co) - NBSA 0.03 to 39.6 0.02 to 31   0.04 to 34.7 0.027 to 27   0.05 to 29.7 0.03 to 22   HfN Co 0.03 to 39.6 0.02 to 27   0.04 to 34.7 0.024 to 23   0.05 to 29.7 0.03 to 20   HfN 60 to 97 70 to 98 65 to 96   74 to 97.6 70 to 95 78 to 97 (NBSA + Co) - NBSA 0.03 to 39.6 0.045 to 53   0.04 to 34.7 0.06 to 47   0.05 to 29.7 0.07 to 41   VN Co 0.03 to 39.6 0.04 to 44   0.04 to 34.7 0.055 to 40   0.05 to 29.7 0.066 to 34   VN 60 to 97 50 to 96 65 to 96 55 to 95 70 to 95 61 to 93 (NBSA + Co) - NBSA 0.03 to 39.6 0.04 to 47   0.04 to 34.7 0.05 to 41   0.05 to 29.7 0.06 to 36   NbN Co 0.03 to 39.6 0.03 to 40   0.04 to 34.7 0.04 to 35   0.05 to 29.7 0.05 to 30   NbN 60 to 97 55 to 97 65 to 96 60 to 96 70 to 95 65 to 95 (Re + Co) - NBSA 0.03 to 39.6 0.02 to 30   0.04 to 34.7 0.026 to 26   0.05 to 29.7 0.032 to 22   TaN Co 0.03 to 39.6 0.017 to 26   0.04 to 34.7 0.023 to 23   0.05 to 29.7 0.03 to 19   TaN 60 to 97 70 to 98 65 to 96   75 to 97.7 70 to 95 79 to 97

TABLE 22 Compositions that use Re, Ni-based superalloy (NBSA), and Co in a binder for binding a carbide from carbides of IVb, Vb, & VIb or a nitride from nitrides of IVb & Vb. The range of Binder is from 0.5% Re + 0.5% Co + 99% superalloy to 99% Re + 0.5% Co + 0.5% Superalloy to 0.5% Re + 99% Co + 0.5% Superalloy Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (Re + Co + Re 0.015 to 39.6  0.06 to 73.6 0.02 to 34.65  0.08 to 69.3 0.025 to 29.7  0.1 to 64.3 NBSA) - NBSA 0.015 to 39.6  0.02 to 51.3 0.02 to 34.65  0.03 to 46.0 0.025 to 29.7 0.035 to 40.5 TiC Co 0.015 to 39.6  0.03 to 54.3 0.02 to 34.65 0.036 to 49.0 0.025 to 29.7 0.045 to 43.5 TiC  60 to 97  26 to 95 65 to 96   30 to 94  70 to 95  35 to 92 (Re + Co + Re 0.015 to 39.6  0.05 to 67.7 0.02 to 34.65  0.06 to 62.9 0.025 to 29.7  0.08 to 57.5 NBSA) - NBSA 0.015 to 39.6 0.017 to 44.2 0.02 to 34.65 0.022 to 39.1 0.025 to 29.7 0.028 to 33.9 ZrC Co 0.015 to 39.6  0.02 to 47.2 0.02 to 34.65 0.027 to 42.0 0.025 to 29.7 0.034 to 36.7 ZrC  60 to 97  32 to 96 65 to 96   37 to 95  70 to 95  43 to 94 (Re + Co + Re 0.015 to 39.6 0.025 to 52.1 0.02 to 34.65 0.034 to 46.8 0.025 to 29.7 0.042 to 41.2 NBSA) - NBSA 0.015 to 39.6 0.009 to 29.3 0.02 to 34.65 0.012 to 25.1 0.025 to 29.7 0.015 to 21   HfC Co 0.015 to 39.6  0.01 to 31.8 0.02 to 34.65 0.014 to 27.4 0.025 to 29.7 0.018 to 23.1 HfC  60 to 97  48 to 98 65 to 96    53 to 97.4  70 to 95   59 to 96.8 (Re + Co + Re 0.015 to 39.6  0.06 to 71.5 0.02 to 34.65 0.08 to 67  0.025 to 29.7  0.09 to 61.8 NBSA) - NBSA 0.015 to 39.6  0.02 to 48.6 0.02 to 34.65 0.026 to 43.4 0.025 to 29.7 0.032 to 38   VC Co 0.015 to 39.6 0.024 to 51.7 0.02 to 34.65 0.032 to 46.4 0.025 to 29.7  0.04 to 40.9 VC  60 to 97  28 to 96 65 to 96   33 to 94  70 to 95  38 to 93 (Re + Co + Re 0.015 to 39.6  0.04 to 63.8 0.02 to 34.65  0.05 to 58.7 0.025 to 29.7  0.07 to 53.1 NBSA) - NBSA 0.015 to 39.6 0.015 to 40   0.02 to 34.65 0.02 to 35  0.025 to 29.7 0.024 to 30   NbC Co 0.015 to 39.6 0.017 to 43   0.02 to 34.65 0.023 to 37.9 0.025 to 29.7  0.03 to 32.7 NbC  60 to 97  36 to 97 65 to 96   41 to 96  70 to 95  47 to 95 (Re + Co + Re 0.015 to 39.6  0.02 to 48.8 0.02 to 34.65  0.03 to 43.5 0.025 to 29.7 0.04 to 38   NBSA) - NBSA 0.015 to 39.6 0.008 to 26.6 0.02 to 34.65 0.011 to 22.6 0.025 to 29.7 0.013 to 18.9 TaC Co 0.015 to 39.6 0.01 to 29  0.02 to 34.65 0.013 to 24.8 0.025 to 29.7 0.016 to 20.8 TaC  60 to 97   51 to 98.3 65 to 96    56 to 97.7  70 to 95  61.8 to 97.2 (Re + Co + Re 0.015 to 39.6  0.05 to 67.3 0.02 to 34.65  0.06 to 62.5 0.025 to 29.7 0.08 to 57  NBSA) - NBSA 0.015 to 39.6 0.017 to 43.8 0.02 to 34.65 0.022 to 38.7 0.025 to 29.7 0.027 to 33.5 Cr₂C₃ Co 0.015 to 39.6  0.02 to 46.8 0.02 to 34.65 0.027 to 41.6 0.025 to 29.7 0.033 to 36.2 Cr₂C₃  60 to 97  32 to 96 65 to 96   37 to 95  70 to 95  43 to 94 (Re + Co + Re 0.015 to 39.6  0.03 to 60.2 0.02 to 34.65 0.05 to 55  0.025 to 29.7 0.06 to 49  NBSA) - NBSA 0.015 to 39.6 0.013 to 36.4 0.02 to 34.65 0.017 to 31.7 0.025 to 29.7 0.02 to 27  Mo₂C Co 0.015 to 39.6 0.015 to 39.3 0.02 to 34.65 0.02 to 34  0.025 to 29.7 0.025 to 29   Mo₂C  60 to 97  39 to 97 65 to 96   45 to 96  70 to 95   50 to 95.6 (Re + Co + Re 0.015 to 39.6  0.02 to 46.9 0.02 to 34.65 0.027 to 41.7 0.025 to 29.7 0.034 to 36.3 NBSA) - NBSA 0.015 to 39.6 0.008 to 25.1 0.02 to 34.65  0.01 to 21.3 0.025 to 29.7 0.013 to 17.8 WC Co 0.015 to 39.6 0.009 to 27.5 0.02 to 34.65 0.012 to 23.5 0.025 to 29.7 0.015 to 19.6 WC  60 to 97  53 to 98 65 to 96    58 to 97.8  70 to 95   64 to 97.4 (Re + Co + Re 0.015 to 39.6  0.06 to 71.6 0.02 to 34.65  0.08 to 67.2 0.025 to 29.7  0.1 to 62 NBSA) - NBSA 0.015 to 39.6  0.02 to 48.8 0.02 to 34.65 0.027 to 43.6 0.025 to 29.7 0.032 to 38.2 TiN Co 0.015 to 39.6 0.025 to 51.9 0.02 to 34.65  0.03 to 46.6 0.025 to 29.7 0.04 to 41  TiN  60 to 97  28 to 96 65 to 96   33 to 94  70 to 95  38 to 93 (Re + Co + Re 0.015 to 39.6  0.04 to 65.3 0.02 to 34.65  0.06 to 60.3 0.025 t 29.7o  0.07 to 54.8 NBSA) - NBSA 0.015 to 39.6 0.016 to 41.6 0.02 to 34.65  0.02 to 36.6 0.025 to 29.7 0.025 to 31.5 ZrN Co 0.015 to 39.6  0.02 to 44.6 0.02 to 34.65 0.025 to 40   0.025 to 29.7 0.03 to 34  ZrN  60 to 97  34 to 97 65 to 96   39 to 96  70 to 95  45 to 95 Re + Co + Re 0.015 to 39.6 0.02 to 50  0.02 to 34.65 0.03 to 45 0.025 to 29.7 0.04 to 39  NBSA - NBSA 0.015 to 39.6 0.009 to 27.5 0.02 to 34.65 0.011 to 23.5 0.025 to 29.7 0.014 to 20   HfN Co 0.015 to 39.6 0.01 to 30  0.02 to 34.65 0.013 to 25.8 0.025 to 29.7 0.017 to 22   HfN  60 to 97  50 to 98 65 to 96    55 to 97.6  70 to 95  61 to 97 Re + Co + Re 0.015 to 39.6 0.05 to 60 0.02 to 34.65 0.07 to 65  0.025 to 29.7 0.09 to 60  NBSA - NBSA 0.015 to 39.6  0.02 to 46.4 0.02 to 34.65 0.024 to 41.2 0.025 to 29.7 0.03 to 36  VN Co 0.015 to 39.6 0.02 to 49  0.02 to 34.65 0.03 to 44  0.025 to 29.7 0.04 to 39  VN  60 to 97  30 to 96 65 to 96   35 to 95  70 to 95  40 to 93 Re + Co + Re 0.015 to 39.6 0.04 to 65  0.02 to 34.65 0.06 to 60  0.025 to 29.7 0.07 to 55  NBSA - NBSA 0.015 to 39.6 0.016 to 42   0.02 to 34.65 0.02 to 37  0.025 to 29.7 0.025 to 32   NbN Co 0.015 to 39.6 0.02 to 45  0.02 to 34.65 0.025 to 39.5 0.025 to 29.7 0.03 to 34  NbN  60 to 97  34 to 97 65 to 96   39 to 96  70 to 95  45 to 95 Re + Co + Re 0.015 to 39.6 0.02 to 49  0.02 to 34.65 0.03 to 44  0.025 to 29.7 0.04 to 38  NBSA - NBSA 0.015 to 39.6 0.008 to 27   0.02 to 34.65 0.011 to 23   0.025 to 29.7 0.014 to 19   TaN Co 0.015 to 39.6 0.01 to 29  0.02 to 34.65 0.013 to 25   0.025 to 29.7 0.016 to 21   TaN  60 to 97   51 to 98.3 65 to 96    56 to 97.7  70 to 95  61.5 to 97.1

TABLE 23 Compositions that use Re for binding WC + TiC or WC + TaC or WC + TiC + TaC Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % Re - Re 3 to 40  4 to 54 4 to 35 5 to 49 5 to 30 7 to 43 WC + TiC WC 40 to 96  40 to 96  43 to 94.5 44 to 94  45 to 93  48 to 93  TiC 1 to 48 0.3 to 21  1.5 to 43   0.5 to 19   2 to 45 0.6 to 18   Re - Re 3 to 40  4 to 48 4 to 35 5 to 42 5 to 30 7 to 37 WC + TaC WC  50 to 96.5 44 to 96 55 to 95  49 to 94   60 to 93.5 55 to 92  TaC 0.5 to 24   0.5 to 21  1 to 22 1 to 19 1.5 to 18   1.5 to 18   Re - Re 3 to 40  4 to 48 4 to 35 5 to 43 5 to 30 7 to 38 WC + TiC + WC  40 to 95.5 36 to 95 45 to 93  41 to 93  50 to 90  48 to 90  TaC TiC 1 to 48 0.3 to 22  2 to 45 0.6 to 20   3 to 42 0.9 to 18   TaC 0.5 to 20   0.5 to 25  1 to 18 0.8 to 22   2 to 15 2 to 17

TABLE 24 Compositions that use Ni-based superalloy (NBSA) for binding WC + TiC or WC + TaC or WC + TiC + TaC Composition Composition Composition Range 1 Range 2 Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % NBSA - NBSA 3 to 40 1.5 to 31 4 to 35 2 to 26 5 to 30 3 to 23 WC + TiC WC 40 to 96   60 to 98  43 to 94.5 63 to 97  45 to 93   66 to 96.5 TiC 1 to 48 0.3 to 25 1.5 to 43   0.5 to 22   2 to 45 0.6 to 20   NBSA - NBSA 3 to 40 1.5 to 26 4 to 35 2 to 22 5 to 30 3 to 18 WC + TaC WC  50 to 96.5  63 to 98 55 to 95  67 to 97   60 to 93.5 71 to 96  TaC 0.5 to 24   0.5 to 26 1 to 22 1 to 23 1.5 to 18   1.5 to 21   NBSA - NBSA 3 to 40 1.5 to 26 4 to 35 2 to 22 5 to 30 3 to 19 WC + TiC + WC  40 to 95.5  51 to 98 45 to 93  56 to 96  50 to 90  61 to 94  TaC TiC 1 to 48 0.4 to 23 2 to 45 0.8 to 21   3 to 42 1 to 19 TaC 0.5 to 20   0.6 to 26 1 to 18 1 to 23 2 to 15 2 to 18

TABLE 25 Compositions that use Re and Ni-based superalloy (NBSA) in a binder for binding WC + TiC or WC + TaC or WC + TiC + TaC Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (Re + Re 0.03 to 39.6 0.04 to 52  0.04 to 34.65 0.06 to 48  0.05 to 29.7 0.07 to 45   NBSA) - NBSA 0.03 to 39.6 0.015 to 29  0.04 to 34.65 0.02 to 26  0.05 to 29.7 0.026 to 23   WC + TiC WC 40 to 96  40 to 98  43 to 94.5  44 to 97 45 to 93   48 to 96.6 TiC  1 to 48 0.3 to 24 1.5 to 45   0.5 to 22  2 to 42 0.6 to 21  (Re + Re 0.03 to 39.6 0.04 to 47  0.04 to 34.65 0.055 to 42  0.05 to 29.7 0.07 to 37   NBSA) - NBSA 0.03 to 39.6 0.015 to 25  0.04 to 34.65 0.02 to 22  0.05 to 29.7 0.025 to 18   WC + TaC WC   50 to 96.5  44 to 98 55 to 95   50 to 97 60 to 93   55 to 95.5 TaC 0.5 to 22  0.5 to 24 1 to 20    1 to 21.5  2 to 18  2 to 19 (Re + Re 0.03 to 39.6 0.04 to 53  0.04 to 34.65 0.06 to 47  0.05 to 29.7 0.07 to 41   NBSA) - NBSA 0.03 to 39.6 0.015 to 30  0.04 to 34.65 0.02 to 25  0.05 to 29.7 0.026 to 21   WC + TiC + WC   40 to 95.5  40 to 98 45 to 93   46 to 96 50 to 90 51 to 94 TaC TiC  1 to 48 0.3 to 23 2 to 45 0.6 to 21  3 to 42 0.9 to 19  TaC 0.5 to 20  0.4 to 26 1 to 18 0.8 to 23  2 to 15  2 to 18

TABLE 26 Compositions that use Re and Co in a binder for binding WC + TiC or WC + TaC or WC + TiC + TaC Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (Re + Re 0.03 to 39.6 0.04 to 53  0.04 to 34.65 0.055 to 48 0.05 to 29.7 0.07 to 43 Co) - Co 0.03 to 39.6 0.017 to 31  0.04 to 34.65 0.023 to 28 0.05 to 29.7 0.03 to 26 WC + TiC WC 40 to 96  40 to 98  43 to 94.5   44 to 97 45 to 93   48 to 96 TiC  1 to 48 0.3 to 23 1.5 to 45    0.5 to 22  2 to 42  0.6 to 21 (Re + Re 0.03 to 39.6 0.04 to 47  0.04 to 34.65 0.055 to 42 0.05 to 29.7 0.07 to 37 Co) - CO 0.03 to 39.6 0.017 to 28  0.04 to 34.65 0.023 to 24 0.05 to 29.7 0.03 to 20 WC + TaC WC   50 to 96.5  44 to 98 55 to 95    50 to 97 60 to 93   55 to 95 TaC 0.5 to 22  0.5 to 24 1 to 20    1 to 21  2 to 18   2 to 19 (Re + Re 0.03 to 39.6 0.04 to 53  0.04 to 34.65  0.06 to 47 0.05 to 29.7 0.07 to 41 Co) - Co 0.03 to 39.6 0.017 to 33  0.04 to 34.65 0.023 to 28 0.05 to 29.7 0.03 to 23 WC + TiC + WC   40 to 95.5  40 to 98 45 to 93    46 to 96 50 to 90   51 to 94 TaC TiC  1 to 48 0.3 to 23 2 to 45  0.6 to 21  3 to 42  0.9 to 19 TaC 0.5 to 20  0.4 to 26 1 to 18  0.8 to 23  2 to 15   2 to 18

TABLE 27 Compositions that use Co and Ni-based superalloy (NBSA) in a binder for binding WC + TiC or WC + TaC or WC + TiC + TaC Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (Co + Co 0.03 to 39.6 0.018 to 33 0.04 to 34.65 0.024 to 29   0.05 to 29.7 0.03 to 25 NBSA) - NBSA 0.03 to 39.6 0.015 to 29 0.04 to 34.65 0.02 to 26   0.05 to 29.7 0.03 to 23 WC + TiC WC 40 to 96   58 to 98  43 to 94.5 61 to 97 45 to 93   64 to 96.7 TiC  1 to 48  0.3 to 24 1.5 to 45   0.5 to 22   2 to 42  0.7 to 21 (Co + Co 0.03 to 39.6 0.018 to 28 0.04 to 34.65 0.024 to 24   0.05 to 29.7 0.03 to 20 NBSA) - NBSA 0.03 to 39.6 0.015 to 25 0.04 to 34.65 0.02 to 22   0.05 to 29.7 0.025 to 18  WC + TaC WC   50 to 96.5   61 to 98 55 to 95  65 to 97 60 to 93   69 to 95 TaC 0.5 to 22   0.5 to 24 1 to 20   1 to 21.5  2 to 18   2 to 19 (Co + Co 0.03 to 39.6 0.018 to 33 0.04 to 34.65 0.024 to 28   0.05 to 29.7 0.03 to 23 NBSA) - NBSA 0.03 to 39.6 0.015 to 30 0.04 to 34.65 0.02 to 25   0.05 to 29.7 0.026 to 21  WC + TiC + WC   40 to 95.5   57 to 98 45 to 93  62 to 96 50 to 90   67 to 94 TaC TiC  1 to 48  0.4 to 23 2 to 45 0.7 to 21   3 to 42   1 to 19 TaC 0.5 to 20   0.6 to 26 1 to 18  1 to 23  2 to 15   2 to 18

TABLE 28 Compositions that use Re, Ni-based superalloy (NBSA), and Co in a binder for binding WC + TiC or WC + TaC or WC + TiC + TaC. The range of Binder is from 0.5% Re + 99.5% superalloy to 99.5% Re + 0.5% Superalloy to 0.5% Re + 0.5% Superalloy + 99% Co. Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (Re + Co Re 0.015 to 39.8 0.02 to 54   0.02 to 34.8 0.027 to 48   0.025 to 29.9 0.035 to 43   NBSA) - NBSA 0.015 to 39.8 0.008 to 29   0.02 to 34.8 0.01 to 26   0.025 to 29.9 0.13 to 24   WC + TiC Co    0 to 39.6  0 to 32   0 to 34.7  0 to 29    0 to 29.8  0 to 26 WC  40 to 96 40 to 98   43 to 94.5 44 to 97  45 to 93 48 to 96 TiC  1 to 48 0.3 to 24  1.5 to 45  0.5 to 22   2 to 42 0.6 to 21  (Re + Co + Re 0.015 to 39.8 0.02 to 47   0.02 to 34.8 0.027 to 42   0.025 to 29.9 0.034 to 37   NBSA) - NBSA 0.015 to 39.8 0.008 to 26   0.02 to 34.8 0.01 to 22   0.025 to 29.9 0.13 to 18   WC + TaC Co    0 to 39.6  0 to 28   0 to 34.7  0 to 24    0 to 29.8  0 to 20 WC   50 to 96.5 45 to 98 55 to 95 50 to 97  60 to 93 55 to 95 TaC  0.5 to 22 0.5 to 24   1 to 20 0.9 to 21   2 to 18 1.8 to 19  (Re + Re 0.015 to 39.8 0.02 to 65   0.02 to 34.8 0.027 to 58   0.025 to 29.9 0.034 to 51   NBSA + NBSA 0.015 to 39.8 0.008 to 41   0.02 to 34.8 0.01 to 34   0.025 to 29.9 0.13 to 28   Co) - Co    0 to 39.6  0 to 44   0 to 34.7  0 to 37    0 to 29.8  0 to 31 WC + TiC + WC  35 to 85 35 to 93 40 to 80 41 to 88  40 to 75 47 to 83 TaC TiC  1 to 50 0.3 to 25   2 to 45 0.6 to 22   3 to 40 0.9 to 18  TaC  0.5 to 25 0.4 to 26   1 to 22 0.8 to 24   2 to 20 1.6 to 21 

TABLE 29 Additional Material Samples and Their Compositions Lot No. Re R95 Co U700 U720 Ni WC TiC TaC VC Mo₂C TiN Composition in Weight % P80 0 0 14.28 74.15 5.835 5.733 P81 0.736 0 13.904 73.84 5.811 5.709 P82 0.707 6.026 7.3694 74.31 5.847 5.744 P83 0.679 12.82 0 74.83 5.889 5.785 P84 1.45 5.903 7.1237 73.98 5.822 5.719 P85 3.06 5.532 6.7027 73.27 5.766 5.665 P86 1.45 5.903 7.1237 36.99 5.822 5.719 P87 1.063 4.126 5.4174 78.14 5.676 5.576 P88 1.861 7.57 9.1372 69.59 5.974 5.869 P89 1.368 5.572 6.7242 80.31 3.004 3.023 P99 0 0 5.5 15 29 10 9.5 20 P100 4.8 4.65 14.5 28.1 9.7 9.5 19.4 P101 4.8 4.65 14.5 28.1 9.7 9.5 19.4 P102 4.8 10 14.5 28.1 9.7 9.5 19.4 P103 9.6 20 11.25 21.65 7.5 7.1 14.9 P104 7.2 15 12.8 25 8.6 8.1 17.3 P105 15 7.5 13.6 26.35 9.05 8.9 18.1 P106 14.49 0 0 74.415 5.092 6.003 P107 15.101 0 0 66.875 7.076 10.95 P108 11.796 0.7485 0.437 75.727 5.182 6.109 P109 12.303 0.7807 0.456 68.105 7.206 11.15 P110 9.5724 1.4017 0.761 76.812 5.256 6.196 P111 9.9896 1.4628 0.794 69.124 7.314 11.32 P112 6.9929 2.1369 1.16 78.07 5.342 6.298 P113 14.131 4.3182 2.343 67.447 5.398 6.363 P114 21.418 6.545 3.552 56.602 5.454 6.43 P115 3.8745 3.0258 1.642 79.591 5.446 6.421 P116 7.988 6.2383 3.385 70.155 5.614 6.619 P117 12.363 9.6552 5.24 60.119 5.793 6.829 P118 1.8824 3.5833 1.961 80.561 5.513 6.499 P119 2.8849 5.4917 3.006 76.345 5.632 6.64 P120 5.0264 9.5681 5.237 67.339 5.888 6.941 P121 13.157 0.5708 0 75.078 5.138 6.057 P122 5.294 2.0672 0 81.057 5.316 6.266 Weight % P123 19.908 5.9798 1.976 60.41 5.382 6.344 P124 20.68 9.9386 2.736 54.464 5.59 6.59 P125 1.5492 3.0246 0.833 82.731 5.444 6.418 P126 8.4621 13.217 3.639 61.723 5.948 7.011 P127 12.191 13.964 3.844 61.702 3.808 4.49 P128 11.906 0.5166 0 86.99 0.604 P129 1.6752 2.0169 1.9524 93.77 0.599 P130 11.97 8.0334 8.085 71.33 0.6 P131 1.4372 3.8162 3.7765 90.39 0.596 P132 6.6223 1.3705 1.3191 90.1 0.605 P133 5.505 1.7196 1.6331 90.55 0.609 P134 11.43 5.0212 4.8443 78.11 0.613 P135 1.644 2.3344 2.571 79.98 3.151 10.32 P136 3.6545 5.1371 5.657 73.439 0 12.11 P137 4.4642 6.3916 7.039 69.776 0 12.33 P138 4.899 6.5757 7.241 69.279 1.435 10.57 P139 6.5381 7.902 8.702 64.651 1.459 10.75 P140 3.0601 5.5324 6.703 73.274 5.766 5.665 P141 2.9261 5.2902 6.409 71.233 3.308 10.83 P142 5.0649 6.1371 7.419 67.113 3.337 10.93 A 13.853 0.2847 0.314 74.887 5.125 5.538 B 2.7327 5.0305 0 81.358 5.488 5.391 C 3.0601 5.5324 6.703 73.274 5.766 5.665 D 1.8803 3.5793 1.988 81.637 5.507 5.41 E 7.7737 9.4819 0 71.578 5.633 5.534 P144 0.6786 12.821 0 74.827 5.889 5.785 P145 0.6437 5.663 0 80.041 3.194 10.46 P146 1.8837 5.3941 0 81.786 5.517 5.42 P147 2.3479 5.1953 0 81.552 5.501 5.404 P148 1.5479 8.462 0 76.038 3.264 10.69 P149 1.6376 15.347 0 68.255 3.453 11.31 J 25.75 2.5 14.5 24.1 8.5 8 16.65 K 11.671 0.4143 0.3935 0 0 86.92 0.605 L 2.6826 5.5683 0 0 0 91.32 0.43 M 3.5669 0 14.235 0 0 81.75 0.452 N 0 7.5039 0 0 0 92.06 0.44 O 12.515 0 0 0 0.2541 86.63 0.601 P 1.7969 0 0 6.9309 90.68 0.597 Q 0 0 0 7.4214 91.98 0.602 S 8.371 0 0 5.3814 85.67 0.579 T 1.6967 0 4.681 0 92.98 0.645 U 3.9002 0 0 3.8684 91.6 0.636 P150 0 0 14.847 84.68 0.469 P151 0 3.2554 11.851 84.38 0.51 P152 1.5219 3.225 11.153 83.59 0.505 P153 12.451 1.2899 4.6957 81.09 0.478 P154 2.6486 2.9933 7.6052 54.464 0.509 P155 0 0 11.55 82.731 0.414 P156 1.1019 3.5804 6.2338 61.723 0.671 P157 0 3.761 6.5607 86.24 0.675 P158 0 0 9.9898 88.04 0.512 P159 0.9437 3.0766 5.5161 88.41 0.502 P160 0 3.0946 5.9144 89 0.505 P161 0 0 8.7552 89.5 0.506 P162 2.967 5.6892 0.6379 0.654 89.817 0.2346 P163 0.581 8.1942 0.9297 0.8972 89.156 0.2413 P164 2.16 7.569 0.8669 0.8333 88.331 0.2391 P165 2.801 6.7279 1.976 2.026 86.226 0.2422 P166 2.797 8.3834 1.2603 1.2361 86.082 0.2418 P167 2.789 11.13 0 0 85.84 0.2411

The following TABLES 30-41 list exemplary cermet compositions with 3 exemplary composition ranges 1, 2, and 3 which may be used for different applications.

TABLE 30 Compositions that use Re as a binder for binding TiC + Mo₂C, or TiN + Mo₂C, or TiC + TiN + Mo₂C, or TiC + TiN + Mo₂C + WC + TaC + VC + Cr₂C₃ Composition Composition Composition Range 1 Range 2 Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % Re - Re 3 to 30 9.5 to 65   4 to 27 13 to 60  5 to 25 15 to 58  TiC + Mo₂C TiC 43 to 97  19 to 88  48 to 92  23 to 79  51 to 90  25 to 75  Mo₂C 0 to 27 0 to 38 0 to 26 0 to 36 0 to 24 0 to 33 Re - Re 3 to 30 9 to 63 4 to 27 12 to 58  5 to 25 15 to 56  TiN + Mo₂C TiN 43 to 97  21 to 89  48 to 92  25 to 81  51 to 90  27 to 76  Mo₂C 0 to 27 0 to 36 0 to 26 0 to 34 0 to 24 0 to 31 Re - Re 3 to 30 9 to 64 4 to 27 12 to 60  5 to 25 15 to 58  TiC + TiN + TiC 0.3 to 93.7 0.2 to 84   0.4 to 91.6 0.3 to 79   0.5 to 89.5 0.35 to 74   Mo₂C TiN 0.3 to 93.7 0.3 to 85   0.4 to 91.6 0.4 to 80   0.5 to 89.5 0.5 to 76   Mo₂C 0 to 27 0 to 36 0 to 26 0 to 34 0 to 24 0 to 31 Re — Re 3 to 30 6 to 65 4 to 27 9 to 61 5 to 25 11 to 65  TiC + TiN + TiC 0.3 to 93.5 0.1 to 83   0.4 to 91.3 0.2 to 78   0.5 to 89.1 0.3 to 74   Mo₂C + TiN 0.3 to 93.5 0.15 to 85   0.4 to 91.3 0.2 to 80   0.5 to 89.1 0.3 to 76   WC + TaC + Mo₂C 0 to 28 0 to 25 0 to 26 0 to 25 0 to 24 0 to 24 VC + Cr₂C₃ WC 0.1 to 20   0.15 to 39   0.15 to 15   0.25 to 32   0.2 to 12   0.35 to 28   TaC 0.1 to 15   0.15 to 30   0.15 to 12   0.25 to 25   0.2 to 10   0.3 to 22   VC 0 to 15 0 to 11 0 to 12 0 to 10 0 to 10 0 to 9  Cr₂C₃ 0 to 15 0 to 16 0 to 12 0 to 14 0 to 10 0 to 12

TABLE 31 Compositions that use Ni-based superalloy (NBSA) as a binder for binding TiC + Mo₂C, or TiN + Mo₂C, or TiC + TiN + Mo₂C, or TiC + TiN + Mo₂C + WC + TaC + VC + Cr₂C₃ Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % NBSA - NBSA 3 to 30 4 to 41 4 to 27 5 to 37 5 to 25 6 to 34 TiC + Mo₂C TiC 43 to 94  30 to 90  48 to 92  35 to 87  51 to 90  37 to 84  Mo₂C 3 to 27 4 to 40 4 to 26 6 to 39 5 to 24 8 to 36 NBSA - NBSA 3 to 30 4 to 38 4 to 27 5 to 34 5 to 25 6 to 32 TiN + Mo₂C TiN 43 to 94  32 to 91  48 to 92  37 to 88  51 to 90  40 to 85  Mo₂C 3 to 27 4 to 38 4 to 26 6 to 37 5 to 24 7 to 34 NBSA - NBSA 3 to 30 4 to 40 4 to 27 5 to 36 5 to 25 6 to 34 TiC + TiN + TiC 0.3 to 93.7 0.2 to 90   0.4 to 91.6 0.3 to 86   0.5 to 89.5 0.4 to 83   Mo₂C TiN 0.3 to 93.7 0.3 to 91   0.4 to 91.6 0.4 to 88   0.5 to 89.5 0.5 to 85   Mo₂C 3 to 27 4 to 38 4 to 26 6 to 37 5 to 24 8 to 34 NBSA - NBSA 3 to 30 2 to 40 4 to 27 4 to 36 5 to 25 5 to 34 TiC + TiN + TiC 0.3 to 93.3 0.15 to 90   0.4 to 91.3 0.2 to 86   0.5 to 89.3 0.3 to 83   Mo₂C + TiN 0.3 to 93.3 0.25 to 90   0.4 to 91.3 0.35 to 87   0.5 to 89.3 0.45 to 84   WC + TaC + Mo₂C 3 to 27 4 to 25 4 to 26 6 to 26 5 to 24   8 to 25.5 VC + Cr₂C₃ WC 0.1 to 20   0.25 to 42   0.15 to 15   0.4 to 34   0.2 to 12   0.5 to 29   TaC 0.1 to 15   0.25 to 36   0.15 to 12   0.4 to 30   0.2 to 10   0.5 to 26   VC 0 to 15 0 to 14 0 to 12 0 to 12 0 to 10 0 to 10 Cr₂C₃ 0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to 13

TABLE 32 Compositions that use Re and Ni-based superalloy (NBSA) in a binder for binding TiC + Mo₂C, or TiN + Mo₂C, or TiC + TiN + Mo₂C, or TiC + TiN + Mo₂C + WC + TaC + VC + Cr₂C₃ Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (Re + NBSA) - Re 0.03 to 29.7  0.1 to 64 0.04 to 26.73 0.13 to 60   0.05 to 24.75 0.16 to 57   TiC + TiN + NBSA 0.03 to 29.7 0.03 to 40 0.04 to 26.73 0.05 to 36   0.05 to 24.75 0.06 to 34   Mo₂C TiC  0 to 94   0 to 90 0 to 92 0 to 87 0 to 90 0 to 84 TiN  0 to 94   0 to 91 0 to 92 0 to 88 0 to 90 0 to 85 Mo₂C  3 to 27   3 to 38 4 to 26 4 to 37 5 to 24 5 to 34 (Re + NBSA) - Re 0.03 to 29.7 0.06 to 64 0.04 to 26.73 0.1 to 60   0.05 to 24.75 0.12 to 57   TiC + TiN + NBSA 0.03 to 29.7 0.02 to 40 0.04 to 26.73 0.03 to 36   0.05 to 24.75 0.04 to 34   Mo₂C + TiC  0.3 to 93.5 0.15 to 89 .40 to 91.3 0.2 to 86   0.5 to 89.1 0.3 to 83   WC + TaC + TiN  0.3 to 93.5 0.15 to 90 .40 to 91.3 0.2 to 87   0.5 to 89.1 0.3 to 84   VC + Cr₂C₃ Mo₂C  3 to 28   3 to 26 4 to 26 4 to 26 5 to 24   5 to 25.5 WC 0.1 to 20  0.15 to 42 0.15 to 15   0.25 to 35   0.2 to 12   0.35 to 29   TaC 0.1 to 15  0.15 to 33 0.15 to 12   0.25 to 28   0.2 to 10   0.3 to 24   VC  0 to 15   0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr₂C₃  0 to 15   0 to 18 0 to 12 0 to 15 0 to 10 0 to 13

TABLE 33 Compositions that use Re and Ni in a binder for binding TiC + Mo₂C, or TiN + Mo₂C, or TiC + TiN + Mo₂C, or TiC + TiN + Mo₂C + WC + TaC + VC + Cr₂C₃ Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (Re + Ni) - Re 0.03 to 29.7 0.1 to 64   0.04 to 26.73 0.13 to 60   0.05 to 24.75 0.16 to 57   TiC + TiN + Ni 0.03 to 29.7 0.04 to 42   0.04 to 26.73 0.05 to 38   0.05 to 24.75 0.06 to 36   Mo₂C TiC  0 to 94 0 to 90 0 to 92 0 to 87 0 to 90 0 to 83 TiN  0 to 94 0 to 91 0 to 92 0 to 88 0 to 90 0 to 85 Mo₂C  3 to 27 3 to 38 4 to 26 4 to 37 5 to 24 5 to 34 (Re + Ni) - Re 0.03 to 29.7 0.06 to 64   0.04 to 26.73 0.1 to 60   0.05 to 24.75 0.12 to 57   TiC + TiN + Ni 0.03 to 29.7 0.03 to 42   0.04 to 26.73 0.04 to 39   0.05 to 24.75 0.05 to 36   Mo₂C + TiC  0.3 to 93.5 0.15 to 89   .40 to 91.3 0.2 to 85   0.5 to 89.1 0.3 to 82   WC + TaC + TiN  0.3 to 93.5 0.15 to 90   .40 to 91.3 0.2 to 87   0.5 to 89.1 0.3 to 83   VC + Cr₂C₃ Mo₂C  3 to 28 3 to 26 4 to 26 4 to 26 5 to 24   5 to 25.5 WC 0.1 to 20  0.15 to 42   0.15 to 15   0.25 to 35   0.2 to 12   0.35 to 29   TaC 0.1 to 15  0.15 to 33   0.15 to 12   0.25 to 28   0.2 to 10   0.3 to 24   VC  0 to 15 0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr₂C₃  0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to 13

TABLE 34 Compositions that use Re and Co in a binder for binding TiC + Mo₂C, or TiN + Mo₂C, or TiC + TiN + Mo₂C, or TiC + TiN + Mo₂C + WC + TaC + VC + Cr₂C₃ Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % Re + Co - Re 0.03 to 29.7 0.1 to 64   0.04 to 26.73 0.13 to 60   0.05 to 24.75 0.16 to 57   TiC + TiN + Co 0.03 to 29.7 0.04 to 43   0.04 to 26.73 0.05 to 39   0.05 to 24.75 0.06 to 36   Mo₂C TiC  0 to 94 0 to 90 0 to 92 0 to 87 0 to 90 0 to 83 TiN  0 to 94 0 to 91 0 to 92 0 to 88 0 to 90 0 to 85 Mo₂C  3 to 27 3 to 38 4 to 26 4 to 37 5 to 24 5 to 34 Re + Co - Re 0.03 to 29.7 0.06 to 64   0.04 to 26.73 0.1 to 60   0.05 to 24.75 0.12 to 57   TiC + TiN + Co 0.03 to 29.7 0.03 to 43   0.04 to 26.73 0.04 to 39   0.05 to 24.75 0.05 to 36   Mo₂C + TiC  0.3 to 93.5 0.15 to 89   .40 to 91.3 0.2 to 85   0.5 to 89.1 0.3 to 82   WC + TaC + TiN  0.3 to 93.5 0.15 to 90   .40 to 91.3 0.2 to 87   0.5 to 89.1 0.3 to 83   VC + Cr₂C₃ Mo₂C  3 to 28 3 to 26 4 to 26 4 to 26 5 to 24   5 to 25.5 WC 0.1 to 20  0.15 to 42   0.15 to 15   0.25 to 34   0.2 to 12   0.35 to 29   TaC 0.1 to 15  0.15 to 32   0.15 to 12   0.25 to 27   0.2 to 10   0.3 to 24   VC  0 to 15 0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr₂C₃  0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to 13

TABLE 35 Compositions that use Ni-based superalloy (NBSA) and Co in a binder for binding TiC + Mo₂C, or TiN + Mo₂C, or TiC + TiN + Mo₂C, or TiC + TiN + Mo₂C + WC + TaC + VC + Cr₂C₃ Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (NBSA + Co) - NBSA 0.03 to 29.7 0.04 to 40   0.04 to 26.73 0.05 to 37   0.05 to 24.75 0.06 to 34   TiC + TiN + Co 0.03 to 29.7 0.04 to 43   0.04 to 26.73 0.06 to 39   0.05 to 24.75 0.07 to 37   Mo₂C TiC  0 to 94 0 to 90 0 to 92 0 to 87 0 to 90 0 to 84 TiN  0 to 94 0 to 91 0 to 92 0 to 88 0 to 90 0 to 86 Mo₂C  3 to 27 4 to 38 4 to 26 6 to 37 5 to 24 7 to 34 (NBSA + Co) - NBSA 0.03 to 29.7 0.02 to 40   0.04 to 26.73 0.03 to 36   0.05 to 24.75 0.05 to 34   TiC + TiN + Co 0.03 to 29.7 0.03 to 43   0.04 to 26.73 0.04 to 39   0.05 to 24.75 0.05 to 36   Mo₂C + TiC  0.3 to 93.5 0.15 to 89   .40 to 91.3 0.2 to 86   0.5 to 89.1 0.3 to 83   WC + TaC + TiN  0.3 to 93.5 0.25 to 90   .40 to 91.3 0.35 to 87   0.5 to 89.1 0.45 to 84   VC + Cr₂C₃ Mo₂C  3 to 28 4 to 26 4 to 26 6 to 26 5 to 24   7 to 25.5 WC 0.1 to 20  0.25 to 42   0.15 to 15   0.38 to 35   0.2 to 12   0.5 to 29   TaC 0.1 to 15  0.23 to 33   0.15 to 12   0.35 to 28   0.2 to 10   0.47 to 24   VC  0 to 15 0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr₂C₃  0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to 13

TABLE 36 Compositions that use Ni-based superalloy (NBSA) and Ni in a binder for binding TiC + Mo₂C, or TiN + Mo₂C, or TiC + TiN + Mo₂C, or TiC + TiN + Mo₂C + WC + TaC + VC + Cr₂C₃ Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (NBSA + Ni) - NBSA 0.03 to 29.7 0.04 to 40   0.04 to 26.73 0.05 to 37   0.05 to 24.75 0.06 to 34   TiC + TiN + Ni 0.03 to 29.7 0.04 to 43   0.04 to 26.73 0.055 to 39    0.05 to 24.75 0.07 to 36   Mo₂C TiC  0 to 94 0 to 90 0 to 92 0 to 88 0 to 90 0 to 85 TiN  0 to 94 0 to 91 0 to 92 0 to 89 0 to 90 0 to 86 Mo₂C  3 to 27 4 to 38 4 to 26 6 to 37 5 to 24 7 to 34 (NBSA + Ni) - NBSA 0.03 to 29.7 0.02 to 40   0.04 to 26.73 0.035 to 36    0.05 to 24.75 0.05 to 34   TiC + TiN + Ni 0.03 to 29.7 0.03 to 43   0.04 to 26.73 0.04 to 39   0.05 to 24.75 0.05 to 36   Mo₂C + TiC  0.3 to 93.5 0.15 to 89   .40 to 91.3 0.2 to 86   0.5 to 89.1 0.3 to 83   WC + TaC + TiN  0.3 to 93.5 0.25 to 90   .40 to 91.3 0.35 to 87   0.5 to 89.1 0.45 to 84   VC + Cr₂C₃ Mo₂C  3 to 28 4 to 26 4 to 26 6 to 26 5 to 24   7 to 25.5 WC 0.1 to 20  0.25 to 42   0.15 to 15   0.38 to 35   0.2 to 12   0.5 to 29   TaC 0.1 to 15  0.23 to 33   0.15 to 12   0.35 to 28   0.2 to 10   0.47 to 24   VC  0 to 15 0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr₂C₃  0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to 13

TABLE 37 Compositions that use Re, Co, and Ni-based superalloy (NBSA) in a binder for binding TiC and Mo₂C, or TiN and Mo₂C, or TiC, TiN, and Mo₂C, or TiC, TiN, Mo₂C, WC, TaC, VC, and Cr₂C₃ Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (Re + NBSA + Re 0.03 to 29.4 0.1 to 64   0.04 to 26.46 0.13 to 60   0.05 to 24.5 0.16 to 57   Co) - NBSA 0.03 to 29.4 0.035 to 40    0.04 to 26.46 0.045 to 36    0.05 to 24.5 0.055 to 34    TiC + TiN + Co 0.03 to 29.4 0.04 to 42   0.04 to 26.46 0.05 to 39   0.05 to 24.5 0.06 to 36   Mo₂C TiC  0 to 94 0 to 90 0 to 92 0 to 88  0 to 90 0 to 84 TiN  0 to 94 0 to 91 0 to 92 0 to 88  0 to 90 0 to 85 Mo₂C  3 to 27 3 to 38 4 to 26 4 to 37  5 to 24 5 to 34 (Re + NBSA + Re 0.03 to 29.4 0.06 to 63   0.04 to 26.46 0.1 to 60   0.05 to 24.5 0.13 to 57   Co) - NBSA 0.03 to 29.4 0.02 to 39   0.04 to 26.46 0.03 to 36   0.05 to 24.5 0.04 to 33   TiC + TiN + Co 0.03 to 29.4 0.03 to 42   0.04 to 26.46 0.04 to 39   0.05 to 24.5 0.05 to 36   Mo₂C + TiC  0.3 to 93.5 0.15 to 89   0.4 to 91.3 0.2 to 86    0.5 to 89.1 0.3 to 83   WC + TaC + TiN  0.3 to 93.5 0.15 to 90   0.4 to 91.3 0.2 to 87    0.5 to 89.1 0.3 to 84   VC + Cr₂C₃ Mo₂C  3 to 28 3 to 26 4 to 26 4 to 26  5 to 24   5 to 25.5 WC 0.1 to 20  0.15 to 42   0.15 to 15   0.25 to 35   0.2 to 12  0.35 to 29   TaC 0.1 to 15  0.15 to 33   0.15 to 12   0.25 to 28   0.2 to 10  0.3 to 24   VC  0 to 15 0 to 16 0 to 12 0 to 13  0 to 10 0 to 11 Cr₂C₃  0 to 15 0 to 18 0 to 12 0 to 15  0 to 10 0 to 13

TABLE 38 Compositions that use Re, Ni, and Ni-based superalloy (NBSA) in a binder for binding TiC + Mo₂C, or TiN + Mo₂C, or TiC + TiN + Mo₂C, or TiC + TiN + Mo₂C + WC + TaC + VC + Cr₂C₃ Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (Re + NBSA + Re 0.03 to 29.4 0.1 to 63   0.04 to 26.46 0.13 to 60   0.05 to 24.5 0.16 to 57   Ni) - NBSA 0.03 to 29.4 0.035 to 40    0.04 to 26.46 0.045 to 36    0.05 to 24.5 0.055 to 33    TiC + TiN + Ni 0.03 to 29.4 0.04 to 42   0.04 to 26.46 0.05 to 38   0.05 to 24.5 0.06 to 36   Mo₂C TiC  0 to 94 0 to 90 0 to 92 0 to 87  0 to 90 0 to 84 TiN  0 to 94 0 to 91 0 to 92 0 to 88  0 to 90 0 to 85 Mo₂C  3 to 27 3 to 38 4 to 26 4 to 37  5 to 24 5 to 34 (Re + NBSA + Re 0.03 to 29.4 0.06 to 63   0.04 to 26.46 0.1 to 60   0.05 to 24.5 0.13 to 57   Ni) - NBSA 0.03 to 29.4 0.02 to 39   0.04 to 26.46 0.03 to 36   0.05 to 24.5 0.04 to 33   TiC + TiN + Ni 0.03 to 29.4 0.03 to 42   0.04 to 26.46 0.04 to 38   0.05 to 24.5 0.05 to 36   Mo₂C + TiC  0.3 to 93.5 0.15 to 89   0.4 to 91.3 0.2 to 86    0.5 to 89.1 0.3 to 83   WC + TaC + TiN  0.3 to 93.5 0.15 to 90   0.4 to 91.3 0.2 to 87    0.5 to 89.1 0.3 to 84   VC + Cr₂C₃ Mo₂C  3 to 28 3 to 26 4 to 26 4 to 26  5 to 24   5 to 25.5 WC 0.1 to 20  0.15 to 42   0.15 to 15   0.25 to 35   0.2 to 12  0.35 to 29   TaC 0.1 to 15  0.15 to 33   0.15 to 12   0.25 to 28   0.2 to 10  0.3 to 24   VC  0 to 15 0 to 16 0 to 12 0 to 13  0 to 10 0 to 11 Cr₂C₃  0 to 15 0 to 18 0 to 12 0 to 15  0 to 10 0 to 13

TABLE 39 Compositions that use Re, Ni, and Co in a binder for binding TiC + Mo₂C, or TiN + Mo₂C, or TiC + TiN + Mo₂C, or TiC + TiN + Mo₂C + WC + TaC + VC + Cr₂C₃ Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (Re + Ni + Re 0.03 to 29.4 0.1 to 63   0.04 to 26.46 0.13 to 60   0.05 to 24.5 0.16 to 57   Co) - Ni 0.03 to 29.4 0.04 to 42   0.04 to 26.46 0.05 to 38   0.05 to 24.5 0.06 to 36   TiC + TiN + Co 0.03 to 29.4 0.04 to 42   0.04 to 26.46 0.05 to 39   0.05 to 24.5 0.06 to 36   Mo₂C TiC  0 to 94 0 to 90 0 to 92 0 to 87  0 to 90 0 to 83 TiN  0 to 94 0 to 91 0 to 92 0 to 88  0 to 90 0 to 85 Mo₂C  3 to 27 3 to 38 4 to 26 4 to 37  5 to 24 5 to 34 (Re + Ni + Re 0.03 to 29.4 0.06 to 63   0.04 to 26.46 0.1 to 60   0.05 to 24.5 0.13 to 57   Co) - Ni 0.03 to 29.4 0.025 to 42    0.04 to 26.46 0.04 to 38   0.05 to 24.5 0.05 to 36   TiC + TiN + Co 0.03 to 29.4 0.03 to 42   0.04 to 26.46 0.04 to 39   0.05 to 24.5 0.05 to 36   Mo₂C + TiC  0.3 to 93.5 0.15 to 89   0.4 to 91.3 0.2 to 85    0.5 to 89.1 0.3 to 82   WC + TaC + TiN  0.3 to 93.5 0.15 to 90   0.4 to 91.3 0.2 to 87    0.5 to 89.1 0.3 to 83   VC + Cr₂C₃ Mo₂C  3 to 28 3 to 26 4 to 26 4 to 26  5 to 24   5 to 25.5 WC 0.1 to 20  0.15 to 42   0.15 to 15   0.25 to 35   0.2 to 12  0.35 to 29   TaC 0.1 to 15  0.15 to 33   0.15 to 12   0.25 to 28   0.2 to 10  0.3 to 24   VC  0 to 15 0 to 16 0 to 12 0 to 13  0 to 10 0 to 11 Cr₂C₃  0 to 15 0 to 18 0 to 12 0 to 15  0 to 10 0 to 13

TABLE 40 Compositions that use Co, Ni, and Ni-based superalloy (NBSA) in a binder for binding TiC + Mo₂C, or TiN + Mo₂C, or TiC + TiN + Mo₂C, or TiC + TiN + Mo₂C + WC + TaC + VC + Cr₂C₃ Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (NBSA + Ni + NBSA 0.03 to 29.4 0.04 to 40   0.04 to 26.46 0.5 to 36   0.05 to 24.5 0.06 to 34   Co) - Ni 0.03 to 29.4 0.04 to 42   0.04 to 26.46 0.055 to 39    0.05 to 24.5 0.07 to 37   TiC + TiN + Co 0.03 to 29.4 0.04 to 43   0.04 to 26.46 0.055 to 39    0.05 to 24.5 0.07 to 36   Mo₂C TiC  0 to 94 0 to 90 0 to 92 0 to 87  0 to 90 0 to 84 TiN  0 to 94 0 to 91 0 to 92 0 to 88  0 to 90 0 to 85 Mo₂C  3 to 27 4 to 38 4 to 26 5 to 37  5 to 24 7 to 34 (NBSA + Ni + NBSA 0.03 to 29.4 0.025 to 40    0.04 to 26.46 0.035 to 36    0.05 to 24.5 0.05 to 33   Co) - Ni 0.03 to 29.4 0.025 to 42    0.04 to 26.46 0.04 to 38   0.05 to 24.5 0.05 to 36   TiC + TiN + Co 0.03 to 29.4 0.03 to 42   0.04 to 26.46 0.04 to 39   0.05 to 24.5 0.05 to 36   Mo₂C + TiC  0.3 to 93.5 0.15 to 89   0.4 to 91.3 0.2 to 86    0.5 to 89.1 0.3 to 83   WC + TaC + TiN  0.3 to 93.5 0.25 to 90   0.4 to 91.3 0.35 to 87    0.5 to 89.1 0.45 to 84   VC + Cr₂C₃ Mo₂C  3 to 28 4 to 26 4 to 26 6 to 26  5 to 24   7 to 25.5 WC 0.1 to 20  0.25 to 42   0.15 to 15   0.35 to 35   0.2 to 12  0.5 to 29   TaC 0.1 to 15  0.25 to 33   0.15 to 12   0.35 to 28   0.2 to 10  0.45 to 24   VC  0 to 15 0 to 16 0 to 12 0 to 13  0 to 10 0 to 11 Cr₂C₃  0 to 15 0 to 18 0 to 12 0 to 15  0 to 10 0 to 13

TABLE 41 Compositions that use Re, Ni, Co, and Ni-based superalloy (NBSA) in a binder for binding TiC + Mo₂C, or TiN + Mo₂C, or TiC + TiN + Mo₂C, or TiC + TiN + Mo₂C + WC + TaC + VC + Cr₂C₃ Composition Range 1 Composition Range 2 Composition Range 3 Material Volume % Weight % Volume % Weight % Volume % Weight % (Re + NBSA + Ni + Re 0.03 to 29.1 0.1 to 63   0.04 to 26.19 0.13 to 59   0.05 to 24.25 0.16 to 57   Co) - NBSA 0.03 to 29.1 0.035 to 39    0.04 to 26.19 0.45 to 36   0.05 to 24.25 0.055 to 33    TiC + TiN + Ni 0.03 to 29.1 0.04 to 42   0.04 to 26.19 0.05 to 38   0.05 to 24.25 0.06 to 36   Mo₂C Co 0.03 to 29.1 0.04 to 42   0.04 to 26.19 0.5 to 38   0.05 to 24.25 0.06 to 36   TiC  0 to 94 0 to 90 0 to 92 0 to 87 0 to 90 0 to 84 TiN  0 to 94 0 to 91 0 to 92 0 to 88 0 to 90 0 to 85 Mo₂C  3 to 27 3 to 38 4 to 26 4 to 37 5 to 24 5 to 34 (Re + NBSA + Ni + Re 0.03 to 29.1 0.06 to 63   0.04 to 26.19 0.1 to 59   0.05 to 24.25 0.12 to 56   Co) - NBSA 0.03 to 29.1 0.02 to 39   0.04 to 26.19 0.03 to 35   0.05 to 24.25 0.04 to 33   TiC + TiN + Ni 0.03 to 29.1 0.025 to 42   0.04 to 26.19 0.035 to 38    0.05 to 24.25 0.05 to 35   Mo₂C + Co 0.03 to 29.1 0.025 to 42    0.04 to 26.19 0.03 to 38   0.05 to 24.25 0.05 to 36   WC + TaC + TiC  0.3 to 93.5 0.15 to 89   0.4 to 91.3 0.2 to 86   0.5 to 89.1 0.3 to 83   VC + Cr₂C₃ TiN  0.3 to 93.5 0.15 to 90   0.4 to 91.3 0.2 to 87   0.5 to 89.1 0.3 to 84   Mo₂C  3 to 28 3 to 26 4 to 26 4 to 26 5 to 24   5 to 25.5 WC 0.1 to 20  0.15 to 42   0.15 to 15   0.25 to 35   0.2 to 12   0.3 to 29   TaC 0.1 to 15  0.15 to 33   0.15 to 12   0.2 to 28   0.2 to 10   0.3 to 24   VC  0 to 15 0 to 16 0 to 12 0 to 13 0 to 10 0 to 11 Cr₂C₃  0 to 15 0 to 18 0 to 12 0 to 15 0 to 10 0 to 13

The following TABLES 42-51 list additional examples of various compositions with 3 exemplary composition ranges 1, 2, and 3 which may be used for different applications. Similar to some compositions described above, some compositions in TABLES 42-51 may be particularly useful for applications at high temperatures as indicated in the last row under “estimated melting points.”

As described above, binder matrix materials with rhenium, a nickel-based superalloy or a combination of both can enhance material performance at high temperatures. Tungsten is typically used as a constituent element in various hard particles such as carbides, nitrides, carbonitrides, borides, and silicides. When used as a binder matrix material, either alone or in combination with other metals, tungsten can significantly raise the melting point of the final hardmetal materials to the range of about 2500 to about 3500° C. Hence, hardmetals using W-based binder matrix materials can be used in applications at high temperatures that may not be possible with other materials. Notably, certain compositions that use a binder matrix based on tungsten (W) shown in TABLES 43-48 show expected high melting points around 3500° C.

For the compositions made of nitrides bound by rhenium and cobalt in TABLE 47, each nitride may be substituted by a combination of a nitride and carbide as the hard particle material. A material under this design includes hard particles comprising at least one nitride from nitrides of IVB and VB columns in the periodic table and one carbide from carbides of IVB, VB and VIB columns in the periodic table, and a binder matrix that binds the hard particles and comprises rhenium and cobalt.

TABLE 42 Re bound a Boride from Borides of IVb, Vb, & VIb or a Silicide from Silicides of IVb, Vb & VIb Composition Composition Composition Estimated Range 1 Range 2 Range 3 Melting Volume % Weight % Volume % Weight % Volume % Weight % Point, ° C. Re Re  3 to 40 12.5 to 76    4 to 35 16 to 71  5 to 30 20 to 67 2700 to 3000 Bound TiB₂ 60 to 97   24 to 87.5 65 to 96 29 to 84 70 to 95 33 to 80 TiB₂ Re Re  3 to 40 9.5 to 70   4 to 35 12.5 to 65    5 to 30 15 to 60 2800 to 3000 Bound ZrB₂ 60 to 97   30 to 90.5 65 to 96   35 to 87.5 70 to 95 40 to 85 ZrB₂ Re Re  3 to 40  5.5 to 55.5  4 to 35  7 to 50  5 to 30   9 to 44.5 3000 to 3200 Bound HfB₂ 60 to 97 44.5 to 94.5 65 to 96 50 to 93 70 to 95 55.5 to 91   HfB₂ Re Re  3 to 40 11 to 73  4 to 35 14.5 to 69    5 to 30 18 to 64 2000 to 2500 Bound VB₂ 60 to 97 27 to 89 65 to 96   31 to 85.5 70 to 95 36 to 82 VB₂ Re Re  3 to 40  8 to 66  4 to 35 11 to 61  5 to 30   13 to 55.5 2800 to 3100 Bound NbB₂ 60 to 97 34 to 92 65 to 96 39 to 89 70 to 95 44.5 to 87   NbB₂ Re Re  3 to 40  5 to 53  4 to 35 6.5 to 47   5 to 30  8 to 42 3000 to 3200 Bound TaB₂ 60 to 97 47 to 95 65 to 96   53 to 93.5 70 to 95 58 to 92 TaB₂ Re Re  3 to 40  9.5 to 69.5  4 to 35 12.5 to 65   5 to 30 15 to 60 1800 to 2200 Bound Cr₃B₂ 60 to 97 30.5 to 90.5 65 to 96   35 to 87.5 70 to 95 40 to 85 Cr₃B₂ Re Re  3 to 40 7.5 to 64   4 to 35 10 to 59  5 to 30 12.5 to 54   2000 to 2400 Bound MoB₂ 60 to 97   36 to 92.5 65 to 96 41 to 90 70 to 95   46 to 87.5 MoB₂ Re Re  3 to 40  4 to 47  4 to 35  5 to 41  5 to 30 6.5 to 36  2700 to 3000 Bound WB 60 to 97 53 to 96 65 to 96 59 to 95 70 to 95   64 to 93.5 WB Re Re  3 to 40  4 to 47  4 to 35  5 to 41  5 to 30 6.5 to 36  2600 to 2900 Bound W₂B 60 to 97 53 to 96 65 to 96 59 to 95 70 to 95   64 to 93.5 W₂B Re Re  3 to 40 13 to 77  4 to 35 17 to 72  5 to 30 20 to 68 2000 to 2400 Bound Ti₅Si₃ 60 to 97 23 to 87 65 to 96 28 to 83 70 to 95 32 to 80 Ti₅Si₃ Re Re  3 to 40 10 to 72  4 to 35 14 to 67  5 to 30 17 to 62 2100 to 2500 Bound Zr₆Si₅ 60 to 97 28 to 90 65 to 96 33 to 86 70 to 95 38 to 83 Zr₆Si₅ Re Re  3 to 40  9 to 69  4 to 35 12 to 64  5 to 30 15 to 59 1800 to 2200 Bound NbSi₂ 60 to 97 31 to 91 65 to 96 36 to 88 70 to 95 41 to 85 NbSi₂ Re Re  3 to 40  7 to 62  4 to 35  9 to 57  5 to 30 12 to 51 2200 to 2600 Bound TaSi₂ 60 to 97 38 to 93 65 to 96 43 to 91 70 to 95 49 to 88 TaSi₂ Re Re  3 to 40  9 to 69  4 to 35 12 to 64  5 to 30 15 to 59 1800 to 2200 Bound MoSi₂ 60 to 97 31 to 91 65 to 96 36 to 88 70 to 95 41 to 85 MoSi₂ Re Re  3 to 40  6 to 60  4 to 35  9 to 55  5 to 30 11 to 49 1800 to 2200 Bound WSi₂ 60 to 97 40 to 94 65 to 96 45 to 91 70 to 95 51 to 89 WSi₂

TABLE 43 W bound a carbide from carbides of IVb, Vb, & VIb or a nitride from nitrides of IVb & Vb. Composition Composition Composition Estimated Range 1 Range 2 Range 3 Melting Volume % Weight % Volume % Weight % Volume % Weight % Point, ° C. W W  3 to 40 11 to 72  4 to 35 25.02 to 70    5 to 30 25.02 to 65   3000 to 3300 Bound TiC 60 to 97 28 to 89 65 to 96   30 to 74.98 70 to 95   35 to 74.98 TiC W W  3 to 40  8 to 66  4 to 35 11 to 61  5 to 30 13 to 56 3200 to 3500 Bound ZrC 60 to 97 34 to 92 65 to 96 39 to 89 70 to 95 44 to 87 ZrC W W  3 to 40  4 to 50  4 to 35  6 to 45  5 to 30  7 to 40 3300 to 3500 Bound HfC 60 to 97 50 to 96 65 to 96 55 to 64 70 to 95 60 to 93 HfC W W  3 to 40 10 to 70  4 to 35 13 to 65  5 to 30 16 to 60 2700 to 3300 Bound VC 60 to 97 30 to 90 65 to 96 35 to 87 70 to 95 40 to 84 VC W W  3 to 40  7 to 62  4 to 35  9 to 57  5 to 30 11 to 51 3000 to 3500 Bound NbC 60 to 97 38 to 93 65 to 96 43 to 91 70 to 95 49 to 89 NbC W W  3 to 40  4 to 47  4 to 35  5 to 42  5 to 30  7 to 36 3300 to 3500 Bound TaC 60 to 97 53 to 96 65 to 96 58 to 95 70 to 95 64 to 93 TaC W W  3 to 40  8 to 66  4 to 35 11 to 61  5 to 30 13 to 55 1700 to 2100 Bound Cr₂C₃ 60 to 97 34 to 92 65 to 96 39 to 89 70 to 95 45 to 87 Cr₂C₃ W W  3 to 40  6 to 59  4 to 35  8 to 53  5 to 30 10 to 48 2400 to 2600 Bound Mo₂C 60 to 97 41 to 94 65 to 96 47 to 93 70 to 95 52 to 90 Mo₂C W W  3 to 40  4 to 45  4 to 35  5 to 40  5 to 30  6 to 35 2800 to 3000 Bound WC 60 to 97 55 to 96 65 to 96 60 to 95 70 to 95 65 to 94 WC W W  3 to 40 11 to 72  4 to 35 14 to 68  5 to 30 16 to 60 2800 to 3300 Bound TiN 60 to 97 28 to 89 65 to 96 32 to 86 70 to 95 40 to 84 TiN W W  3 to 40  8 to 64  4 to 35 10 to 59  5 to 30 12 to 53 2900 to 3300 Bound ZrN 60 to 97 36 to 92 65 to 96 41 to 90 70 to 95 47 to 88 ZrN W W  3 to 40  4 to 48  4 to 35  6 to 43  5 to 30  7 to 37 3200 to 3500 Bound HfN 60 to 97 52 to 96 65 to 96 57 to 94 70 to 95 63 to 93 HfN W W  3 to 40  9 to 68  4 to 35 12 to 63  5 to 30 15 to 58 2000 to 2400 Bound VN 60 to 97 32 to 91 65 to 96 37 to 88 70 to 95 42 to 85 VN W W  3 to 40  8 to 64  4 to 35 10 to 59  5 to 30 12 to 53 2200 to 2600 Bound NbN 60 to 97 36 to 92 65 to 96 41 to 90 70 to 95 47 to 88 NbN W W  3 to 40  4 to 47  4 to 35  5 to 42  5 to 30  7 to 37 3000 to 3500 Bound TaN 60 to 97 53 to 96 65 to 96 58 to 95 70 to 95 63 to 93 TaN

TABLE 44 W bound a Boride from Borides of IVb, Vb, & VIb or a Silicide from Silicides of IVb, Vb & Vib Composition Composition Composition Estimated Range 1 Range 2 Range 3 Melting Volume % Weight % Volume % Weight % Volume % Weight % Point, ° C. W W  3 to 40 12 to 74  4 to 35 15 to 70  5 to 30 18 to 65 2700 to 3000 Bound TiB₂ 60 to 97 26 to 88 65 to 96 30 to 85 70 to 95 35 to 82 TiB₂ W W  3 to 40  9 to 68  4 to 35 12 to 63  5 to 30 14 to 58 2800 to 3000 Bound ZrB₂ 60 to 97 32 to 91 65 to 96 37 to 88 70 to 95 42 to 86 ZrB₂ W W  3 to 40  5 to 54  4 to 35  7 to 48  5 to 30  8 to 42 3000 to 3400 Bound HfB₂ 60 to 97 46 to 95 65 to 96 52 to 93 70 to 95 58 to 92 HfB₂ W W  3 to 40 10 to 72  4 to 35 14 to 67  5 to 30 17 to 62 2000 to 2500 Bound VB₂ 60 to 97 28 to 90 65 to 96 33 to 86 70 to 95 38 to 83 VB₂ W W  3 to 40  8 to 64  4 to 35 10 to 59  5 to 30 12 to 53 2900 to 3400 Bound NbB₂ 60 to 97 36 to 92 65 to 96 41 to 90 70 to 95 47 to 88 NbB₂ W W  3 to 40  5 to 51  4 to 35 6 to 45  5 to 30  7 to 40 3100 to 3400 Bound TaB₂ 60 to 97 49 to 95 65 to 96 55 to 94 70 to 95 60 to 93 TaB₂ W W  3 to 40  9 to 68  4 to 35 12 to 63  5 to 30 14 to 58 1800 to 2200 Bound Cr₃B₂ 60 to 97 32 to 91 65 to 96 37 to 88 70 to 95 42 to 86 Cr₃B₂ W W  3 to 40  7 to 62  4 to 35  9 to 57  5 to 30 12 to 52 2000 to 2400 Bound MoB₂ 60 to 97 38 to 93 65 to 96 43 to 91 70 to 95 48 to 88 MoB₂ W W  3 to 40  4 to 45  4 to 35  5 to 39  5 to 30  6 to 34 2700 to 3000 Bound WB 60 to 97 55 to 96 65 to 96 61 to 95 70 to 95 66 to 94 WB W W  3 to 40  3 to 44  4 to 35  5 to 38  5 to 30  6 to 33 2600 to 2900 Bound W₂B 60 to 97 56 to 97 65 to 96 62 to 95 70 to 95 67 to 94 W₂B W W  3 to 40 12 to 75  4 to 35 16 to 71  5 to 30 19 to 66 2000 to 2400 Bound Ti₅Si₃ 60 to 97 25 to 88 65 to 96 29 to 84 70 to 95 34 to 81 Ti₅Si₃ W W  3 to 40 10 to 70  4 to 35 13 to 65  5 to 30 16 to 60 2100 to 2500 Bound Zr₆Si₅ 60 to 97 30 to 90 65 to 96 35 to 87 70 to 95 40 to 84 Zr₆Si₅ W W  3 to 40  9 to 67  4 to 35 11 to 62  5 to 30 14 to 57 1800 to 2200 Bound NbSi₂ 60 to 97 33 to 91 65 to 96 38 to 89 70 to 95 43 to 86 NbSi₂ W W  3 to 40  7 to 60  4 to 35  9 to 55  5 to 30 11 to 49 2200 to 2600 Bound TaSi₂ 60 to 97 40 to 93 65 to 96 45 to 91 70 to 95 51 to 89 TaSi₂ W W  3 to 40  9 to 67  4 to 35 11 to 62  5 to 30 14 to 57 1800 to 2200 Bound MoSi₂ 60 to 97 31 to 91 65 to 96 38 to 89 70 to 95 43 to 86 MoSi₂ W W  3 to 40  6 to 58  4 to 35  8 to 53  5 to 30 10 to 47 1800 to 2200 Bound WSi₂ 60 to 97 42 to 94 65 to 96 47 to 92 70 to 95 43 to 90 WSi₂

TABLE 45 Re and W (Re + W) bound a carbide from carbides of IVb, Vb, & VIb or a nitride from nitrides of IVb & Vb. The range of Binder is from 1% Re + 99% W to 99% Re + 1% W. Composition Composition Composition Estimated Range 1 Range 2 Range 3 Melting Volume % Weight % Volume % Weight % Volume % Weight % Point, ° C. Re + W Re 0.03 to 39.6 0.12 to 73   0.04 to 34.7 0.15 to 69   0.05 to 29.7 0.19 to 64   2900 to 3300 Bound W 0.03 to 39.6 0.1 to 72  0.04 to 34.7 0.14 to 67   0.05 to 29.7 0.17 to 62   TiC TiC 60 to 97 26 to 89 65 to 96 30 to 86 70 to 95 35 to 83 Re + W Re 0.03 to 39.6 0.09 to 67   0.04 to 34.7 0.12 to 63   0.05 to 29.7 0.15 to 57   3000 to 3400 Bound W 0.03 to 39.6 0.08 to 66   0.04 to 34.7 0.11 to 61   0.05 to 29.7 0.13 to 55   ZrC ZrC 60 to 97 32 to 92 65 to 96 37 to 89 70 to 95 42 to 87 Re + W Re 0.03 to 39.6 0.05 to 52   0.04 to 34.7 0.07 to 47   0.05 to 29.7 0.08 to 41   3100 to 3500 Bound W 0.03 to 39.6 0.05 to 50   0.04 to 34.7 0.06 to 45   0.05 to 29.7 0.07 to 39   HfC HfC 60 to 97 48 to 95 65 to 96 53 to 94 70 to 95 58 to 93 Re + W Re 0.03 to 39.6 0.11 to 71   0.14 to 67   0.15 to 67.0 0.17 to 62   0.19 to 61.8 2700 to 3000 Bound W 0.03 to 39.6 0.1 to 69  0.13 to 65   0.06 to 46.3 0.15 to 60   0.07 to 40.8 VC VC 60 to 97 28 to 90 33 to 87 32.8 to 93.5 70 to 95 38 to 84 Re + W Re 0.03 to 39.6 0.08 to 64   0.04 to 34.7 0.1 to 59  0.05 to 29.7 0.13 to 53   3200 to 3500 Bound W 0.03 to 39.6 0.07 to 56   0.04 to 34.7 0.09 to 56   0.05 to 29.7 0.11 to 51   NbC NbC 60 to 97 36 to 93 65 to 96 41 to 91 70 to 95 47 to 88 Re + W Re 0.03 to 39.6 0.04 to 49   0.04 to 34.7 0.06 to 43   0.05 to 29.7 0.07 to 38   3100 to 3500 Bound W 0.03 to 39.6 0.04 to 47   0.04 to 34.7 0.05 to 41   0.05 to 29.7 0.07 to 36   TaC TaC 60 to 97 51 to 96 65 to 96 56 to 95 70 to 95 62 to 93 Re + W Re 0.03 to 39.6 0.09 to 67   0.04 to 34.7 0.12 to 62   0.05 to 29.7 0.14 to 57   1700 to 1900 Bound W 0.03 to 39.6 0.08 to 65   0.04 to 34.7 0.11 to 60   0.05 to 29.7 0.13 to 55   Cr₂C₃ Cr₂C₃ 60 to 97 32 to 92 65 to 96 37 to 89 70 to 95 43 to 87 Re + W Re 0.03 to 39.6 0.07 to 60   0.04 to 34.7 0.09 to 55   0.05 to 29.7 0.11 to 49   2400 to 2600 Bound W 0.03 to 39.6 0.06 to 58   0.04 to 34.7 0.08 to 53   0.05 to 29.7 0.1 to 47  Mo₂C Mo₂C 60 to 97 39 to 94 65 to 96 45 to 92 70 to 95 50 to 90 Re + W Re 0.03 to 39.6 0.04 to 47   0.04 to 34.7 0.05 to 42   0.05 to 29.7 0.07 to 36   2700 to 2900 Bound W 0.03 to 39.6 0.04 to 45   0.04 to 34.7 0.05 to 40   0.05 to 29.7 0.06 to 34   WC WC 60 to 97 53 to 96 65 to 96 58 to 95 70 to 95 63 to 94 Re + W Re 0.03 to 39.6 0.1 to 71  0.04 to 34.7 0.14 to 67   0.05 to 29.7 0.17 to 62   2900 to 3200 Bound W 0.03 to 39.6 0.1 to 70  0.04 to 34.7 0.13 to 65   0.05 to 29.7 0.16 to 60   TiN TiN 60 to 97 28 to 90 65 to 96 32 to 87 70 to 95 38 to 84 Re + W Re 0.03 to 39.6 0.08 to 65   0.04 to 34.7 0.11 to 60   0.05 to 29.7 0.13 to 55   2900 to 3200 Bound W 0.03 to 39.6 0.08 to 63   0.04 to 34.7 0.1 to 58  0.05 to 29.7 0.12 to 53   ZrN ZrN 60 to 97 34 to 92 65 to 96 39 to 90 70 to 95 45 to 88 Re + W Re 0.03 to 39.6 0.05 to 50   0.04 to 34.7 0.06 to 45   0.05 to 29.7 0.08 to 39   3100 to 3400 Bound W 0.03 to 39.6 0.04 to 48   0.04 to 34.7 0.06 to 43   0.05 to 29.7 0.07 to 37   HfN HfN 60 to 97 50 to 96 65 to 96 55 to 95 70 to 95 61 to 93 Re + W Re 0.03 to 39.6 0.1 to 69  0.04 to 34.7 0.13 to 65   0.05 to 29.7 0.16 to 59   2100 to 2300 Bound W 0.03 to 39.6 0.09 to 67   0.04 to 34.7 0.12 to 63   0.05 to 29.7 0.14 to 57   VN VN 60 to 97 30 to 91 65 to 96 35 to 88 70 to 95 40 to 86 Re + W Re 0.03 to 39.6 0.08 to 65   0.04 to 34.7 0.11 to 60   0.05 to 29.7 0.13 to 55   2300 to 2500 Bound W 0.03 to 39.6 0.08 to 63   0.04 to 34.7 0.1 to 58  0.05 to 29.7 0.12 to 53   NbN NbN 60 to 97 35 to 92 65 to 96 39 to 90 70 to 95 45 to 88 Re + W Re 0.03 to 39.6 0.04 to 49   0.04 to 34.7 0.06 to 44   0.05 to 29.7 0.07 to 38   2900 to 3400 Bound W 0.03 to 39.6 0.04 to 47   0.04 to 34.7 0.05 to 42   0.05 to 29.7 0.07 to 36   TaN TaN 60 to 97 51 to 96 65 to 96 56 to 95 70 to 95 61 to 93

TABLE 46 Re and W (Re + W) bound a boride from borides of IVb, Vb, & VIb or a silicide from silicides of IVb & Vb. The range of Binder is from 1% Re + 99% W to 99% Re + 1% W Composition Composition Composition Estimated Range 1 Range 2 Range 3 Melting Volume % Weight % Volume % Weight % Volume % Weight % Point, ° C. Re + W Re 0.03 to 39.6 0.13 to 75   0.04 to 34.7 0.16 to 71   0.05 to 29.7 0.2 to 66  2900 to 3100 Bound W 0.03 to 39.6 0.12 to 73   0.04 to 34.7 0.15 to 69   0.05 to 29.7 0.18 to 64   TiB₂ TiB₂ 60 to 97 24 to 88 65 to 96 29 to 85 70 to 95 33 to 82 Re + W Re 0.03 to 39.6 0.1 to 69  0.04 to 34.7 0.13 to 64   0.05 to 29.7 0.16 to 59   2900 to 3100 Bound W 0.03 to 39.6 0.09 to 67   0.04 to 34.7 0.12 to 63   0.05 to 29.7 0.14 to 57   ZrB₂ ZrB₂ 60 to 97 30 to 91 65 to 96 35 to 88 70 to 95 40 to 86 Re + W Re 0.03 to 39.6 0.05 to 54   0.04 to 34.7 0.07 to 50   0.05 to 29.7 0.09 to 44   3100 to 3300 Bound W 0.03 to 39.6 0.05 to 53   0.04 to 34.7 0.07 to 48   0.05 to 29.7 0.08 to 42   HfB₂ HfB₂ 60 to 97 44 to 95 65 to 96 50 o 93 70 to 95 55 to 92 Re + W Re 0.03 to 39.6 0.11 to 73   0.14 to 67   0.15 to 68   0.17 to 62   0.18 to 63   2000 to 2200 Bound W 0.03 to 39.6 0.1 to 71  0.13 to 65   0.13 to 66   0.15 to 60   0.16 to 61   VB₂ VB₂ 60 to 97 27 to 90 33 to 87 31 to 86 70 to 95 36 to 84 Re + W Re 0.03 to 39.6 0.08 to 65   0.04 to 34.7 0.1 to 61  0.05 to 29.7 0.13 to 55   2900 to 3100 Bound W 0.03 to 39.6 0.08 to 63   0.04 to 34.7 0.1 to 58  0.05 to 29.7 0.12 to 53   NbB₂ NbB₂ 60 to 97 34 to 92 65 to 96 39 to 90 70 to 95 44 to 88 Re + W Re 0.03 to 39.6 0.05 to 52   0.04 to 34.7 0.07 to 47   0.05 to 29.7 0.08 to 41   3100 to 3300 Bound W 0.03 to 39.6 0.05 to 50   0.04 to 34.7 0.06 to 39   0.05 to 29.7 0.07 to 39   TaB₂ TaB₂ 60 to 97 47 to 96 65 to 96 53 to 94 70 to 95 58 to 93 Re + W Re 0.03 to 39.6 0.1 to 69  0.04 to 34.7 0.13 to 64   0.05 to 29.7 0.16 to 59   1900 to 2100 Bound W 0.03 to 39.6 0.09 to 67   0.04 to 34.7 0.12 to 62   0.05 to 29.7 0.14 to 57   Cr₃B₂ Cr₃B₂ 60 to 97 32 to 91 65 to 96 35 to 88 70 to 95 40 to 86 Re + W Re 0.03 to 39.6 0.08 to 64   0.04 to 34.7 0.1 to 59  0.05 to 29.7 0.13 to 53   2000 to 2200 Bound W 0.03 to 39.6 0.07 to 62   0.04 to 34.7 0.09 to 57   0.05 to 29.7 0.11 to 51   MoB₂ MoB₂ 60 to 97 36 to 93 65 to 96 41 to 91 70 to 95 46 to 88 Re + W Re 0.03 to 39.6 0.04 to 46   0.04 to 34.7 0.05 to 41   0.05 to 29.7 0.07 to 36   2800 to 2900 Bound W 0.03 to 39.6 0.04 to 44   0.04 to 34.7 0.05 to 39   0.05 to 29.7 0.06 to 34   WB WB 60 to 97 53 to 96 65 to 96 57 to 95 70 to 95 64 to 94 Re + W Re 0.03 to 39.6 0.04 to 45   0.04 to 34.7 0.05 to 40   0.05 to 29.7 0.06 to 35   2700 to 2900 Bound W 0.03 to 39.6 0.03 to 43   0.04 to 34.7 0.05 to 38   0.05 to 29.7 0.06 to 33   W₂B W₂B 60 to 97 54 to 97 65 to 96 60 to 95 70 to 95 65 to 94 Re + W Re 0.03 to 39.6 0.13 to 76   0.04 to 34.7 0.17 to 72   0.05 to 29.7 0.21 to 67   2000 to 2200 Bound W 0.03 to 39.6 0.12 to 74   0.04 to 34.7 0.16 to 70   0.05 to 29.7 0.19 to 65   Ti₅Si₃ Ti₅Si₃ 60 to 97 24 to 88 65 to 96 28 to 84 70 to 95 32 to 81 Re + W Re 0.03 to 39.6 0.11 to 71   0.04 to 34.7 0.14 to 67   0.05 to 29.7 0.17 to 61   2100 to 2400 Bound W 0.03 to 39.6 0.1 to 69  0.04 to 34.7 0.13 to 65   0.05 to 29.7 0.15 to 59   Zr₆Si₅ Zr₆Si₅ 60 to 97 28 to 90 65 to 96 33 to 87 70 to 95 38 to 84 Re + W Re 0.03 to 39.6 0.09 to 68   0.04 to 34.7 0.12 to 64   0.05 to 29.7 0.15 to 58   1900 to 2100 Bound W 0.03 to 39.6 0.09 to 66   0.04 to 34.7 0.11 to 62   0.05 to 29.7 0.14 to 56   NbSi₂ NbSi₂ 60 to 97 31 to 91 65 to 96 36 to 89 70 to 95 41 to 86 Re + W Re 0.03 to 39.6 0.07 to 62   0.04 to 34.7 0.09 to 57   0.05 to 29.7 0.12 to 51   2300 to 2500 Bound W 0.03 to 39.6 0.07 to 60   0.04 to 34.7 0.09 to 54   0.05 to 29.7 0.11 to 49   TaSi₂ TaSi₂ 60 to 97 38 to 93 65 to 96 43 to 91 70 to 95 49 to 89 Re + W Re 0.03 to 39.6 0.1 to 69  0.04 to 34.7 0.12 to 64   0.05 to 29.7 0.15 to 58   1900 to 2100 Bound W 0.03 to 39.6 0.09 to 67   0.04 to 34.7 0.11 to 62   0.05 to 29.7 0.14 to 56   MoSi₂ MoSi₂ 60 to 97 31 to 91 65 to 96 36 to 89 70 to 95 41 to 86 Re + W Re 0.03 to 39.6 0.07 to 60   0.04 to 34.7 0.09 to 54   0.05 to 29.7 0.11 to 49   1900 to 2100 Bound W 0.03 to 39.6 0.06 to 58   0.04 to 34.7 0.08 to 52   0.05 to 29.7 0.1 to 47  WSi₂ WSi₂ 60 to 97 40 to 94 65 to 96 45 to 92 70 to 95 51 to 90

TABLE 47 Re and Co (Re + Co) bound a carbide from carbides of IVb, Vb, & VIb or a nitride from nitrides of IVb & Vb. The range of Binder is from 1% Re + 99% Co to 99% Re + 1% Co. Estimated Composition Range 1 Composition Range 2 Composition Range 3 Melting Volume % Weight % Volume % Weight % Volume % Weight % Point, ° C. Re + Re 0.03 to 39.6 0.12 to 74   0.04 to 34.7 0.17 to 69   0.05 to 29.7 0.2 to 64  1400 to 3200 Co Co 0.03 to 39.6 0.05 to 54   0.04 to 34.7 0.07 to 49   0.05 to 29.7 0.08 to 43   Bound TiC 60 to 97 26 to 95 65 to 96 30 to 93 70 to 95 35 to 91 TiC Re + Re 0.03 to 39.6 0.09 to 68   0.04 to 34.7 0.13 to 63   0.05 to 29.7 0.16 to 57   1400 to 3200 Co Co 0.03 to 39.6 0.04 to 47   0.04 to 34.7 0.05 to 42   0.05 to 29.7 0.06 to 37   Bound ZrC 60 to 97 32 to 96 65 to 96 37 to 95 70 to 95 42 to 93 ZrC Re + Re 0.03 to 39.6 0.05 to 52   0.04 to 34.7 0.07 to 47   0.05 to 29.7 0.08 to 41   1400 to 3200 Co Co 0.03 to 39.6 0.02 to 32   0.04 to 34.7 0.03 to 27   0.05 to 29.7 0.04 to 23   Bound HfC 60 to 97 48 to 98 65 to 96 53 to 97 70 to 95 59 to 96 HfC Re + Re 0.03 to 39.6 0.11 to 71   0.14 to 67   0.15 to 67.0 0.17 to 62   0.19 to 62   1400 to 2900 Co Co 0.03 to 39.6 0.05 to 51   0.13 to 65   0.06 to 46   0.15 to 60   0.07 to 41   Bound VC 60 to 97 28 to 95 33 to 87 33 to 94 70 to 95 38 to 92 VC Re + Re 0.03 to 39.6 0.08 to 64   0.04 to 34.7 0.1 to 59  0.05 to 29.7 0.13 to 53   1400 to 3200 Co Co 0.03 to 39.6 0.03 to 43   0.04 to 34.7 0.04 to 38   0.05 to 29.7 0.05 to 33   Bound NbC 60 to 97 36 to 97 65 to 96 41 to 95 70 to 95 47 to 94 NbC Re + Re 0.03 to 39.6 0.04 to 49   0.04 to 34.7 0.06 to 43   0.05 to 29.7 0.07 to 38   1400 to 3200 Co Co 0.03 to 39.6 0.02 to 29   0.04 to 34.7 0.024 to 25   0.05 to 29.7 0.03 to 21   Bound TaC 60 to 97 51 to 98 65 to 96 56 to 97 70 to 95 62 to 97 TaC Re + Re 0.03 to 39.6 0.09 to 67   0.04 to 34.7 0.12 to 62   0.05 to 29.7 0.15 to 57   1400 to 1900 Co Co 0.03 to 39.6 0.04 to 47   0.04 to 34.7 0.05 to 41   0.05 to 29.7 0.06 to 36   Bound Cr₂C₃ 60 to 97 32 to 96 65 to 96 37 to 95 70 to 95 43 to 93 Cr₂C₃ Re + Re 0.03 to 39.6 0.07 to 60   0.04 to 34.7 0.09 to 55   0.05 to 29.7 0.11 to 49   1400 to 2600 Co Co 0.03 to 39.6 0.03 to 39   0.04 to 34.7 0.04 to 34   0.05 to 29.7 0.05 to 29   Bound Mo₂C 60 to 97 40 to 97 65 to 96 45 to 96 70 to 95 50 to 95 Mo₂C Re + Re 0.03 to 39.6 0.04 to 47   0.04 to 34.7 0.05 to 42   0.05 to 29.7 0.07 to 36   1400 to 2900 Co Co 0.03 to 39.6 0.017 to 27   0.04 to 34.7 0.023 to 23   0.05 to 29.7 0.028 to 20   Bound WC 60 to 97 53 to 96 65 to 96 58 to 95 70 to 95 63 to 94 WC Re + Re 0.03 to 39.6 0.11 to 71   0.04 to 34.7 0.15 to 67   0.05 to 29.7 0.19 to 62   1400 to 3200 Co Co 0.03 to 39.6 0.05 to 52   0.04 to 34.7 0.06 to 46   0.05 to 29.7 0.07 to 41   Bound TiN 60 to 97 28 to 95 65 to 96 33 to 93 70 to 95 38 to 92 TiN Re + Re 0.03 to 39.6 0.08 to 65   0.04 to 34.7 0.11 to 60   0.05 to 29.7 0.14 to 55   1400 to 3200 Co Co 0.03 to 39.6 0.04 to 44   0.04 to 34.7 0.05 to 39   0.05 to 29.7 0.06 to 34   Bound ZrN 60 to 97 34 to 96 65 to 96 39 to 95 70 to 95 45 to 94 ZrN Re + Re 0.03 to 39.6 0.05 to 50   0.04 to 34.7 0.06 to 45   0.05 to 29.7 0.08 to 39   1400 to 3200 Co Co 0.03 to 39.6 0.019 to 30   0.04 to 34.7 0.026 to 26   0.05 to 29.7 0.032 to 22   Bound HfN 60 to 97 50 to 98 65 to 96 55 to 97 70 to 95 61 to 97 HfN Re + Re 0.03 to 39.6 0.1 to 70  0.04 to 34.7 0.14 to 65   0.05 to 29.7 0.17 to 60   1400 to 2300 Co Co 0.03 to 39.6 0.04 to 49   0.04 to 34.7 0.05 to 44   0.05 to 29.7 0.07 to 39   Bound VN 60 to 97 30 to 96 65 to 96 35 to 94 70 to 95 40 to 93 VN Re + Re 0.03 to 39.6 0.08 to 65   0.04 to 34.7 0.11 to 60   0.05 to 29.7 0.14 to 55   1400 to 2500 Co Co 0.03 to 39.6 0.04 to 45   0.04 to 34.7 0.05 to 39   0.05 to 29.7 0.06 to 34   Bound NbN 60 to 97 34 to 96 65 to 96 39 to 95 70 to 95 45 to 94 NbN Re + Re 0.03 to 39.6 0.04 to 49   0.04 to 34.7 0.06 to 44   0.05 to 29.7 0.07 to 38   1400 to 3200 Co Co 0.03 to 39.6 0.02 to 29   0.04 to 34.7 0.025 to 25   0.05 to 29.7 0.03 to 21   Bound TaN 60 to 97 51 to 98 65 to 96 56 to 97 70 to 95 62 to 98 TaN

TABLE 48 Re and Co (Re + Co) bound a boride from borides of IVb, Vb, & VIb or a silicide from silicides of IVb & Vb. The range of Binder is from 1% Re + 99% Co to 99% Re + 1% Co. Composition Composition Composition Estimated Range 1 Range 2 Range 3 Melting Volume % Weight % Volume % Weight % Volume % Weight % Point, ° C. Re + Co Re 0.03 to 39.6 0.13 to 75   0.04 to 34.7 0.18 to 71   0.05 to 29.7 0.22 to 66   1400 to 3100 Bound Co 0.03 to 39.6 0.05 to 56   0.04 to 34.7 0.07 to 51   0.05 to 29.7 0.08 to 45   TiB₂ TiB₂ 60 to 97 24 to 34 65 to 96 29 to 92 70 to 95 34 to 90 Re + Co Re 0.03 to 39.6 0.1 to 69  0.04 to 34.7 0.13 to 64   0.05 to 29.7 0.17 to 59   1400 to 3100 Bound Co 0.03 to 39.6 0.04 to 49   0.05 to 34.7 0.05 to 44   0.05 to 29.7 0.07 to 38   ZrB₂ ZrB₂ 60 to 97 30 to 96 65 to 96 35 to 94 70 to 95 40 to 93 Re + Co Re 0.03 to 39.6 0.06 to 55   0.04 to 34.7 0.08 to 50   0.05 to 29.7 0.09 to 44   1400 to 3200 Bound Co 0.03 to 39.6 0.2 to 34  0.04 to 34.7 0.03 to 30   0.05 to 29.7 0.04 to 25   HfB₂ HfB₂ 60 to 97 45 to 98 65 to 96 50 o 97 70 to 95 56 to 96 Re + Co Re 0.03 to 39.6 0.12 to 73   0.14 to 67   0.16 to 69   0.17 to 62   0.2 to 63  1400 to 2200 Bound Co 0.03 to 39.6 0.05 to 53   0.13 to 65   0.06 to 48   0.15 to 60   0.08 to 42   VB₂ VB₂ 60 to 97 27 to 95 33 to 87 31 to 93 70 to 95 36 to 91 Re + Co Re 0.03 to 39.6 0.09 to 66   0.04 to 34.7 0.12 to 61   0.05 to 29.7 0.14 to 55   1400 to 3100 Bound Co 0.03 to 39.6 0.04 to 45   0.04 to 34.7 0.05 to 40   0.05 to 29.7 0.06 to 34   NbB₂ NbB₂ 60 to 97 34 to 96 65 to 96 39 to 95 70 to 95 45 to 94 Re + Co Re 0.03 to 39.6 0.05 to 52   0.04 to 34.7 0.07 to 47   0.05 to 29.7 0.08 to 41   1400 to 3300 Bound Co 0.03 to 39.6 0.02 to 32   0.04 to 34.7 0.03 to 27   0.05 to 29.7 0.035 to 23   TaB₂ TaB₂ 60 to 97 48 to 98 65 to 96 53 to 97 70 to 95 58 to 96 Re + Co Re 0.03 to 39.6 0.1 to 69   0.04 to 34.7 0.13 to 65   0.05 to 29.7 0.17 to 59   1400 to 2100 Bound Co 0.03 to 39.6 0.04 to 49   0.04 to 34.7 0.05 to 44   0.05 to 29.7 0.07 to 38   Cr₃B₂ Cr₃B₂ 60 to 97 30 to 96 65 to 96 35 to 93 70 to 95 41 to 93 Re + Co Re 0.03 to 39.6 0.08 to 64   0.04 to 34.7 0.1 to 59   0.05 to 29.7 0.13 to 53   1400 to 2200 Bound Co 0.03 to 39.6 0.03 to 43   0.04 to 34.7 0.04 to 38   0.05 to 29.7 0.05 to 33   MoB₂ MoB₂ 60 to 97 36 to 97 65 to 96 41 to 95 70 to 95 46 to 94 Re + Co Re 0.03 to 39.6 0.04 to 46   0.04 to 34.7 0.05 to 41   0.05 to 29.7 0.07 to 36   1400 to 2900 Bound Co 0.03 to 39.6 0.017 to 27   0.04 to 34.7 0.022 to 23   0.05 to 29.7 0.028 to 19   WB WB 60 to 97 53 to 98 65 to 96 59 to 98 70 to 95 64 to 97 Re + Co Re 0.03 to 39.6 0.04 to 45   0.04 to 34.7 0.05 to 40   0.05 to 29.7 0.06 to 35   1400 to 2900 Bound Co 0.03 to 39.6 0.016 to 26   0.04 to 34.7 0.021 to 22   0.05 to 29.7 0.027 to 19   W₂B W₂B 60 to 97 55 to 98 65 to 96 60 to 98 70 to 95 65 to 97 Re + Co Re 0.03 to 39.6 0.14 to 76   0.04 to 34.7 0.18 to 72   0.05 to 29.7 0.23 to 67   1400 to 2200 Bound Co 0.03 to 39.6 0.06 to 57   0.04 to 34.7 0.07 to 52   0.05 to 29.7 0.09 to 47   Ti₅Si₃ Ti₅Si₃ 60 to 97 24 to 94 65 to 96 28 to 92 70 to 95 32 to 90 Re + Co Re 0.03 to 39.6 0.11 to 71   0.04 to 34.7 0.15 to 67   0.05 to 29.7 0.19 to 62   1400 to 2400 Bound Co 0.03 to 39.6 0.05 to 51   0.04 to 34.7 0.06 to 46   0.05 to 29.7 0.07 to 41   Zr₆Si₅ ZrN 60 to 97 28 to 95 65 to 96 33 to 94 70 to 95 38 to 92 Re + Co Re 0.03 to 39.6 0.1 to 69  0.04 to 34.7 0.13 to 64   0.05 to 29.7 0.16 to 58   1400 to 2100 Bound Co 0.03 to 39.6 0.04 to 48   0.04 to 34.7 0.05 to 43   0.05 to 29.7 0.06 to 37   NbSi₂ NbSi₂ 60 to 97 31 to 96 65 to 96 36 to 94 70 to 95 41 to 93 Re + Co Re 0.03 to 39.6 0.07 to 62   0.04 to 34.7 0.1 to 57  0.05 to 29.7 0.12 to 51   1400 to 2500 Bound Co 0.03 to 39.6 0.03 to 41   0.04 to 34.7 0.04 to 36   0.05 to 29.7 0.05 to 31   TaSi₂ TaSi₂ 60 to 97 38 to 97 65 to 96 43 to 96 70 to 95 49 to 95 Re + Co Re 0.03 to 39.6 0.1 to 69  0.04 to 34.7 0.13 to 64   0.05 to 29.7 0.16 to 59   1400 to 2100 Bound Co 0.03 to 39.6 0.04 to 48   0.04 to 34.7 0.05 to 43   0.05 to 29.7 0.07 to 38   MoSi₂ MoSi₂ 60 to 97 31 to 96 65 to 96 36 to 94 70 to 95 41 to 93 Re + Co Re 0.03 to 39.6 0.07 to 60   0.04 to 34.7 0.09 to 55   0.05 to 29.7 0.11 to 49   1400 to 2100 Bound Co 0.03 to 39.6 0.03 to 39   0.04 to 34.7 0.04 to 34   0.05 to 29.7 0.046 to 29   WSi₂ WSi₂ 60 to 97 40 to 97 65 to 96 45 to 96 70 to 95 51 to 95

TABLE 49 Re and Mo (Re + Mo) bound a carbide from carbides of IVb, Vb, & VIb. The range of Binder is from 1% Re + 99% Mo to 99% Re + 1% Mo. Composition Composition Composition Estimated Range 1 Range 2 Range 3 Melting Volume % Weight % Volume % Weight % Volume % Weight % Point, ° C. Re + Mo Re 0.03 to 39.6 0.12 to 74 0.04 to 34.7 0.16 to 69 0.05 to 29.7  0.2 to 64 2600 to 3200 Bound Mo 0.03 to 39.6 0.06 to 57 0.04 to 34.7 0.07 to 52 0.05 to 29.7 0.09 to 46 TiC TiC 60 to 97   26 to 94 65 to 96   30 to 92 70 to 95   35 to 90 Re + Mo Re 0.03 to 39.6 0.09 to 68 0.04 to 34.7 0.13 to 63 0.05 to 29.7 0.16 to 57 2600 to 3200 Bound Mo 0.03 to 39.6 0.04 to 50 0.04 to 34.7 0.06 to 45 0.05 to 29.7 0.07 to 39 ZrC ZrC 60 to 97   32 to 95 65 to 96   37 to 94 70 to 95   42 to 92 Re + Mo Re 0.03 to 39.6 0.05 to 52 0.04 to 34.7 0.07 to 47 0.05 to 29.7 0.08 to 41 2600 to 3200 Bound Mo 0.03 to 39.6 0.02 to 34 0.04 to 34.7 0.03 to 30 0.05 to 29.7 0.04 to 25 HfC HfC 60 to 97   48 to 98 65 to 96   53 to 97 70 to 95   59 to 96 Re + Mo Re 0.03 to 39.6 0.11 to 71 0.14 to 67     0.15 to 67.0 0.17 to 62   0.18 to 62 2600 to 2900 Bound Mo 0.03 to 39.6 0.05 to 55 0.13 to 65   0.07 to 49 0.15 to 60   0.08 to 44 VC VC 60 to 97   28 to 95 33 to 87   33 to 93 70 to 95   38 to 91 Re + Re 0.03 to 39.6 0.08 to 64 0.04 to 34.7  0.1 to 59 0.05 to 29.7 0.13 to 53 2600 to 3200 Mo Mo 0.03 to 39.6 0.04 to 46 0.04 to 34.7 0.05 to 41 0.05 to 29.7 0.06 to 35 Bound NbC 60 to 97   36 to 96 65 to 96   41 to 95 70 to 95   47 to 94 NbC Re + Re 0.03 to 39.6 0.04 to 49 0.04 to 34.7 0.06 to 43 0.05 to 29.7 0.07 to 38 2600 to 3200 Mo Mo 0.03 to 39.6 0.02 to 31 0.04 to 34.7 0.028 to 27  0.05 to 29.7 0.03 to 22 Bound TaC 60 to 97   51 to 98 65 to 96   56 to 97 70 to 95   62 to 96 TaC Re + Mo Re 0.03 to 39.6 0.09 to 67 0.04 to 34.7 0.12 to 62 0.05 to 29.7 0.15 to 57 1700 to 1900 Bound Mo 0.03 to 39.6 0.04 to 50 0.04 to 34.7 0.06 to 45 0.05 to 29.7 0.07 to 39 Cr₂C₃ Cr₂C₃ 60 to 97   32 to 95 65 to 96   37 to 94 70 to 95   43 to 92 Re + Re 0.03 to 39.6 0.07 to 60 0.04 to 34.7 0.09 to 55 0.05 to 29.7 0.11 to 49 2500 to 2600 Mo Mo 0.03 to 39.6 0.03 to 42 0.04 to 34.7 0.04 to 37 0.05 to 29.7 0.05 to 32 Bound Mo₂C 60 to 97   40 to 97 65 to 96   45 to 96 70 to 95   50 to 95 Mo₂C Re + Re 0.03 to 39.6 0.04 to 47 0.04 to 34.7 0.05 to 42 0.05 to 29.7 0.07 to 36 2600 to 2900 Mo Mo 0.03 to 39.6 0.019 to 30  0.04 to 34.7 0.026 to 26  0.05 to 29.7 0.032 to 22  Bound WC 60 to 97   53 to 98 65 to 96   58 to 97   70 to 95   64 to 97 WC

TABLE 50 Re and Ni (Re + Ni) bound a carbide from carbides of IVb, Vb, & VIb. The range of Binder is from 1% Re + 99% Ni to 99% Re + 1% Ni. Estimated Composition Range 1 Composition Range 2 Composition Range 3 Melting Volume % Weight % Volume % Weight % Volume % Weight % Point, ° C. Re + Re 0.03 to 39.6 0.12 to 74 0.04 to 34.7 0.17 to 69 0.05 to 29.7  0.2 to 64 1400 to 3200 Ni Ni 0.03 to 39.6 0.05 to 54 0.04 to 34.7 0.06 to 49 0.05 to 29.7 0.08 to 43 Bound TiC 60 to 97   26 to 95 65 to 96   30 to 93 70 to 95   35 to 91 TiC Re + Re 0.03 to 39.6 0.09 to 68 0.04 to 34.7 0.13 to 63 0.05 to 29.7 0.16 to 57 1400 to 3200 Ni Ni 0.03 to 39.6 0.04 to 47 0.04 to 34.7 0.05 to 42 0.05 to 29.7 0.06 to 36 Bound ZrC 60 to 97   32 to 96 65 to 96   37 to 95 70 to 95   42 to 93 ZrC Re + Re 0.03 to 39.6 0.05 to 52 0.04 to 34.7 0.07 to 47 0.05 to 29.7 0.08 to 41 1400 to 3200 Ni Co 0.03 to 39.6 0.02 to 31 0.04 to 34.7 0.027 to 27  0.05 to 29.7 0.034 to 23  Bound HfC 60 to 97   48 to 98 65 to 96   53 to 97 70 to 95   59 to 96 HfC Re + Re 0.03 to 39.6 0.11 to 71 0.14 to 67     0.15 to 67.0 0.17 to 62   0.19 to 62 1400 to 2900 Ni Ni 0.03 to 39.6 0.04 to 51 0.13 to 65   0.06 to 46 0.15 to 60   0.07 to 40 Bound VC 60 to 97   28 to 95 33 to 87   33 to 94 70 to 95   38 to 92 VC Re + Re 0.03 to 39.6 0.08 to 64 0.04 to 34.7  0.1 to 59 0.05 to 29.7 0.13 to 53 1400 to 3200 Ni Ni 0.03 to 39.6 0.03 to 43 0.04 to 34.7 0.04 to 37 0.05 to 29.7 0.05 to 32 Bound NbC 60 to 97   36 to 97 65 to 96   41 to 95 70 to 95   47 to 94 NbC Re + Re 0.03 to 39.6 0.04 to 49 0.04 to 34.7 0.06 to 43 0.05 to 29.7 0.07 to 38 1400 to 3200 Ni Ni 0.03 to 39.6 0.018 to 29  0.04 to 34.7 0.024 to 25  0.05 to 29.7 0.03 to 21 Bound TaC 60 to 97   51 to 98 65 to 96   56 to 97 70 to 95   62 to 97 TaC Re + Re 0.03 to 39.6 0.09 to 67 0.04 to 34.7 0.12 to 62 0.05 to 29.7 0.15 to 57 1400 to 1900 Ni Ni 0.03 to 39.6 0.04 to 46 0.04 to 34.7 0.05 to 41 0.05 to 29.7 0.06 to 36 Bound Cr₂C₃ 60 to 97   32 to 96 65 to 96   37 to 95 70 to 95   43 to 93 Cr₂C₃ Re + Re 0.03 to 39.6 0.07 to 60 0.04 to 34.7 0.09 to 55 0.05 to 29.7 0.11 to 49 1400 to 2600 Ni Ni 0.03 to 39.6 0.03 to 39 0.04 to 34.7 0.04 to 34 0.05 to 29.7 0.05 to 29 Bound Mo₂C 60 to 97   40 to 97 65 to 96   45 to 96 70 to 95   50 to 95 Mo₂C Re + Re 0.03 to 39.6 0.04 to 47 0.04 to 34.7 0.06 to 42 0.05 to 29.7 0.07 to 36 1400 to 2900 Ni Ni 0.03 to 39.6 0.017 to 27 0.04 to 34.7 0.022 to 23  0.05 to 29.7 0.028 to 19  Bound WC 60 to 97   53 to 98 65 to 96   58 to 98 70 to 95   64 to 97 WC

TABLE 51 Re and Cr (Re + Cr) bound a carbide from carbides of IVb, Vb, & VIb. The range of Binder is from 1% Re + 99% Cr to 99% Re + 1% Cr. Estimated Composition Range 1 Composition Range 2 Composition Range 3 Melting Volume % Weight % Volume % Weight % Volume % Weight % Point, ° C. Re + Re 0.03 to 39.6 0.13 to 74 0.04 to 34.7 0.17 to 69 0.05 to 29.7  0.2 to 64 1800 to 3200 Cr Cr 0.03 to 39.6 0.04 to 48 0.04 to 34.7 0.05 to 43 0.05 to 29.7 0.06 to 39 Bound TiC 60 to 97   26 to 96 65 to 96   30 to 94 70 to 95   36 to 93 TiC Re + Re 0.03 to 39.6  0.1 to 68 0.04 to 34.7 0.13 to 63 0.05 to 29.7 0.16 to 57 1800 to 3200 Cr Cr 0.03 to 39.6 0.03 to 41 0.04 to 34.7 0.04 to 36 0.05 to 29.7 0.05 to 32 Bound ZrC 60 to 97   32 to 97 65 to 96   37 to 95 70 to 95   42 to 94 ZrC Re + Re 0.03 to 39.6 0.05 to 52 0.04 to 34.7 0.07 to 47 0.05 to 29.7 0.09 to 41 1800 to 3200 Cr Cr 0.03 to 39.6 0.017 to 27  0.04 to 34.7 0.022 to 23  0.05 to 29.7 0.027 to 19  Bound HfC 60 to 97   48 to 98 65 to 96   53 to 98 70 to 95   59 to 97 HfC Re + Re 0.03 to 39.6 0.11 to 71 0.14 to 67     0.15 to 67.0 0.17 to 62   0.19 to 62 1800 to 2900 Cr Cr 0.03 to 39.6 0.04 to 46 0.13 to 65   0.05 to 41 0.15 to 60   0.06 to 35 Bound VC 60 to 97   28 to 96 33 to 87   33 to 95 70 to 95   38 to 93 VC Re + Re 0.03 to 39.6 0.08 to 64 0.04 to 34.7  0.1 to 59 0.05 to 29.7 0.13 to 53 1800 to 3200 Cr Cr 0.03 to 39.6 0.026 to 37  0.04 to 34.7 0.034 to 33  0.05 to 29.7 0.04 to 28 Bound NbC 60 to 97   36 to 97 65 to 96   41 to 96 70 to 95   47 to 95 NbC Re + Re 0.03 to 39.6 0.04 to 49 0.04 to 34.7 0.06 to 43 0.05 to 29.7 0.07 to 38 1800 to 3200 Cr Cr 0.03 to 39.6 0.015 to 25  0.04 to 34.7 0.019 to 21  0.05 to 29.7 0.024 to 17  Bound TaC 60 to 97   51 to 98 65 to 96   56 to 98 70 to 95   62 to 97 TaC Re + Re 0.03 to 39.6 0.09 to 67 0.04 to 34.7 0.12 to 62 0.05 to 29.7 0.16 to 57 1800 to 1900 Cr Cr 0.03 to 39.6 0.03 to 41 0.04 to 34.7 0.04 to 36 0.05 to 29.7 0.05 to 31 Bound Cr₂C₃ 60 to 97   32 to 97 65 to 96   37 to 96 70 to 95   43 to 95 Cr₂C₃ Re + Re 0.03 to 39.6 0.07 to 60 0.04 to 34.7 0.09 to 55 0.05 to 29.7 0.11 to 49 1800 to 2600 Cr Cr 0.03 to 39.6 0.023 to 34  0.04 to 34.7 0.03 to 29 0.05 to 29.7 0.037 to 25  Bound Mo₂C 60 to 97   40 to 98 65 to 96   45 to 97 70 to 95   50 to 96 Mo₂C Re + Re 0.03 to 39.6 0.04 to 47 0.04 to 34.7 0.05 to 42 0.05 to 29.7 0.07 to 36 1800 to 2900 Cr Cr 0.03 to 39.6 0.014 to 23  0.04 to 34.7 0.018 to 20  0.05 to 29.7 0.023 to 16  Bound WC 60 to 97    53 to 98.6 65 to 96   58 to 98 70 to 95    64 to 97.6 WC

The above compositions for hardmetals or cermets may be used for a variety of applications. For example, a material as described above may be used to form a wear part in a tool that cuts, grinds, or drills a target object by using the wear part to remove the material of the target object. Such a tool may include a support part made of a different material, such as a steel. The wear part is then engaged to the support part as an insert. The tool may be designed to include multiple inserts engaged to the support part. For example, some mining drills may include multiple button bits made of a hardmetal material. Examples of such a tool includes a drill, a cutter such as a knife, a saw, a grinder, and a drill. Alternatively, hardmetals described here may be used to form the entire head of a tool as the wear part for cutting, drilling or other machining operations. The hardmetal particles may also be used to form abrasive grits for polishing or grinding various materials. In addition, such hardmetals may also be used to construct housing and exterior surfaces or layers for various devices to meet specific needs of the operations of the devices or the environmental conditions under which the devices operate.

More specifically, the hardmetals described here may be used to manufacture cutting tools for machining metals, alloys, composite materials, plastic materials, wooden materials, and others. The cutting tools may include indexable inserts for turning, milling, boring and drilling, drills, end mills, reamers, taps, hobs and milling cutters. Since the temperature of the cutting edge of such tools may be higher than 500° C. during machining, the hardmetal compositions for high-temperature operating conditions described above may have special advantages when used in such cutting tools, e.g., extended tool life and improved productivity by such tools by increasing the cutting speed.

The hardmetals described here may be used to manufacture tools for wire drawing, extrusion, forging and cold heading. Also as mold and Punch for powder process. In addition, such hardmetals may be used as wear-resistant material for rock drilling and mining.

The hardmetal materials described in this application may be fabricated in bulk forms or as coatings on metal surfaces. Coatings with such new hardmetal materials may be advantageously used to form a hard layer on a metal surface to achieve desired hardness that would otherwise be difficult to achieve with the underlying metal material. Bulk hardmetal materials based on the compositions in this application may be expensive and hence the use of coatings on less expensive metals with lower hardness may be used to reduce the costs of various components or parts with high hardness.

A number of powder processes for producing commercial hardmetals may be used to manufacture the hardmetals of this application. As an example, a binder alloy with Re higher than 85% in weight may be fabricated by the process of solid phase sintering to eliminate open porosities then HIP replaces liquid phase sintering.

FIG. 9 shows a flowchart for several fabrication methods for materials or structures from the above hardmetal compositions. As illustrated, alloy powders for the binders and the hard particle powders may be mixed with a milling liquid in a wet mixing process with or without a lubricant (e.g., wax). The fabrication flows on the left hand side of FIG. 9 are for fabricating hardmetals with lubricated wet mixing. The mixture is first dried by vacuum drying or spray drying process to produce lubricated grade powder. Next, the lubricated grade power is shaped into a bulky material via pill pressing, extruding, or cold isostatic press (CIP) and shaping. The CIP is a process to consolidate powder by isostatic pressure. The bulky material is then heated to remove the lubricant and is sintered in a presintering process. Next, the material may be processed via several different processes. For example, the material may be processed via a liquid phase sintering in vacuum or hydrogen and then further processed by a HIP process to form the final hardmetal parts. Alternatively, the material after the presintering may go through a solid phase sintering to eliminate open porosity and then a HIP process to form the final hardmetal parts.

When alloy powders for the binders and the hard particle powders are mixed without the lubricant, the unlubricated grade power after the drying process may be processed in two different ways to form the final hardmetal parts. The first way as illustrated simply uses hot pressing to complete the fabrication. The second way uses a thermal spray forming process to form the grade powder on a metal substrate in vacuum. Next, the metal substrate is removed to leave the structure by the thermal spray forming as a free-standing material as the final hardmetal part. In addition, the free-standing material may be further processed by a HIP process to reduce the porosities if needed.

In forming a hardmetal coating on a metal surface, a thermal spray process may be used under a vacuum condition to produce large parts coated with hardmetal materials. For example, surfaces of steel parts and tools may be coated to improve their hardness and thus performance. FIG. 10 shows an exemplary flow chart of a thermal spray process.

Various thermal spray processes are known for coating metal surfaces. For example, the ASM Handbook Vol. 7 (P408, 1998) describes the thermal spray as a family of particulate/droplet consolidation processes capable of forming metals, ceramics, intermetallics, composites, and polymers into coatings or freestanding structures. During the process, powder, wire, or rods can be injected into combustion or arc-heated jets, where they are heated, melted or softened, accelerated, and directed toward the surface, or substrate, being coated. On impact at the substrate, the particles or droplets rapidly solidify, cool, contract, and incrementally build up to form a deposit on a target surface. The thin “splats” may undergo high cooling rates, e.g., in excess of 10⁶ K/s for metals.

A thermal spray process may use chemical (combustion) or electrical (plasma or arc) energy to heat feed materials injected into hot—gas jets to create a stream of molten droplets that are accelerated and directed toward the substrates being coated. Various thermal spray processes are shown in FIGS. 3 and 4 in ASM Handbook Vol. 7, pages 409-410.

Various details of thermal spray processes are described in “Spray Forming” by Lawley et al. and “Thermal Spray Forming of Materials” by Knight et al., which are published in ASM Handbook, Volume 7, Powder Metal Technologies and Application (1998), from pages 396 to 407, and pages 408 to 419, respectively.

Only a few implementations and examples are disclosed. However, it is understood that variations and enhancements may be made. 

1. A material, comprising: hard particles comprising at least one carbide from carbides of IVb, Vb, and VIb columns in the periodic table; and a binder matrix that binds the hard particles and comprises a Ni-based superalloy and cobalt.
 2. The material as in claim 1, wherein the hard particles are between about 45% to about 98% of a total weight of the material.
 3. The material as in claim 1, wherein the hard particles comprise WC and TiC.
 4. The material as in claim 3, wherein WC and TiC are between about 58% to about 98%, and up to about 24% of a total weight of the material, respectively, and wherein cobalt and the nickel-based superalloy are up to about 33% and about 29% of the total weight of the material, respectively.
 5. The material as in claim 1, wherein the hard particles comprise WC and TaC.
 6. The material as in claim 5, wherein WC and TaC are between about 61% to about 98%, and up to about 24% of a total weight of the material, respectively, and wherein cobalt and the nickel-based superalloy are up to about 28% and about 25% of the total weight of the material, respectively.
 7. A material, comprising: hard particles comprising hard particles comprising at least one carbide from carbides of IVb, Vb, and VIb columns in the periodic table; and a binder matrix that binds the hard particles and comprises a nickel-based superalloy.
 8. The material as in claim 7, wherein the at least one carbide comprise TiC and Mo₂C.
 9. The material as in claim 8, wherein TiC and Mo₂C are between about 30% to about 90% and up to about 40% of a total weight of the material, respectively; and wherein the nickel-based superalloy is between about 4% to about 41% of the total weight of the material.
 10. The material as in claim 7, wherein the at least one carbide comprise Mo₂C, and wherein the hard particles further comprise TiN.
 11. The material as in claim 10, wherein TiN and Mo₂C are up to about 91% and up to about 38% of a total weight of the material, respectively; and wherein the nickel-based superalloy is between about 4% to about 38% of the total weight of the material.
 12. The material as in claim 10, wherein the at least one carbide comprise TiC.
 13. The material as in claim 12, wherein TiC, TiN and Mo₂C are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and wherein the nickel based superalloy which is between about 4% to about 40% of the total weight of the material.
 14. The material as in claim 10, wherein the at least one carbide comprise TiC, WC, TaC, VC and Cr₂C₃.
 15. The material as in claim 14, wherein TiC, TiN, Mo₂C, WC, and TaC are up to about 90%, about 90%, about 25%, about 42%, and about 36% of a total weight of the material, respectively, and VC and Cr₂C₃ are up to about 14% and 18% of the total weight of the material, respectively; and wherein the nickel based superalloy is between about 2% to about 40% of the total weight of the material.
 16. A material, comprising: hard particles comprising hard particles comprising TiN and at least one carbide from carbides of IVb, Vb, and VIb columns in the periodic table; and a binder matrix that binds the hard particles and comprises rhenium, a nickel-based superalloy and cobalt.
 17. The material as in claim 16, wherein the at least one carbide comprise TiC and Mo₂C.
 18. The material as in claim 17, wherein TiC, TiN and Mo₂C are up to about 90%, about 91% and about 38% of a total weight of the material, respectively; and wherein rhenium, the nickel-based superalloy and cobalt are up to about 64%, about 40% and about 42% of the total weight of the material, respectively.
 19. The material as in claim 16, wherein the at least one carbide comprise TiC, Mo₂C, WC, TaC, VC and Cr₂C₃.
 20. The material as in claim 19, wherein TiC, TiN, Mo₂C, WC, and TaC are up to about 89%, about 90%, about 26%, about 42%, and about 33% of a total weight of the material, respectively, and VC and Cr₂C₃ are up to about 16% and 18% of the total weight of the material, respectively; and wherein rhenium, the nickel-based superalloy and cobalt are up to about 63%, about 39% and about 42% of the total weight of the material, respectively. 